Abstract: Novel SiO2 hierarchical nanostructure has been grown on SiC nanowires using thermal decomposition of a mixture of ethanol and titanium tetrachloride. Novel nanostructure was realized in one synthesis route. Based on SEM and TEM observations, the hierarchical nanostructure consists of core-shell SiC–SiO2 main stem nanowire and a lot of SiO2 nanorod branches grown on the main stem. A mean diameter of SiC central cores was about 40nm and their lengths reach about 100μm. The lengths and diameters of SiO2 nanorod-like branches were ranged in 400–800nm and 30–120nm, respectively. The growth of core-shell SiC–SiO2 nanowires obeyed vapor–liquid–solid mechanism and the SiO2 nanorod-like branches grew via vapor–solid mechanism. The infrared absorption and photoluminescence properties of the grown nanostructure were investigated. [Copyright &y& Elsevier]

Abstract: Large-scale SiC nanocables were synthesized on a Ni(NO3)2-catalyzed Si substrate by using a simple and cheap method based on thermal decomposition of methanol. Based on X-ray diffraction and high-magnification transmission electron microscopy, the as-grown nanocables consisted of crystalline SiC cores and amorphous SiO2 shells. The diameters of SiC cores were 5.7–10nm and the thicknesses of SiO2 shells were 9–20nm. Dividing of nanocables was observed and its origin was investigated. An asymmetric feature of SiC TO band with a shoulder at the high-frequency side was attributed to the contribution of SiC TO mode. The nanocables displayed strong violet–blue emission. A possible growth mechanism was proposed. [Copyright &y& Elsevier]

Abstract: Large-scale SiC–SiO2 core–shell nanowires decorated with carbon nanoparticles have been synthesized on Si substrate using thermal decomposition of ethanol. The amorphous carbon nanoparticles on SiO2 shell are of hemispherical configuration hiving a mean diameter of about 20nm. The average size of carbon nanoparticles estimated from Raman measurement is 23.4nm close to that evaluated from transmission electron microscopic observation. Strong enhancement of blue emission band and appearance of a new yellow emission band were observed in SiC–SiO2 core–shell nanowires decorated with carbon nanoparticles and their origins were discussed. A possible synthesis mechanism of SiC–SiO2 core–shell nanowires decorated with carbon nanoparticles was proposed. [Copyright &y& Elsevier]