Zr57Cu15Ni10Nb5 (more known as Vit-106) is a promising zirconium-based alloy with a high glass-forming ability, and belongs to the so-called bulk metallic glasses (BMG). Workpieces with a size of around one centimeter in all three dimensions can be obtained from a BMG alloy by casting. However, further increasing the cast size decreases the cooling rate and thus induces crystallization. Selective laser melting (SLM) is a well-known technique to overcome size limitations for BMGs because a workpiece is built by the addition of multiple melt portions in which the cooling rate is kept above the critical one. Currently, BMG parts obtained by SLM suffer from partial crystallization. The present work studies the influence of SLM process parameters on the partial crystallization of Vit-106 by metallography and the influence of the microstructure on mechanical properties by microhardness and wear resistance testing. Submicron crystalline inclusions are observed in an amorphous matrix of a Vit-106 alloy obtained by SLM. The size and the concentration of the inclusions can be controlled by varying the laser scanning speed. It is shown that submicron crystalline inclusions formed in the amorphous matrix during SLM can favorably affect microhardness and wear resistance. [ABSTRACT FROM AUTHOR]

Phase composition and microstructure of initial WC, BK8 (powder alloy 92 wt.% WC-8 wt.% Co), Co powders, ball-milled powders with four different compositions (1) 25 wt.% WC-75 wt.% Co, (2) 30 wt.% BK8-70 wt.% Co, (3) 50 wt.% WC-50 wt.% Co, (4) 94 wt.% WC-6 wt.% Co, and bulk alloys obtained by selective laser melting (SLM) from as-milled powders in as-melted state and after heat treatment were investigated by scanning electron microscopy and X-ray diffraction analysis. Initial and ball-milled powders consist of WC, hexagonal a-Co and face-centered cubic b-Co. The SLM leads to the formation of major new phases W3Co3C, W4Co2C and face-centered cubic b-Co-based solid solution. During the heat treatment, there occurs partial decomposition of the face-centered cubic b-Co-based solid solution with the formation of W2C and hexagonal a-Co solid solution. The microstructure of obtained bulk samples, in general, corresponds to the observed phase composition. [ABSTRACT FROM AUTHOR]