Black-phase formamidinium lead iodide (FAPbI3), with a narrow bandgap and high thermal stability, has emerged as an in-demand material for highly efficient perovskite solar cells (PSCs). In a two-step sequential deposition, the PbI2 film plays an important role in the formation of a perovskite film with desirable qualities. This paper explores using N-methyl-2-pyrrolidone (NMP), a strong Lewis base, and N,N-dimethylformamide (DMF) as a mixed precursor solvent (DMF/NMP) of PbI2 and reports on preparing PbI2 films with a porous morphology by thermal treatment. Porous PbI2 films ensure the diffusion and sufficient reaction of the formamidinium iodide solution to form a smooth perovskite film. In addition, a dynamic spin coating method is also introduced to improve the uniformity of the perovskite film. Both methods yield a pure α-phase FAPbI3 film immediately in the unannealed state, which is necessary for the perovskite film to maintain phase stability. Finally, PSCs with a power conversion efficiency of 21.20% (0.13 cm2) are fabricated and optimized. The unencapsulated PSCs retain 90% of the initial efficiency for 1000 hours in dry air and exhibit a good thermal stability when heated to 85 °C. [ABSTRACT FROM AUTHOR]

• The perovskite film was prepared by ultrasonic spraying method. • Isopropyl alcohol (IPA), a green solvent with low boiling point, was introduced into perovskite precursor solution. • IPA-based PSCs exhibit the champion device efficiency of 22.43 %. The ultrasonic spray coating has been shown to be an effective technique for scaling up production. The nucleation and crystallization process of the perovskite film prepared by the ultrasonic spraying approach is more complicated than that by the spin coating, but they are essential to gaining efficient perovskite solar cells (PSCs). At the same time, the green solvent is the primary problem that must be solved in the process of PSCs commercialization. In this paper, the low boiling point and green solvent isopropyl alcohol (IPA) is introduced into the perovskite precursor solution to prepare FAPbI 3 perovskite by ultrasonic spraying. The addition of IPA enhanced the saturated vapor pressure of the precursor solution, which can create the local chemical microenvironment on the film surface and subsequently retard the nucleation rate from 8.31 s to 8.54 s at nucleation stage. The local chemical improves the initial homogeneity of the sol–gel phase and then leads to improved structural and optoelectronic properties within the FAPbI 3 film via sufficient crystallization from the sol–gel phase to α-FAPbI 3. Ultimately, IPA-based PSCs exhibit the champion device efficiency of 22.43 %. The good long-term stability of PSCs (maintain more than 90 % of the initial efficiency after 1000 h, and keep 80 % after 400 h) in ambient conditions. [ABSTRACT FROM AUTHOR]