The fabrication of new membrane that is able to produce stable high power density is essential for the development of pressure retarded osmosis (PRO) technology. In this work, thin film composite (TFC) polyetherimide membranes with three different substrate structures were fabricated and characterized. The PRO performance of the resultant membrane was evaluated through two pressure cycle experiments and stability tests. The primary objective of this work is to systematically study PRO membrane’s mechanical stability and mass transfer properties under high operating pressures, which determine the power density of the membrane in the PRO process. Experiments revealed that water permeability ( A p ) and salt permeability ( B p ) under different pressures varied. The A p and B p are better indicators for examining the variation of PRO membrane structure under pressure. Within the operating pressure range of 17.2 bar, the top polyamide layer of TFC PEI-2# membrane mainly experienced a reversible deformation. In the two pressure cycle tests, the water flux, specific salt flux and power density obtained in the upward and downward measurements in each cycle are close to each other. The first cycle and the second cycle also show excellent reproducibility. The membrane was able to maintain almost unchanged water flux and power density of 12.8 W/m 2 at 17.2 bar over the 10 h testing time, suggesting the membrane’s great potential to be used in practical application in the future. [ABSTRACT FROM AUTHOR]

Abstract: Polyamide thin film composite (TFC) membranes with tailored porous substrate and rejection layer are promising for forward osmosis (FO) applications. The current study investigates the effect of rejection layer synthesis conditions on the performance of the resulting TFC polyamide FO membranes. The influence of monomer concentrations (i.e., m-phenylenediamine (MPD) and trimesoyl chloride (TMC) concentrations) on the membrane separation properties as well as FO performance was systematically studied. A strong trade-off between the water permeability and salt rejection was observed, where increasing the TMC concentration or reducing the MPD concentration resulted in higher membrane permeability but lower salt rejection. In FO tests, membranes with poor salt rejection had severe solute reverse diffusion, which enhanced the internal concentration polarization (ICP). It was found that the FO water flux was governed by both the membrane water permeability and its solute rejection. For a membrane with higher water permeability but lower solute rejection, the reduced membrane frictional resistance was compensated by the simultaneously more severe solute-reverse-diffusion-induced ICP. The net effect on the FO water flux depends on the competition of these two opposing mechanisms. Under conditions where solute reverse diffusion may cause severe ICP (e.g., high draw solution concentration and high water flux level), membranes need be optimized to achieve a high salt rejection even if this is at the expense of lower water permeability. [Copyright &y& Elsevier]