Search

Hydrogen production from the thermochemical conversion of biomass was carried out with nano-sized NiZnAlOx catalysts using a two-stage fixed bed reactor system. The gases derived from the pyrolysis of wood sawdust in the first stage were catalytically steam reformed in the second stage. The NiZnAlOx catalysts were synthesized by a co-precipitation method with different Ni molar fractions (5, 10, 15, 25 and 35%) and a constant Zn:Al molar ratio of 1:4. The catalysts were characterized by a wide range of techniques, including N 2 adsorption, SEM, XRD, TEM and temperature-programmed oxidation (TPO) and reduction (TPR). Fine metal particles of size around 10–11 nm were obtained and the catalysts had high stability characteristics, which improved the dispersion of active centers during the reaction and promoted the performance of the catalysts. The yield of gas was increased from 49.3 to 74.8 wt.%, and the volumetric concentration of hydrogen was increased from 34.7 to 48.1 vol.%, when the amount of Ni loading was increased from 5 to 35%. Meanwhile, the CH 4 fraction decreased from 10.2 to 0.2 vol.% and the C 2 –C 4 fraction was reduced from 2.4 vol.% to 0.0 vol.%. During the reaction, the crystal size of all catalysts was successfully maintained at around 10–11 nm with lowered catalyst coke formation, (particularly for the 35NiZn4Al catalyst where negligible coke was found) and additionally no obvious catalyst sintering was detected. The efficient production of hydrogen from the thermochemical conversion of renewable biomass indicates that it is a promising sustainable route to generate hydrogen from biomass using the NiZnAl metal oxide catalyst prepared in this work via a two-stage reaction system. [ABSTRACT FROM AUTHOR]

The production of hydrogen-enriched syngas from the thermo-chemical conversion of biomass was studied using Ni/CaAlO x catalysts prepared by co-precipitation method. The effect of Ca addition with different molar ratios of Ca:Al (1:3, 1:2, 1:1, 2:1, 3:1) on the properties and catalytic behavior in relation to syngas production and the coke formation on the surface of the catalysts were investigated. Catalysts were characterized by BET, XRD, TPR, SEM, and TEM. The SEM and TEM results showed that rod-shaped nano-particles were highly dispersed on the surface of the catalyst. The particle size of NiO was slightly affected with the increase of Ca content in the catalyst. It appeared that the selectivity of CO was increased and the selectivity of CO 2 was reduced with the increase of Ca addition to the catalyst. For example, CO 2 concentration was reduced from 20 to 12 vol.%, when the molar ratio of Ca/Al was increased from 1:3 to 3:1 for the Ni/CaAlO x catalyst; it is suggested that the water gas shift reaction was inhibited and CO 2 reforming reactions were promoted in the presence of the catalyst with higher Ca content. The CO/H 2 molar ratio could be manipulated by changing the Ca content in the catalyst, while the H 2 concentration remained almost constant (around 45 vol.%). Thus, using the Ni/CaAlO x catalyst developed in this work could provide a promising route to control the syngas composition, which is an important factor for syngas applications. [ABSTRACT FROM AUTHOR]

Thermo-chemical processing of biomass is a promising alternative to produce renewable hydrogen as a clean fuel or renewable syngas for a sustainable chemical industry. However, the fast deactivation of catalysts due to coke formation and sintering limits the application of catalytic thermo-chemical processing in the emerging bio-refining industry. In this research, Fe–Zn/Al 2 O 3 nanocatalysts have been prepared for the production of hydrogen through pyrolysis catalytic reforming of wood sawdust. Through characterization, it was found that Fe and Zn were well distributed on the surface with a narrow particle size. During the reactions, the yield of hydrogen increased with the increase of Zn content, as Zn is an efficient metal promoter for enhancing the performance of the Fe active site in the reaction. The 20% Fe/Al 2 O 3 catalyst with Zn/Al ratio of 1:1 showed the best performance in the process in relation to the hydrogen production and resistance to coke formation on the surface of the reacted catalyst. All the catalysts showed ultra-high stability during the process and nearly no sintering were observed on the used catalysts. Therefore, the nanocatalysts prepared in this work from natural-abundant and low-cost metals have promising catalytic properties (high metal dispersion and stability) to produce H 2 -rich syngas with optimal H 2 /CO ratio from the thermo-chemical processing of biomass. [ABSTRACT FROM AUTHOR]