Search

Many research works have already been made and are still in progress on metallic fibres, as their incorporation reduces the brittleness of the concrete and improves its resistance to the impact and crack propagation. But the use of such non-metallic fibres may induce corrosion which is a major problem to be addressed from the durability aspect. To overcome this problem, in the present research work, a non-metallic hybrid fibre combination was investigated with synthetic fibres like polypropylene and abaca fibres. Also, rather than using conventional cementitious materials such as silica fume, fly ash, and ground granulated blast furnace slag, a new generation of ultra-fine material namely alccofine was used as a partial replacement for the cement by 15%. Abaca fibre was utilised in a constant addition of 0.5% and blended with polypropylene fibre in a range varying from 0% to 2% with an increment of 0.5%. The fresh properties of self-compacting concrete (SCC) in mono and hybrid fibres combinations were assessed through slump flow, J-ring, and V-funnel tests. Water absorption and sorptivity tests were conducted to ensure the durability of the prepared mix. Further, impact tests were carried out on the prepared cylinder specimens to check the capability of the mix with the non-metallic hybrid combination. The main objective here was to check whether a high-strength durable SCC could be achieved using non-metallic fibres and natural fibres. From the obtained experimental results, it was observed that 15% alccofine as a partial substitute to the cement with the addition of 0.5% of abaca fibre and 2% of polypropylene fibre to SCC performed better than the control SCC.

This study presents a detailed experimental investigation on the effects incorporating non-metallic fibers in hybrid form in self-compacting concrete (SCC). In this regard SCC was prepared with Alccofine and Metakaolin as partial replacement for cement in 15% and 20% respectively along with the hybrid fibre combinations namely abaca fibres (0.25%, 0.5% & 0.75%), polypropylene fibres (0.5%, 1%, 1.5% & 2%) and glass fibres (0.5%, 1%, 1.5%, & 2%). The fresh properties of SCC with and without hybrid fibre combinations were assessed through the standard tests such as slump flow, J ring and V-funnel tests. The conventional mechanical tests such as compressive strength test, split tensile strength test and flexural strength test were performed at 7 and 28 days. The experimental results reveal that the fresh properties of SCC were highly influenced by alccofine and Metakaolin adopted in this research. Furthermore, that the hybrid combination of abaca with polypropylene and glass fibres improved the mechanical properties of SCC and in particular the mix with 1% glass fibre and 0.25% Abaca fibre had shown better flexural and tensile strength behaviour. Microstructure analyses were also done to confirm the improvement in mechanical properties. The Scanning Electron Microscope images of the mix with 1% glass fibre and 0.25% abaca fibre showed less voids presence and presence of more hydrated components conveying that the usage of hybrid fibres had restricted the propagation of cracks there by reducing the percentage of voids and the use of metakaolin and alcofine helping in forming hydrated components at earlier stage leading to better strength.