We present a transmon qubit fabrication technique that yields systematic improvements in T1 relaxation times. We encapsulate the surface of niobium and prevent the formation of its lossy surface oxide. By maintaining the same superconducting metal and only varying the surface, this comparative investigation examining different capping materials, such as tantalum, aluminum, titanium nitride, and gold, as well as substrates across different qubit foundries demonstrates the detrimental impact that niobium oxides have on coherence times of superconducting qubits, compared to native oxides of tantalum, aluminum or titanium nitride. Our surface-encapsulated niobium qubit devices exhibit T1 relaxation times 2–5 times longer than baseline qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 300 μs, with maximum values up to 600 μs. Our comparative structural and chemical analysis provides insight into why amorphous niobium oxides may induce higher losses compared to other amorphous oxides. [ABSTRACT FROM AUTHOR]

Continued advances in superconducting qubit performance require more detailed understandings of the many sources of decoherence. Within these devices, two-level systems arise due to defects, interfaces, and grain boundaries and are thought to be a major source of qubit decoherence at millikelvin temperatures. In addition to Al, Nb is a commonly used metallization layer in superconducting qubits. Consequently, a significant effort is required to develop and qualify processes that mitigate defects in Nb films. As the fabrication of complete superconducting qubits and their characterization at millikelvin temperatures is a time and resource intensive process, it is desirable to have measurement tools that can rapidly characterize the properties of films and evaluate different treatments. Here, we show that measurements of the variation of the superconducting critical temperature Tc with an applied external magnetic field H (of the phase boundary T c − H) performed with very high-resolution show features that are directly correlated with the structure of the Nb films. In combination with x-ray diffraction measurements, we show that one can even distinguish variations in the size and crystal orientation of the grains in a Nb film by small but reproducible changes in the measured superconducting phase boundary. [ABSTRACT FROM AUTHOR]