Search

A systematic investigation of the electrical characteristics of $\beta$-Ga$_2$O$_3$ Schottky barrier diodes (SBDs) has been conducted under high dose $^{60}$Co gamma radiation up to 5 Mrad (Si). Initial exposure of the diodes to 1 Mrad (Si) resulted in a significant decrease in on-current by $\sim$78% and an increase in on-resistance from $\sim$3 m$\Omega \cdot$cm$^2$ to $\sim$14 m$\Omega \cdot$cm$^2$ compared to the pre-radiation condition, likely due to the generation of radiation-induced deep-level acceptor traps. However, upon exposure to higher doses of gamma radiation (3 and 5 Mrad (Si)) over a prolonged duration, the device performance partially recovered due to a radiation annealing effect. This effect is facilitated by secondary electrons generated through Compton scattering, which dissipate kinetic energy as heat throughout the lattice, thereby annealing the trapping centers responsible for device performance degradation. The capacitance-voltage (C-V) characterization revealed that the net carrier concentration in the $\beta$-Ga$_2$O$_3$ drift layer reduced from $\sim$3.19 $\times$ 10$^{16}$ cm$^{-3}$ to $\sim$3.05 $\times$ 10$^{16}$ cm$^{-3}$ after 5 Mrad (Si) irradiation. Temperature-dependent I-V characteristics showed that irradiation leads to a reduction in both forward and reverse current across all investigated temperatures ranging from 25 to 250$^\circ$C, accompanied by slight increases in on-resistance, ideality factors, and Schottky barrier heights. The reverse breakdown characteristics of the $\beta$-Ga$_2$O$_3$ SBDs showed a slight increase of the breakdown voltage after radiation. Overall, $\beta$-Ga$_2$O$_3$ Schottky diode exhibits high resilience to gamma irradiation, with performance degradation mitigated by radiation-induced self-recovery, highlighting its potential for radiation-hardened electronic applications in extreme environments.

This letter reports a highly scaled 90 nm gate length beta-Ga2O3 T-gate MOSFET with no current collapse and record power gain cut off frequency (fMAX). The epitaxial stack of 60 nm thin channel MOSFET was grown by Molecular Beam Epitaxy (MBE) and highly doped (n++) contact regrowth was carried out by Metal Organic Chemical Vapour Deposition (MOCVD) in the source/drain region. Maximum on current (IDS, MAX) of 160 mA/mm and transconductance (gm) around 36 mS/mm was measured at VDS= 10 V for LSD= 1.5 micrometer channel length. Transconductance is limited by higher channel sheet resistance (Rsheet). We observed no current collapse for both drain and gate lag measurement even at higher VDG,Q quiescent bias points. This is the first report of Ga2O3 FET showing no current collapse without any external passivation. Breakdown voltage around 125 V was reported for LGD= 1.2 micrometer. We extracted 27 GHz current gain cut off frequency (fT) and 55 GHz fMAX for 20 V drain bias. fMAX value mentioned here is the highest for Ga2O3 and the first demonstration of 55 GHz operation. fT. VBR product of 3.375 THz.V has been calculated which is comparable with state-of-art GaN HEMT. This letter suggests that Ga2O3 can be a suitable candidate for X-band application.

The lack of p-type doping has impeded the development of vertical gallium oxide (Ga2O3) devices. Current blocking layers (CBL) using implanted deep acceptors has been used to demonstrate vertical devices. This paper presents the first demonstration of in situ Mg-doped beta-Ga2O3 CBLs grown using metalorganic chemical vapor deposition. Device structures were designed with in-situ Mg doped layers with varied targeted Mg doping concentrations, which were calibrated by quantitative secondary ion mass spectroscopy (SIMS). The effectiveness of the CBL is characterized using temperature dependent current-voltage measurements using n-Mg-doped-n structures, providing crucial insight into the underlying mechanisms. To further validate the experimental results, a TCAD simulation is performed and the electrically active effective doping is found to be dependent on the Mg-doping density, offering a new perspective on the optimization of CBL performance. Breakdown measurements show a 3.4 MV/cm field strength. This study represents a significant step forward in the development of Ga2O3-based devices and paves the way for future advancements in this exciting field.

This letter reports high-performance $\mathrm{\beta} Ga2O3 thin channel MOSFETs with T-gate and degenerately doped source/drain contacts regrown by MOCVD. Gate length scaling (LG= 160-200 nm) leads to a peak drain current (ID,MAX) of 285 mA/mm and peak trans-conductance (gm) of 52 mS/mm at 10 V drain bias with 23.5 Ohm mm on resistance (Ron). A low metal/n+ contact resistance of 0.078 Ohm mm was extracted from TLM measurement. Ron is dominated by interface resistance between channel and regrown layer. A gate-to-drain breakdown voltage of 192 V is measured for LGD = 355 nm resulting in average breakdown field (E_AVG) of 5.4 MV/cm. This E_AVG is the highest reported among all sub-micron gate length lateral FETs. RF measurements on 200 nm Silicon Nitride (Si3N4) passivated device shows a current gain cut off frequency (f_T) of 11 GHz and record power gain cut off frequency (f_MAX) of 48 GHz. The f_T.V_Br product is 2.11 THz.V for 192 V breakdown voltage. The switching figure of merit exceeds that of silicon and is comparable to mature wide-band gap devices.

