Search

The aim of this study was to evaluate and compare the biofilm formation properties of common pathogens associated with implant-related infections on two different implant material types. Bacterial strains tested in this study were Staphylococcus aureus, Streptococcus mutans, Enterococcus faecalis, and Escherichia coli. Implant materials tested and compared were PLA Resorb × polymer of Poly DL-lactide (PDLLA) comprising 50% poly-L-lactic acid and 50% poly-D-lactic acid) and Ti grade 2 (tooled with a Planmeca CAD-CAM milling device). Biofilm assays were done with and without saliva treatment to evaluate the effect of saliva on bacterial adhesion and to mimic the intraoral and extraoral surgical routes of implant placement, respectively. Five specimens of each implant type were tested for each bacterial strain. Autoclaved material specimens were first treated with 1:1 saliva-PBS solution for 30 min, followed by washing of specimens and the addition of bacterial suspension. Specimens with bacterial suspension were incubated for 24 h at 37 °C for biofilm formation. After 24 h, non-adhered bacteria were removed, and specimens were washed, followed by removal and calculation of adhered bacterial biofilm. S. aureus and E. faecalis showed more attachment to Ti grade 2, whereas S. mutans showed higher adherence to PLA in a statistically significant manner. The salivary coating of specimens enhanced the bacterial attachment by all the bacterial strains tested. In conclusion, both implant materials showed significant levels of bacterial adhesion, but saliva treatment played a vital role in bacterial attachment, therefore, saliva contamination of the implant materials should be minimized and considered when placing implant materials inside the body. [ABSTRACT FROM AUTHOR]

This study investigated two of the most commonly used CAD–CAM materials for patient-specific reconstruction in craniomaxillofacial surgery. The aim of this study was to access the biofilm formation of Staphylococcus aureus, Streptococcus mutans, Enterococcus faecalis, and Escherichia coli on titanium and PEEK medical implant materials. Two titanium specimens (titanium grade 2 tooled with a Planmeca CAD–CAM milling device and titanium grade 5 tooled with a computer-aided design direct metal laser sintering device (CAD-DMLS)) and one PEEK specimen tooled with a Planmeca CAD–CAM milling device were studied. Bacterial adhesion on implants was evaluated in two groups (saliva-treated group and non-saliva-treated group) to imitate intraoral and extraoral surgical routes for implant placement. The PEEK medical implant material showed higher bacterial adhesion by S. aureus, S. mutans, and E. coli than titanium grade 2 and titanium grade 5, whereas E. faecalis showed higher adhesion to titanium as compared to PEEK. Saliva contamination of implants also effected bacterial attachment. Salivary coating enhanced biofilm formation by S. aureus, S. mutans, and E. faecalis. In conclusion, our findings imply that regardless of the implant material type or tooling techniques used, salivary coating plays a vital role in bacterial adhesion. In addition, the majority of the bacterial strains showed higher adhesion to PEEK than titanium. [ABSTRACT FROM AUTHOR]

The aim of this study was to assess the biofilm formation of Streptococcus mutans, Staphylococcus aureus, Enterococcus faecalis, and Escherichia coli on titanium implants with CAD-CAM tooling techniques. Twenty specimens of titanium were studied: Titanium grade 2 tooled with a Planmeca CAD-CAM milling device (TiGrade 2), Ti6Al4V grade 5 as it comes from CAD-DMLS device (computer aided design-direct metal laser sintering device) (TiGrade 5), Ti6Al4V grade 23 as it comes from a CAD-CAM milling device (TiGrade 23), and CAD-DMLS TiGrade 5 polished with an abrasive disc (TiGrade 5 polished). Bacterial adhesion on the implants was completed with and without saliva treatment to mimic both extraoral and intraoral surgical methods of implant placement. Five specimens/implant types were used in the bacterial adhesion experiments. Autoclaved implant specimens were placed in petri plates and immersed in saliva solution for 30 min at room temperature and then washed 3× with 1× PBS. Bacterial suspensions of each strain were made and added to the specimens after saliva treatment. Biofilm was allowed to form for 24 h at 37 °C and the adhered bacteria was calculated. Tooling techniques had an insignificant effect on the bacterial adhesion by all the bacterial strains studied. However, there was a significant difference in biofilm formation between the saliva-treated and non-saliva-treated implants. Saliva contamination enhanced S. mutans, S. aureus, and E. faecalis adhesion in all material types studied. S. aureus was found to be the most adherent strain in the saliva-treated group, whereas E. coli was the most adherent strain in the non-saliva-treated group. In conclusion, CAD-CAM tooling techniques have little effect on bacterial adhesion. Saliva coating enhances the biofilm formation; therefore, saliva contamination of the implant must be minimized during implant placement. Further extensive studies are needed to evaluate the effects of surface treatments of the titanium implant on soft tissue response and to prevent the factors causing implant infection and failure. [ABSTRACT FROM AUTHOR]