Search

[Display omitted] • First report on the microbial corrosion mechanism of Acinetobacter soli. • EDS distinguishes abiotic and biotic processes in microbial corrosion systems. • EDS and XRD highlight the significance of oxygen mass transfer in X70 corrosion. • Accumulation of acetic acid influences iron ion dissolution. • Coupling of metal microbial corrosion with oil microbial degradation. Deterioration corrosion occurs between the external surface of oil pipelines and aerobic oil-degrading microorganisms in oil fields. Microorganisms with aerobic oil pollution remediation capabilities may catalyze more serious anaerobic microbial corrosion due to the carbon source supply. In this study, Acinetobacter soli strains were isolated from oil-contaminated environments, and their role in the deterioration corrosion behavior of X70 steel in an oil-water environment was investigated using the EDS multipoint scanning method. The presence of oil controls the deposition of carbon and phosphorus and diffusion of oxygen, leading to significant adhesion attraction and initial growth inhibition of biofilm on the metal surface. A. soli facilitates oxygen transfer and iron ion dissolution, thereby accelerating the pitting corrosion of X70 steel. This corrosion of the X70 steel, in turn, further accelerates the microbial degradation of oil, inhibiting the appearance of calcareous scale in the later stage of corrosion. The corrosion of X70 steel is influenced by microbial degradation, and the specific corrosion behaviors are related to the activity of A. soli in the petroleum environment. This study sheds light on the corrosion mechanisms of X70 steel by A. soli at different stages, providing insights into the interactions between microorganisms, oil pollution, and metal corrosion in oil fields. [ABSTRACT FROM AUTHOR]

Marine is the harshest corrosive environment where almost all marine underwater equipment and facilities undergo corrosion caused by marine microorganisms. With the development of marine resources globally, the marine engineering and relevant infrastructures have increased exponentially. Microbiologically influenced corrosion (MIC) leads to severe safety accidents and great economic losses. The specific aggregation of corrosive microbial communities and their interactions with materials conform to a typical ecological adaptation mechanism. On the one hand, corrosive biofilms in the marine environment selectively colonize on a specific steel substrate by utilizing their complex community composition and various extracellular polymeric substances; on the other hand, the elemental composition and surface microstructure of different engineering steels affect the microbial community and corrosive process. MIC in the marine environment is a dynamic process evolving with the formation of corrosive biofilms and corrosion products. In this mini-review, the interactions between corrosive biofilm and steel substrates are explored and discussed, especially those conducted in situ in the marine environment. Herein, the important role of iron in the dynamic process of marine corrosion is highlighted. [ABSTRACT FROM AUTHOR]

[Display omitted] Microbiologically influenced corrosion (MIC) is a complicated process that happens ubiquitously and quietly in many fields. As a useful nutritional ingredient in microbial culture media, yeast extract (YE) is a routinely added in the MIC field. However, how the YE participated in MIC is not fully clarified. In the present work, the effect of YE on the growth of sulfate reducing prokaryotes (SRP) Desulfovibrio bizertensis SY-1 and corrosion behavior of X70 pipeline steel were studied. It was found that the weight loss of steel coupons in sterile media was doubled when YE was removed from culture media. However, in the SRP assays without YE the number of planktonic cells decreased, but the attachment of bacteria on steel surfaces was enhanced significantly. Besides, the corrosion rate of steel in SRP assays increased fourfold after removing YE from culture media. MIC was not determined for assays with planktonic SRP but only for biofilm assays. The results confirm the effect of YE on D. bizertensis SY-1 growth and also the inhibitory role of YE on MIC. [ABSTRACT FROM AUTHOR]

[Display omitted] • 75 ppm THPS is insufficient to prevent D. hontreensis biofilm formation on X70 steel. • It reduces the planktonic cell count, but increases sessile cell count on carbon steel. • The inadequate THPS dosage leads to increased weight loss and pit size. Biocides are often used to mitigate the microbially influenced corrosion (MIC) of construction materials in many fields. To study the effect of inadequate dosing of non-oxidizing biocide tetrakis (hydroxymethyl) phosphonium sulfate (THPS) on corrosion of pipeline steel caused by microorganisms, a novel marine isolate Desulfovibrio hontreensis SY-21 was selected as a test microorganism. Weight loss rate determination, morphological analyses, and corrosion product analyses combined with electrochemical measurements were performed to investigate the influence of THPS on the MIC of X70 pipeline steel. The responses of sessile and planktonic cells of D. hontreensis to THPS were also studied. Results showed that D. hontreensis cells could significantly promote steel corrosion and induce local corrosion pits. With a THPS addition within the tolerance range of D. hontreensis for the biocide, MIC of the steel was further promoted by 65%. The growth of planktonic cells was inhibited by the biocide, but the number of biofilm cells was significantly increased. This study revealed that THPS concentrations within a specific range increased the corrosive effect of the presence of D. hontreensis by promoting the growth of sessile cells and biofilm formation. Therefore, the use of the biocide in practical applications needs to be properly considered and managed. [ABSTRACT FROM AUTHOR]