Search

Submersible drainage sump pumps work in a highly corrosive environment, forming films with corrosive reaction products on the surface. Pump rotors are high-demand parts, so they are made of quality materials with good wear and corrosion resistance properties such as nodular graphite cast iron. This paper analyses the corrosion behaviour of cast iron used in the manufacture of rotors in three types of wastewaters, with variable pH. Nodular graphite cast iron samples were immersed in wastewater for 30, 60, and 90 days and tested by linear polarisation and electrochemical impedance spectroscopy (EIS). Also, the layers of reaction products formed on the surface of the material were analysed by SEM and EDS. The results showed that nodular cast-iron immersed in wastewater with acidic pH showed intense corrosion, the oxide layer formed on its surface is unstable. Also, the final structure of the product layer is that of a tri-layer with cations and anions absorbed from the corrosion media: the double-electric layer directly connected to the metal surface, an internal layer consisting of ferrous compounds and ferric compounds that control the diffusion of oxygen, an outer layer, and a compact crust of ferric compounds. The change in the pH of the wastewater has a major influence on the corrosion rate of the cast iron, which increases from 356.4 µm/year in DWW-1 (6.5 pH) to 1440 µm/year in DWW-2 (3 pH) and 1743 µm/year DWWW-3 (11 pH) respectively. As can be seen, the experimental study covers the problem of the corrosion behaviour of the pump rotor in various types of wastewaters this aspect is particularly important for the good use of wastewater pumps and to predict possible deviations for the operation of the equipment within the treatment plants. [ABSTRACT FROM AUTHOR]

Phosphate coatings are one of the most important methods in preventing metal corrosion, especially iron alloys. The high interest in this method for industrial applications is mainly due to the low costs associated with the phosphating solution component and technological process. Considering this aspect and the advantages offered to the materials (corrosion resistance, good adhesion, wear resistance), this study evaluates the potential of using the phosphate coating method in health and safety applications. Therefore, the deposition of a layer of zinc phosphate on the steel surface used in the manufacture of components for personal protective equipment was approached. Firefighters, during rescue/evacuation operations, use protective equipment for fall arrest, whose accessories (hooks, carabiners) are made of steel. Due to the low corrosion resistance property of carbon steel, these accessories must be replaced frequently. This paper aims to analyze the possibility of improving the corrosion resistance of carbon steel in a fire extinguishing solution. Accordingly, the electrochemical behavior of two different types of coatings was studied by electrochemical impedance spectroscopy (EIS) and scanning electron microscope (SEM). In the literature, different corrosion evaluating methods or systems have been considered, and up until now, there has been no previous study to have approached the corrosive behavior of C45, phosphate C45, and painted phosphate C45 immersed in fire extinguishing solution. [ABSTRACT FROM AUTHOR]

The carbon steel is used in many areas due to its good mechanical properties; however, its low corrosion resistance presents a very important problem, for example, when carbon steel carabiners are used in the petroleum industry or navy, the possibility of an accident is higher due to carabiner failure. This phenomenon could occur as a consequence of the corrosion process which negatively affects mechanical properties. This paper study the possibility to improve its corrosion resistance by depositing on its surface a phosphate layer and a paint layer, and also aims to analyze the immersion behavior in saltwater of carbon steel, phosphate carbon steel, and phosphate and painted carbon steel. According to this study, by coating the carbon steel with a phosphate or paint layer, a higher polarization resistance is obtained in saltwater. Moreover, by electrochemical impedance spectroscopy (EIS), it was observed that the corrosion rate decreases with the increase of the immersion time. Meanwhile scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) revealed that the main compounds which formed on the sample's surface were iron oxides or hydroxy-oxides, after immersion for a longer period. The overall results show that all types of deposited layers increase the corrosion resistance of C45 steel. [ABSTRACT FROM AUTHOR]