Search

Eupatorium adenophorum was utilized as raw materials for the preparation of activated carbon via microwave assisted steam activation. Influences of the three vital process parameters – activation temperature, activation duration and steam flow rate – have been assessed on the adsorption capacity and yield of Eupatorium adenophorum activated carbon (EAAC). The process parameters were optimized utilizing the Design Expert software and were identified to be an activation duration of 45 min, an activation temperature of 950 °C and a steam flow rate of 0.7 ml/min, with the resultant iodine number and yield being 1,010 mg/g and 20.13% respectively. The validity of process model to optimize the process parameters was verified using the analysis of variance (ANOVA). The key parameters that characterize quality of the porous carbon such as the BET surface area, total pore volume and average pore diameter were estimated to be 1,142 m2/g, 0.84 ml/g and 3.3 nm respectively, for the sample corresponding to the optimized process conditions. Additionally the pore structure is characterized using Scanning Electron Microscope (SEM). The present work strongly supports utilization of Eupatorium adenophorum as a potential precursor through microwave heating.

The dielectric properties of petroleum coke at five temperatures between 20 to100∘C, covering different moisture content levels at 2.45 GHz, were measured using an open-ended coaxial probe dielectric measurement system. The effects of drying temperature, duration of drying, and sample mass on the moisture content and dehydration rate of petroleum coke was assessed utilizing the response surface methodology. The dielectric constant, loss factor, and loss tangent were all found to increase nearly linearly with increase in moisture content. Three predictive empirical models were developed to relate the dielectric constant, loss factor, and loss tangent of petroleum coke as a linear function of moisture content from 3–10%. An increase in temperature between 20 to100∘Cwas found to increase the dielectric properties. The penetration depth was observed to increase linearly with decrease in moisture content in the range of 3 to 10%. A predictive empirical model was developed to calculate penetration depth for petroleum coke. Two mathematical models were established and analyzed using RSM to describe the relationship between the microwave drying conditions and the responses, moisture content, and dehydration rate. Statistical analysis with response surface regression showed that microwave drying temperature, duration of drying, and sample mass were significantly related to moisture content and dehydration rate. Based on the RSM analysis, the optimum process conditions were estimated to be a microwave drying temperature of75∘C, drying duration of 10 sec, and sample mass of 60 g, with the resultant moisture content being 0.34 at a dehydration rate of 2.94 g/min. [ABSTRACT FROM PUBLISHER]

Crofton weed was converted into a high-quality activated carbon (CWAC) via microwave-induced CO2 physical activation. The operational variables including activation temperature, activation duration and CO2 flow rate on the adsorption capability and activated carbon yield were identified. Additionally the surface characteristics of CWAC were characterized by nitrogen adsorption isotherms, FTIR and SEM. The operating variables were optimized utilizing the response surface methodology and were identified to be an activation temperature of 980 °C, an activation duration of 90 min and a CO2 flow rate of 300 ml/min with a iodine adsorption capacity of 972 mg/g and yield of 18.03%. The key parameters that characterize quality of the porous carbon such as the BET surface area, total pore volume and average pore diameter were estimated to be 1036m²/g, 0.71 ml/g and 2.75 nm, respectively. The findings strongly support the feasibility of microwave heating for preparation of high surface area porous carbon from Crofton weed via CO2 activation. [ABSTRACT FROM AUTHOR]