Search

The plasma-based surface modification of polymer materials with desirable bulk properties is a useful way to obtain polymers with tailor-made surface properties. This is necessary because the surface properties of most engineering polymers in use today are less then optimum for many applications. New functionalities such as biocompatibility, adhesion, special functional groups as well as lubricative, friction and wear-and-tear properties are demanded. By optimization of the process parameters during a low pressure plasma treatment, most of these requirements can be fulfilled. A specific functionalization with, e.g., carboxyl, amino, epoxy or hydroxyl groups as well as the generation of ultra thin layers with those functionalities is possible. The most challenging problem is not only to find parameters which do not lead to a fragmentation of the monomeric structure, but moreover the adhesion of the thin films to the substrates must overcome a stability test without delamination. To optimize plasma processes, with their great variety of parameters influencing the obtained surface properties, several surface analytical techniques are indispensable. XPS, AES as well as AFM are helpful tools to characterize the modified sample surfaces and consequently optimize the set of parameters for the glow discharge treatment. With XPS the retention of the monomer structure can be controlled. AES depth profiling clarifies the elemental composition of gradient layers, necessary for a good adhesion of scratch-resistant coatings. AFM visualizes the surface morphology which is important for, e.g., the friction properties of plasma-coated substrates. [ABSTRACT FROM AUTHOR]

Graphical abstract Highlights • Poly-3-hydroxybutyrate (PHB) films were plasma-treated in NH 3 , Ar and NH 3 /Ar mixtures. • Surface chemistry and topography changes were observed in PHB films. • A significant decrease in contact angle and an increase in free surface energy were observed. • Fibroblast cell adhesion was significantly improved after Ar plasma treatment. Abstract Poly-3-hydroxybutyrate (PHB) films were plasma-treated using pure NH 3 , pure Ar or mixtures of the two different proportions (20%, 30%, 40%, 50%, 70% NH 3 in Ar). Surface chemistry and surface topography changes of PHB films were observed after plasma processing in all plasma regimes. The XPS results confirmed the absence of chemical modification in the case of pure Ar plasma treatment. Nitrogen-containing groups (e.g., N C O) were detected on the surfaces of P3HB films treated with NH 3 -containing plasma. The surfaces of the untreated P3HB films were hydrophobic, and plasma treatment turned the surfaces hydrophilic, irrespective of the treatment. A significant decrease in the contact angle and an increase in the free surface energy were observed. An insignificant surface ageing effect was observed when P3HB samples were exposed to air for 10 days. In NIH 3T3 mice fibroblast cells, cell adhesion was significantly improved after plasma treatment in an Ar atmosphere, which is likely related to the fact that there was a surface ξ potential of 88.6 mV at neutral pH, causing a cleavage of the polymer chains and an increase in surface roughness. [ABSTRACT FROM AUTHOR]

The oxygen and ammonia radio-frequency (RF) plasma treatment of poly(3-hydroxybutyrate) P3HB films was performed. We revealed significant changes in the topography, a decrease in the surface zeta potential from −63 to −75 mV after the oxygen–plasma treatment and an increase after ammonia plasma treatment from −63 to −45 mV at a pH of 7.4. Investigations into the NIH 3T3 fibroblast adhesion and growth demonstrated the best cell vitality and a higher cell number for the ammonia plasma treatment at 150 W. [ABSTRACT FROM AUTHOR]