Search

In this study, we investigated the effects of the modification of bacterial cellulose used as a template on the in situ polymerization of catechol by laccase. The bacterial cellulose was modified by sulfonation and the entrapment of carboxymethyl cellulose. The catechol polymerization was optimized at a pH of 5.5, catechol concentration of 50 mM, and synthesis time of 24 h. After the in situ polymerization, conductive and colored bacterial cellulose composites were obtained. The bacterial cellulose composites containing oligomers/polymers were analyzed using Fourier-transform infrared spectroscopy, scanning electron microscopy, and color strength measurements, and the conductivity of the bacterial cellulose composites was evaluated using a four-probe method. The results revealed that the modification of bacterial cellulose as a template for catechol oxidation resulted in the production of fibers with enhanced coloration and conductive properties owing to the presence of the enzymatically-obtained polymers. The results suggest the promising potential of both sulfonated bacterial cellulose and carboxymethyl cellulose-bacterial cellulose as templates for the formation of other functional polymers and composite materials. [ABSTRACT FROM AUTHOR]

Conductive and colored bacterial cellulose (BC) was developed by entrapment of polyaniline (PANi) onto dry BC membranes. The polyaniline was produced by in situ green polymerization of aniline by Myceliophthora thermophila laccase at pH = 4, 25°C, in the presence of a mediator, 1-hydroxybenzotriazol (HBT), using two different reactors, a water bath (WB) and an ultrasonic bath (US). MALDI-TOF and 1H NMR characterization of the experiment solutions confirmed the efficient polymerization of aniline by laccase. The dried BC membranes with entrapped polyaniline showed electrical conductive behavior and strong coloration, opening novel routes for the exploitation of functionalized bacterial cellulose as a green material for technical textiles, wearables, and other applications. [ABSTRACT FROM AUTHOR]

Bacterial cellulose (BC) was obtained by static cultivation using commercial BC gel from scoby. BC membranes (oven dried and freeze-dried) were swelled with 8% NaOH, in the absence and in the presence of ultrasound (US), for 30, 60, and 90 min. The influence of swelling conditions on both physico-chemical properties and molecules entrapment was evaluated. Considering the highest levels of entrapment, an optimum swelling procedure was established: 8% NaOH for 30 min at room temperature in the presence of US. Native and PEGylated laccase from Myceliophthora thermophila was immobilized on BC membranes and a different catalytic behaviour was observed after immobilization. Native laccase presented activity values similar to published reports (5-7 U/gBC) after immobilization whereas PEGylated enzymes showed much lower activity (1-2 U/gBC). BC swelled membranes are presented herein as a potential support for the preparation of immobilized enzymes for industrial applications, like phenolics polymerization. [ABSTRACT FROM AUTHOR]

Conductive cotton fabrics were obtained via in situ aniline polymerization by laccase from Myceliophthora thermophila under mild reaction conditions without the addition of strong proton acids. The reactions were conducted using two types of reactors, namely a water bath (WB) and an ultrasonic bath (US), and the role of a mediator, 1-hydroxybenzotriazol (HBT), on the laccase-assisted polymerization of aniline was investigated. A similar polymerization degree was obtained when using both reactors—however, the ultrasonic bath allowed the experiments to be conducted in shorter periods of time (24 h for WB vs. 2 h for US). The data obtained also revealed that the mediator (1-hydroxybenzotriazol-HBT) played a crucial role in aniline oxidation. A higher conversion yield and polymerization degree were obtained when the reaction was conducted in the presence of this compound, as confirmed by MALDI-TOF analysis. The cotton fabrics coated with polyaniline presented deep coloration and conductivity, especially when the mediator was included on the reactional system. The results obtained are a step forward in the enzymatic polymerization of aniline with the purpose of obtaining coloured conductive textile surfaces, with potential applications in wearable electronics. [ABSTRACT FROM AUTHOR]