Search

The in situ metalorganic chemical vapor deposition (MOCVD) growth of Al2O3 dielectrics on β-Ga2O3 and β-(AlxGa1−x)2O3 films is investigated as a function of crystal orientations and Al compositions of β-(AlxGa1−x)2O3 films. The interface and film qualities of Al2O3 dielectrics are evaluated by high-resolution x-ray diffraction and scanning transmission electron microscopy imaging, which indicate the growth of high-quality amorphous Al2O3 dielectrics with abrupt interfaces on (010), (100), and ( 2 ¯ 01) oriented β-(AlxGa1−x)2O3 films. The surface stoichiometries of Al2O3 deposited on all orientations of β-(AlxGa1−x)2O3 are found to be well maintained with a bandgap energy of 6.91 eV as evaluated by high-resolution x-ray photoelectron spectroscopy, which is consistent with the atomic layer deposited (ALD) Al2O3 dielectrics. The evolution of band offsets at both in situ MOCVD and ex situ ALD deposited Al2O3/β-(AlxGa1−x)2O3 is determined as a function of Al composition, indicating the influence of the deposition method, orientation, and Al composition of β-(AlxGa1−x)2O3 films on resulting band alignments. Type II band alignments are determined at the MOCVD grown Al2O3/β-(AlxGa1−x)2O3 interfaces for the (010) and (100) orientations, whereas type I band alignments with relatively low conduction band offsets are observed along the ( 2 ¯ 01) orientation. The results from this study on MOCVD growth and band offsets of amorphous Al2O3 deposited on differently oriented β-Ga2O3 and β-(AlxGa1−x)2O3 films will potentially contribute to the design and fabrication of future high-performance β-Ga2O3 and β-(AlxGa1−x)2O3 based transistors using MOCVD in situ deposited Al2O3 as a gate dielectric. [ABSTRACT FROM AUTHOR]

Growths of monoclinic (AlxGa1−x)2O3 thin films up to 99% Al contents are demonstrated via metalorganic chemical vapor deposition (MOCVD) using trimethylgallium (TMGa) as the Ga precursor. The utilization of TMGa, rather than triethylgallium, enables a significant improvement of the growth rates (>2.5 μm h−1) of β‐(AlxGa1−x)2O3 thin films on (010), (100), and (2¯01) β‐Ga2O3 substrates. By systematically tuning the precursor molar flow rates, growth of coherently strained phase pure β‐(AlxGa1−x)2O3 films is demonstrated by comprehensive material characterizations via high‐resolution X‐ray diffraction (XRD) and atomic‐resolution scanning transmission electron microscopy (STEM) imaging. Monoclinic (AlxGa1−x)2O3 films with Al contents up to 99, 29, and 16% are achieved on (100), (010), and (2¯01) β‐Ga2O3 substrates, respectively. Beyond 29% of Al incorporation, the (010) (AlxGa1−x)2O3 films exhibit β‐ to γ‐phase segregation. β‐(AlxGa1−x)2O3 films grown on (2¯01) β‐Ga2O3 show local segregation of Al along (100) plane. Record‐high Al incorporations up to 99% in monoclinic (AlxGa1−x)2O3 grown on (100) Ga2O3 are confirmed from XRD, STEM, electron nanodiffraction, and X‐ray photoelectron spectroscopy measurements. These results indicate great promises of MOCVD development of β‐(AlxGa1−x)2O3 films and heterostructures with high Al content and growth rates using TMGa for next‐generation high‐power and high‐frequency electronic devices. [ABSTRACT FROM AUTHOR]

