Search

In this work, new information concerning the optical properties of black phosphorus (BP) sheets chemically/electrochemically functionalized with diphenyl amine (DPA) and its macromolecular compound (poly(diphenylamine) (PDPA)) in the absence/presence of phosphotungstic acid (PTA) is reported. Raman scattering and FTIR spectroscopy studies indicate that the interaction of BP with PTA leads to the elimination of the PxOy layer onto the surface of the BP sheets. In the case of the chemical interaction of BP with DPA, the reaction product corresponds to DPA chemically functionalized BP sheets having an imino-phosphorane (IP) structure. The electrochemical oxidation of BP sheets chemically functionalized with DPA in the presence of PTA leads to an increase in the weight of P-N bonds as a consequence of the generation of PDPA doped with the PTA heteropolyanions, as shown by FTIR spectroscopy and Raman scattering. This process is evidenced by a shift of the Raman line from 362 cm−1 to 378 cm−1, assigned to the A1g mode. This change was explained by taking into account the compression of the layers containing P atoms, which is induced by PDPA macromolecular chains. The decrease in the intensity of the PL spectra of DPA as well as PDPA, in the presence of BP, indicates that BP acts as a PL quenching agent for these compounds. A preferential orientation of the PDPA doped with the PTA heteropolyanions on the surface of BP sheets is highlighted by the variation of the binding angle of the PDPA on the surface of BP sheets from 44.7° to 39.9°. [ABSTRACT FROM AUTHOR]

The effect of sodium thiosulfate (ST) on the photodegradation of azathioprine (AZA) was analyzed by UV-VIS spectroscopy, photoluminescence (PL), FTIR spectroscopy, Raman scattering, X-ray photoelectron (XPS) spectroscopy, thermogravimetry (TG) and mass spectrometry (MS). The PL studies highlighted that as the ST concentration increased from 25 wt.% to 75 wt.% in the AZA:ST mixture, the emission band of AZA gradual downshifted to 553, 542 and 530 nm. The photodegradation process of AZA:ST induced: (i) the emergence of a new band in the 320–400 nm range in the UV-VIS spectra of AZA and (ii) a change in the intensity ratio of the photoluminescence excitation (PLE) bands in the 280–335 and 335–430 nm spectral ranges. These changes suggest the emergence of new compounds during the photo-oxidation reaction of AZA with ST. The invoked photodegradation compounds were confirmed by studies of the Raman scattering, the FTIR spectroscopy and XPS spectroscopy through: (i) the downshift of the IR band of AZA from 1336 cm−1 to 1331 cm−1, attributed to N-C-N deformation in the purine ring; (ii) the change in the intensity ratio of the Raman lines peaking at 1305 cm−1 and 1330 cm−1 from 3.45 to 4.57, as the weight of ST in the AZA:ST mixture mass increased; and (iii) the emergence of a new band in the XPS O1s spectrum peaking at 531 eV, which was associated with the C=O bond. Through correlated studies of TG-MS, the main key fragments of ST-reacted AZA are reported. [ABSTRACT FROM AUTHOR]

We demonstrate that under continuous single-beam excitation, one can generate an abnormal anti-Stokes Raman emission (AASRE) whose properties are similar to a coherent anti-Stokes Raman scattering. The effect has been observed in mesoscopic materials, which possess intrinsically nonlinear properties [lithium niobate (LiNbO3), bismuth germanium oxide (Bi12GeO20; BGO), bismuth silicon oxide (Bi12GeO20; BSO)], which have a nonzero electric susceptibility of the third order, χ(³) ≠ 0. Corroborated Raman and coherent backscattering studies demonstrate that the occurrence of both effects is conditioned by the existence of a mesoscopic morphology of the sample, which is able to ensure efficient transport of the light inside the sample through a multiple light scattering mechanism. In this context, both AASRE and coherent backscattering effects are because of the Anderson localization of the light. [ABSTRACT FROM AUTHOR]

This paper prepared composites under the free membranes form that are based on thermoplastic polymers of the type of polyurethane (TPU) and polyolefin (TPO), which are blended in the weight ratio of 2:1, and ceramic nanoparticles (CNs) such as BaSrTiO3 and SrTiO3. The structural, optical, and conductive properties of these new composite materials are reported. The X-ray diffraction studies highlight a cubic crystalline structure of these CNs. The main variations in the vibrational properties of the TPU:TPO blend induced by CNs consist of the following: (i) the increase in the intensity of the Raman line of 1616 cm−1; (ii) the down-shift of the IR band from 800 to 791 cm−1; (iii) the change of the ratio between the absorbance of IR bands localized in the spectral range 950–1200 cm−1; and (iv) the decrease in the absorbance of the IR band from 1221 cm−1. All these variations were correlated with a preferential adsorption of thermoplastic polymers on the CNs surface. A photoluminescence (PL) quenching process of thermoplastic polymers is demonstrated to occur in the presence of CNs. The anisotropic PL measurements have highlighted a change in the angle of the binding of the TPU:TPO blend, which varies from 23.7° to ≈49.3° and ≈53.4°, when the concentration of BaSrTiO3 and SrTiO3 CNs, respectively, is changed from 0 to 25 wt. %. Using dielectric spectroscopy, two mechanisms are invoked to take place in the case of the composites based on TPU:TPO blends and CNs, i.e., one regarding the type of the electrical conduction and another specifying the dielectric–dipolar relaxation processes. [ABSTRACT FROM AUTHOR]