Apricots are a fragile fruit that rots quickly after harvest. Therefore, they have a short shelf-life. The purpose of this work is to determine the effect of coatings containing chitosan (CH) as well as its nanoparticles (CHNPs) as thin films on the quality and shelf-life of apricots stored at room (25 ± 3 °C) and cold (5 ± 1 °C) temperatures. The physical, chemical, and sensorial changes that occurred during storage were assessed, and the shelf-life was estimated. Transmission electron microscopy was used to examine the size and shape of the nanoparticle. The nanoparticles had a spherical shape with an average diameter of 16.4 nm. During the storage of the apricots, those treated with CHNPs showed an obvious decrease in weight loss, decay percent, total soluble solids, and lipid peroxidation, whereas total acidity, ascorbic acid, and carotenoid content were higher than those in the fruits treated with CH and the untreated fruits (control). The findings of the sensory evaluation revealed a significant difference in the overall acceptability scores between the samples treated with CHNPs and the other samples. Finally, it was found that CHNP coatings improved the qualitative features of the apricots and extended their shelf-life for up to 9 days at room temperature storage and for 30 days in cold storage. [ABSTRACT FROM AUTHOR]

The strawberry has a very short postharvest life due to its fast softening and decomposition. The goal of this research is to see how well a starch-silver nanoparticle (St-AgNPs) coating affects the physical, chemical, and microbiological qualities of strawberries during postharvest life. Additionally, the effect of washing with running water on silver concentration in coated strawberry fruit was studied by an inductively coupled plasma-optical emission spectrometer (ICP-OES). Furthermore, the shelf-life period was calculated in relation to the temperature of storage. Fourier transform infrared-attenuated total reflectance (FTIR-ATR), UV-Visible, and Transmission Electron Microscopic (TEM) were used to investigate the structure of starch-silver materials, the size and shape of AgNPs, respectively. The AgNPs were spherical, with an average size range of 12.7 nm. The coated samples had the lowest weight loss, decay, and microbial counts as compared to the uncoated sample. They had higher total acidity and anthocyanin contents as well. The washing process led to the almost complete removal of silver particles by rates ranging from 98.86 to 99.10%. Finally, the coating maintained strawberry qualities and lengthened their shelf-life from 2 to 6 days at room storage and from 8 to 16 days in cold storage. [ABSTRACT FROM AUTHOR]