Search

Compression creep experiments of Douglas-fir wood (Pseudotsuga menziesii) were performed at high temperature (150°C, 160°C, and 170°C) and under various conditions of steam pressure. The results established that environment conditions had a significant effect on compressive deformation, with the largest deformation obtained under saturated steam conditions. While the temperature significantly affected the compressive deformation of specimens under transient conditions, the temperature within the range studied had little effect on the compressive deformation in saturated steam. Furthermore, in specimens compressed under superheated and transient steam conditions, primary creep behavior was exhibited; while in specimens compressed under saturated steam conditions, creep deformation appeared to enter directly into secondary creep. Moreover, in saturated steam specimens very little creep was observed due to high initial deformation and little potential for additional cell wall buckling. The compressive creep measurements of Douglas-fir were compared with compressive creep of hybrid poplar (Populus deltoides×Populus trichocarpa). Due to lower initial density, and perhaps smaller microfiber angle and lower lignin content of tension wood, the compressive creep modulus of hybrid poplar was lower than Douglas-fir. Therefore, compressive deformation of Douglas-fir, at nearly all examined steam conditions and temperatures, was smaller than compressive deformation of hybrid poplar. [ABSTRACT FROM AUTHOR]

In this paper, the compressive deformation of hybrid poplar wood ( Populus deltoides × Populus trichocarpa) at high temperature (150, 160, and 170°C) and under various conditions of steam pressure was studied. Temperature and conditions of steam environment affected the relative density change and creep deformation during compression, as well as properties of the resulting densified material. While the temperature significantly affected the compression deformation of specimens compressed under transient and superheated steam conditions, temperature within the range studied had little effect on the compressive deformation in saturated steam. In all tested conditions, compression deformation was achieved without cell wall fractures. Higher temperature of compression, regardless of steam condition, resulted in lower equilibrium moisture content. In specimens compressed under saturated steam, the modulus of rupture (MOR) and modulus of elasticity (MOE) were increased proportionally to the increase in density, while the compression under superheated steam produced lower increase in the MOE and MOR than expected based on the increase in density. Compression in transient steam conditions at 170°C produced densified wood with higher MOE and MOR than expected based on the increase in density. [ABSTRACT FROM AUTHOR]

Density profile relation to hardness of VTC wood composites was evaluated using X-ray densitometry and modified Brinell hardness method using different applied forces. Moreover, surface elasticity was evaluated. Prior to lamination, the low-density hybrid poplar ( Populus deltoides × Populus trichocarpa L.) and Douglas-fir ( Pseudotsuga menziesii L.) thin boards were compressed to 1.22 or 1.14 g/cm, respectively. Two different kinds of laminations were made, either single layer of 1.5 mm thickness or two 1.5-mm layers bonded to unmodified wood. The results show that thicker laminate has a great positive influence on Brinell hardness. This study suggests that results from the existing method for Brinell hardness are not comparable, and if applied force is chosen without restraint, the effect on the hardness value is significant for inhomogeneous wood composites. [ABSTRACT FROM AUTHOR]

Surface energy of yellow-poplar wood from three wood treatment groups was studied using sessile-drop contact-angle measurements and the Chang acid–base model for surface energy calculation. Water, glycerol, formamide, ethylene glycol and α-bromonaphthalene were used as probe liquids. Wood treatments were control, hygro-thermal treatment and densification. Contact angle trends for densified and hygro-thermally treated wood were found to be the same. Total surface energy decreased with both hygro-thermal treatment and densification. [ABSTRACT FROM AUTHOR]