Epitaxial growth of \k{appa}-phase Ga2O3 thin films are investigated on c-plane sapphire, GaN- and AlNon-sapphire, and (100) oriented yttria stabilized zirconia (YSZ) substrates via metalorganic chemical vapor deposition (MOCVD). The structural and surface morphological properties are investigated by comprehensive material characterization. Phase pure \k{appa}-Ga2O3 films are successfully grown on GaN-, AlN-on sapphire, and YSZ substrates through a systematical tuning of the growth parameters including the precursor molar flow rates, chamber pressure and growth temperature, whereas the growth on c-sapphire substrates leads to a mixture of \b{eta}- and \k{appa}polymorphs of Ga2O3 under the investigated growth conditions. The influence of the crystalline structure, surface morphology and roughness of \k{appa}-Ga2O3 films grown on different substrates are investigated as a function of precursor flow rate. High resolution scanning transmission electron microscopy (HR-STEM) imaging of \k{appa}-Ga2O3 films reveals abrupt interfaces between the epitaxial film and the sapphire, GaN and YSZ substrates. The growth of single crystal orthorhombic \k{appa}Ga2O3 films is confirmed by analyzing the STEM nano-diffraction pattern. The chemical composition, surface stoichiometry, and the bandgap energies of \k{appa}-Ga2O3 thin films grown on different substrates are studied by high resolution x-ray photoelectron spectroscopy (XPS) measurements. The type-II (staggered) band alignments at three interfaces between \k{appa}-Ga2O3 and c-sapphire, AlN, and YSZ substrates are determined by XPS, with the exception of \k{appa}-Ga2O3/GaN interface, which shows type I (straddling) band alignment.

In this paper, we have demonstrated the large-size free-standing single-crystal b-Ga2O3 NMs fabricated by the hydrogen implantation and lift-off process directly from MOCVD grown b-Ga2O3 epifilms on native substrates. The optimum implantation conditions were simulated with a Monte-Carlo simulation to obtain the high hydrogen concentration with a narrow ion distribution at the desired depth. Two as grown b-Ga2O3 samples with different orientation ([100] and [001]) were used and successfully create 1.2 um thick b-Ga2O3 NMs without any physical damages. These b-Ga2O3 NMs were then transfer-printed onto rigid and flexible substrates such as SiC substrate and polyimide substrate. Various material characterizations were performed to investigate the crystal quality, surface morphology, optical property, mechanical property, and bandgap before and after the lift-off and revealed that good material quality is maintained. This result offers several benefits in that the thickness, doping, and size of b-Ga2O3 NMs can be fully controlled. Moreover, more advanced b-Ga2O3-based NM structures such as (AlxGa1-x)2O3/Ga2O3 heterostructure NMs can be directly created from their bulk epitaxy substrates thus this result provides a viable route for the realization of high performance b-Ga2O3 NM-based electronics and optoelectronics that can be built on various substrates and platforms.

In this work, the interaction of n-type dopants in Si doped (AlxGa1-x)2O3 films with varying Al content over the entire composition range (x = 0-100%) was analyzed using atom probe tomography. An almost uniform dopant distribution with dopant density in the range of 1018 cm-3 was obtained in all (AlxGa1-x)2O3 layers containing different Al contents. We have demonstrated that for the single phase \b{eta}-(AlxGa1-x)2O3 films with Al content of x<0.30, dopants prefer to occupy on Ga sites while Al site is preferred for high Al content (x>0.50) (AlxGa1-x)2O3 layers. It was also observed for Al content, x = 0.30-0.50, no specific cationic site occupancy was observed, Si occupies either Al or Ga sites. This can be attributed to highly inhomogeneous layers within this composition range due to which dopant Si atoms are either in the Al-rich or Al-depleted regions.

The performance of ultra-wide band gap materials like $\beta$-Ga$_\mathrm{2}$O$_\mathrm{3}$ is critically dependent on achieving high average electric fields within the active region of the device. In this report, we show that high-k gate dielectrics like BaTiO$_\mathrm{3}$ can provide an efficient field management strategy by improving the uniformity of electric field profile in the gate-drain region of lateral field effect transistors. Using this strategy, we were able to achieve high average breakdown fields of 1.5 MV/cm and 4 MV/cm at gate-drain spacing (L$_\mathrm{gd}$) of 6 um and 0.6 um respectively in $\beta$-Ga$_\mathrm{2}$O$_\mathrm{3}$, at a high channel sheet charge density of 1.8x10$^\mathrm{13}$cm$^\mathrm{-2}$. The high sheet charge density together with high breakdown field enabled a record power figure of merit (V$^\mathrm{2}$$_\mathrm{br}$/R$_\mathrm{on}$) of 376 MW/cm$^\mathrm{2}$ at a gate-drain spacing of 3 um.

A new record-high room temperature electron Hall mobility (${\mu}_{RT} = 194\space cm^{2}/V\space s$ at $n\sim 8\times 10^{15}\space cm^{-3}$) for ${\beta}$-Ga2O3 is demonstrated in the unintentionally doped thin film grown on (010) semi-insulating substrate via metalorganic chemical vapor deposition (MOCVD). A peak electron mobility of $\sim 9500\space cm^{2}/V\space s$ is achieved at 45 K. Further investigation on the transport properties indicate the existence of sheet charges near the epi-layer/substrate interface. Si is identified as the primary contributor to the background carrier in both the epi-layer and the interface, originated from both surface contamination as well as growth environment. Pre-growth hydrofluoric acid cleaning of the substrate lead to an obvious decrease of Si impurity both at interface and in epi-layer. In addition, the effect of MOCVD growth condition, particularly the chamber pressure, on the Si impurity incorporation is studied. A positive correlation between the background charge concentration and the MOCVD growth pressure is confirmed. It is noteworthy that in a ${\beta}$-Ga2O3 film with very low bulk charge concentration, even a reduced sheet charge density can play an important role in the charge transport properties., Comment: 19 pages, 5 figures