Search

Various sectors of the industry are searching for new materials with specific requirements, providing improved properties. The study presents novel composite materials based on polylactide that have been modified with the organosilicon compound, (3-thiopropyl) polysilsesquioxane (SSQ-SH). The SSQ-SH compound is a mixture of cage structures and not fully condensed random structures. The composite materials were obtained through injection moulding. The study includes a comprehensive characterization of the new materials that analyze their functional properties, such as rheology (MFR), mechanical strength (tensile strength, Charpy impact strength), and thermal properties. SEM microscopic photos were also taken to analyze the microstructure of the samples. The addition of a 5% by-weight organosilicon compound to polylactide resulted in a significant increase in MFR by 73.8% compared to the neat polymer. The greatest improvement in impact strength was achieved for the 5% SSQ-SH/PLA composite, increasing it by 32.0 kJ/m2 compared to PLA, which represents an increase of up to 187%. The conducted research confirms the possibility of modifying the properties of the polymer by employing organosilicon compounds. [ABSTRACT FROM AUTHOR]

This study delineates a methodology for the preparation of new composites based on a photocurable urethane-acrylate resin, which has been modified with (3-thiopropyl)polysilsesquioxane (SSQ-SH). The organosilicon compound combines fully enclosed cage structures and incompletely condensed silanols (a mixture of random structures) obtained through the hydrolytic condensation of (3-mercaptopropyl)trimethoxysilane. This process involves a thiol-ene "click" reaction between SSQ-SH and a commercially available resin (Ebecryl 1271®) in the presence of the photoinitiator DMPA, resulting in composites with significantly changed thermal properties. Various tests were conducted, including thermogravimetric analysis (TGA), Fourier transmittance infrared spectroscopy (FT-IR), differential scanning calorimetry (Photo-DSC), and photoreological measurement mechanical property, and water contact angle (WCA) tests. The modification of resin with SSQ-SH increased the temperature of 1% and 5% mass loss compared to the reference (for 50 wt% SSQ-SH, T5% was 310.8 °C, an increase of 20.4 °C). A composition containing 50 wt% of SSQ-SH crosslinked faster than the reference resin, a phenomenon confirmed by photorheological tests. This research highlights the potential of new composite materials in coating applications across diverse industries. The modification of resin with SSQ-SH not only enhances thermal properties but also introduces a host of functional improvements, thereby elevating the performance of the resulting coatings. [ABSTRACT FROM AUTHOR]

In this study, organosilicon compounds were used as modifiers of filaments constituting building materials for 3D printing technology. Polymethylhydrosiloxane underwent a hydrosilylation reaction with styrene, octadecene, and vinyltrimethoxysilane to produce new di- or tri-functional derivatives with varying ratios of olefins. These compounds were then mixed with silica and incorporated into the ABS matrix using standard processing methods. The resulting systems exhibited changes in their physicochemical and mechanical characteristics. Several of the obtained composites (e.g., modified with VT:6STYR) had an increase in the contact angle of over 20° resulting in a hydrophobic surface. The addition of modifiers also prevented a decrease in rheological parameters regardless of the amount of filler added. In addition, comprehensive tests of the thermal decomposition of the obtained composites were performed and an attempt was made to precisely characterize the decomposition of ABS using FT-IR and optical microscopy, which allowed us to determine the impact of individual groups on the thermal stability of the system. [ABSTRACT FROM AUTHOR]

This paper discusses the historical beginnings and the current state of knowledge of the synthesis of organosilicon compounds and chlorine derivatives of silicon. The key importance of these compounds for modern industry, including the semiconductor industry (photovoltaic cells, microprocessors, memory chips and many other electronic elements) is highlighted. Significant environmental threats related to the production of these compounds and the research challenges aimed at their elimination are discussed. The complexity of the catalytic mechanism of direct reaction of silicon with CH3Cl and alcohols is presented in an accessible way. In the last part of the work, the directions of the development of direct synthesis technology in line with the principles of green chemistry are indicated. [ABSTRACT FROM AUTHOR]

