Polylactic acid (PLA) is a biodegradable polymer that can replace petroleum-based polymers and is widely used in material extrusion additive manufacturing (AM). The reprocessing of PLA leads to a downcycling of its properties, so strategies are being sought to counteract this effect, such as blending with virgin material or creating nanocomposites. Thus, two sets of nanocomposites based respectively on virgin PLA and a blend of PLA and reprocessed PLA (rPLA) with the addition of 0, 3, and 7 wt% of titanium dioxide nanoparticles (TiO2) were created via a double screw extruder system. All blends were used for material extrusion for 3D printing directly from pellets without difficulty. Scanning electron micrographs of fractured samples' surfaces indicate that the nanoparticles gathered in agglomerations in some blends, which were well dispersed in the polymer matrix. The thermal stability and degree of crystallinity for every set of nanocomposites have a rising tendency with increasing nanoparticle concentration. The glass transition and melting temperatures of PLA/TiO2 and PLA/rPLA/TiO2 do not differ much. Tensile testing showed that although reprocessed material implies a detriment to the mechanical properties, in the specimens with 7% nano-TiO2, this effect is counteracted, reaching values like those of virgin PLA. [ABSTRACT FROM AUTHOR]

This paper studies the thermal, morphological, and mechanical properties of 3D-printed polylactic acid (PLA) blends of virgin and recycled material in the following proportions: 100/0, 25/75, 50/50, and 75/25, respectively. Real waste, used as recycled content, was shredded and sorted by size without a washing step. Regular dog-bone specimens were 3D printed from filaments, manufactured in a single screw extruder. Thermogravimetric analysis indicated that adding PLA debris to raw material did not significantly impact the thermal stability of the 3D-printed samples and showed that virgin and recycled PLA degraded at almost the same temperature. Differential scanning calorimetry revealed a significant reduction in crystallinity with increasing recycled content. Scanning electron microscopy showed a more homogenous structure for specimens from 100% pure PLA, as well as a more heterogeneous one for PLA blends. The tensile strength of the PLA blends increased by adding more recycled material, from 44.20 ± 2.18 MPa for primary PLA to 52.61 ± 2.28 MPa for the blend with the highest secondary PLA content. However, this study suggests that the mechanical properties of the reprocessed parts and their basic association are unique compared with those made up of virgin material. [ABSTRACT FROM AUTHOR]