Epitaxial growth of κ-phase Ga2O3 thin films is investigated on c-plane sapphire, GaN- and AlN-on-sapphire, and (100) oriented yttria stabilized zirconia (YSZ) substrates via metalorganic chemical vapor deposition. The structural and surface morphological properties are investigated by comprehensive material characterization. Phase pure κ-Ga2O3 films are successfully grown on GaN-, AlN-on-sapphire, and YSZ substrates through a systematical tuning of growth parameters including the precursor molar flow rates, chamber pressure, and growth temperature, whereas the growth on c-sapphire substrates leads to a mixture of β- and κ-polymorphs of Ga2O3 under the investigated growth conditions. The influence of the crystalline structure, surface morphology, and roughness of κ-Ga2O3 films grown on different substrates are investigated as a function of precursor flow rate. High-resolution scanning transmission electron microscopy imaging of κ-Ga2O3 films reveals abrupt interfaces between the epitaxial film and the sapphire, GaN, and YSZ substrates. The growth of single crystal orthorhombic κ-Ga2O3 films is confirmed by analyzing the scanning transmission electron microscopy nanodiffraction pattern. The chemical composition, surface stoichiometry, and bandgap energies of κ-Ga2O3 thin films grown on different substrates are studied by high-resolution x-ray photoelectron spectroscopy (XPS) measurements. The type-II (staggered) band alignments at three interfaces between κ-Ga2O3 and c-sapphire, AlN, and YSZ substrates are determined by XPS, with an exception of κ-Ga2O3/GaN interface, which shows type-I (straddling) band alignment. [ABSTRACT FROM AUTHOR]

Metalorganic chemical vapor deposition (MOCVD) growths of β-Ga2O3 on on-axis (100) Ga2O3 substrates are comprehensively investigated. Key MOCVD growth parameters including growth temperature, pressure, group VI/III molar flow rate ratio, and carrier gas flow rate are mapped. The dependence of the growth conditions is correlated with surface morphology, growth rate, and electron transport properties of the MOCVD grown (100) β-Ga2O3 thin films. Lower shroud gas (argon) flow is found to enhance the surface smoothness with higher room temperature (RT) electron Hall mobility. The growth rate of the films decreases but with an increase of electron mobility as the VI/III molar flow rate ratio increases. Although no significant variation on the surface morphologies is observed at different growth temperatures, the general trend of electron Hall mobilities are found to increase with increasing growth temperature. The growth rates reduce significantly with uniform surface morphologies as the chamber pressure increases. By tuning the silane flow rate, the controllable carrier concentration of (100) β-Ga2O3 thin films between low-1017 cm−3 and low-1018 cm−3 was achieved. Under optimized growth condition, an (100) β-Ga2O3 thin film with RMS roughness value of 1.64 nm and a RT mobility of 24 cm2/Vs at a carrier concentration of 7.0 × 1017 cm−3 are demonstrated. The mobilities are primarily limited by the twin lamellae and stacking faults defects generated from the growth interface. Atomic resolution scanning transmission electron microscopy reveals the formation of twin boundary defects in the films, resulting in the degradation of crystalline quality. Results from this work provide fundamental understanding of the MOCVD epitaxy of (100) β-Ga2O3 on on-axis Ga2O3 substrates and the dependence of the material properties on growth conditions. The limitation of electron transport properties of the (100) β-Ga2O3 thin films below 25 cm2/Vs is attributed to the formation of incoherent boundaries (twin lamellae) and stacking faults grown along the on-axis (100) crystal orientation. [ABSTRACT FROM AUTHOR]

This paper investigated the growth of (AlxGa1−x)2O3 thin films on semi-insulating (010) Ga2O3 substrates over the entire Al composition range (0% < x ≤ 100%) via metalorganic chemical vapor deposition (MOCVD). For the Al composition x < 27%, high quality single phase β-(AlxGa1−x)2O3 was achieved. A mixture of β and γ phases existed in (AlxGa1−x)2O3 when Al composition ranged between 27% and 40%, whereas a single γ-phase was observed for the films with Al composition x > 40%. The transition from the β to γ phase in AlGaO alloys was observed from x-ray diffraction spectra. The growth of γ-phase AlGaO with higher Al content was further confirmed via atomic resolution scanning transmission electron microscopy imaging and nanodiffraction. Compositional and statistical analyses performed on data acquired from atom probe tomography provided insight on the local compositional homogeneity in AlGaO films with different Al compositions. For AlGaO with pure β or γ phases, the Al composition distribution showed homogeneity with similar Al composition values as extracted from the x-ray diffraction peak positions. For AlGaO films with mixed β and γ phases, inhomogeneity in the Al composition distribution became more obvious in the nm scale. A mechanism was proposed for the observed phase transformation between β and γ phases in MOCVD growth of AlGaO films. [ABSTRACT FROM AUTHOR]