Anti-icing coatings have provided a very good alternative to current, uneconomic, active deicing methods, and their use would bring a number of significant benefits to many industries, such as aviation and energy. Some of the most promising icephobic surfaces are those with hydrophobic properties. However, the relationship between hydrophobicity and low ice adhesion is not yet clearly defined. In this work, chemical modification of an epoxy gelcoat with chemical modifiers from the group of double organofunctionalized polysiloxanes (generally called multifunctionalized organosilicon compounds (MFSCs)) was applied. The anti-icing properties of manufactured coatings were determined by means of measurements of shear strength between the ice layer and the modified surface, conducted using a tensile machine. In the work, tests were also performed on the roughness, wettability, and durability of the properties in an aging chamber. It was found that the performed modifications of the coating's chemical composition by the addition of polysiloxanes enabled us to reduce ice adhesion by 51% and to increase the water contact angle by 14% in comparison to the neat gelcoat. A reduction in ice adhesion was also observed with the increasing water contact angle and with decreasing surface roughness. In addition, only one modification recorded an increase in ice adhesion after exposure in the aging chamber. [ABSTRACT FROM AUTHOR]

In this study, the influence of TiO2 pigment filler modified with spherosilicate derivatives on the processes and thermomechanical properties of composites based on PLA was investigated. Rheological tests (MFR) were carried out, on the basis of which it was found that the addition of organosilicon compounds has a plasticizing effect on the polymer-filler systems. TGA and DSC analysis were performed. The analysis of the contact angle showed that 1.5% of the additives had an influence on the superhydrophobic properties of TiO2 (above 135°), and a slight improvement of this parameter was also observed for composites containing the modified pigment. Microscopic analysis and mechanical tests (tensile strength, impact strength and flexural strength tests) were carried out as well. It has been observed that the addition of certain derivatives adversely affects the dispersion of the filler, thus a slight improvement in mechanical properties is observed. For modifiers that do not affect filler agglomeration, a plasticizing effect on the composite is observed. [ABSTRACT FROM AUTHOR]

In this work, silsesquioxane and spherosilicate compounds were assessed as novel organosilicon coupling agents for surface modification of TiO2 in a green process, and compared with their conventional silane counterparts. The surface-treated TiO2 particles were then applied in preparation of epoxy (EP) composites and the aspects of pigment dispersion, suspension stability, hiding power, as well as the composite mechanical and thermal properties were discussed. The studied compounds loading was between 0.005–0.015% (50–150 ppm) in respect to the bulk composite mass and resulted in increase of suspension stability and hiding power by over an order of magnitude. It was found that these compounds may be an effective alternative for silane coupling agents, yet due to their low cost and simplicity of production and manipulation, silanes and siloxanes are still the most straight-forward options available. Nonetheless, the obtained findings might encourage tuning of silsesquioxane compounds structure and probably process itself if implementation of these novel organosilicon compounds as surface treatment agents is sought for special applications, e.g., high performance coating systems. [ABSTRACT FROM AUTHOR]

This work concerns research on the use of inorganic chemical compounds Fe 2 O 3 , Fe 3 O 4 , and Al and organosilicon modifiers used as additives controlling the properties of PLA for material extrusion in 3D printing technology. The addition of inorganic compounds reduces the temperature at the beginning of the composite decomposition, which is related to the presence of metal and metal oxides. An effect of inhibition of catalytic activity was also noticed as a result of the addition of organosilicon compounds. An increase in the melt flow index parameter was observed, making improving the extrusion and 3D printing process possible. The presence of inorganic additives results in a better fusion of the print paths, which leads to reduced structure defects and better interlayer adhesion. The tensile strength of the obtained composite samples decreases with the increase in the concentration of the metal and metal oxides. The addition of organosilicon substances increases the tensile strength regardless of the inorganic compound concentration. The highest increase in tensile strength was obtained for the PLA/12.5% Fe 3 O 4 /OSS-5OD-3TMOS sample and it was 24.35% compared to the sample without the addition of organosilicon compounds. The use of organosilicon additives resulted in an increase in the water contact angle. [Display omitted] [ABSTRACT FROM AUTHOR]