Search

The thermal modification of wood in a nitrogen atmosphere shapes the functional properties of wood. The aim of this research was to determine the influence of different levels of temperature and the duration of thermal modification on the mechanical properties of the black poplar (Populus nigra L.). Black poplar was thermally modified in nitrogen atmosphere in the temperature range from 160 °C to 220 °C (6 levels) for 2 h to 8 h (4 levels), resulting in a total of 24 treatments. The effect of these treatments on compressive strength parallel to the grain (CS), modulus of rupture (MOR), and modulus of elasticity during bending (MOE) were analyzed. Thermal modification influenced the mechanical properties of black poplar wood. After thermal modification occurred in a nitrogen atmosphere, an increase in compressive strength was noticeable for all variants of black poplar wood modification. The highest 16% increase in CS was obtained for the modification carried out at the temperature of 160 °C and for 2 h. An increase was also found for MOE when modified under mild conditions, while a decrease occurred for variants at higher temperatures, i.e., for 200 °C and 220 °C. The study showed that for all modification variants, there was a decrease in MOR alongside the increase in modification temperature and time. [ABSTRACT FROM AUTHOR]

Black poplar (Populus nigra L.) was subjected to thermal modification in superheated steam. The modification was performed at 160 °C, 190 °C, and 220 °C for 2 h. The equilibrium moisture content of the black poplar wood was examined when it was exposed to 76% ± 2% relative humidity at a temperature of 20 °C ± 2 °C. The thermal modification of the poplar wood changed its moisture-exchange-related physical properties to a large extent. The effects of temperature on individual properties (density, mass loss, hygroscopicity, swelling, and water absorption) were diverse, and the intensity of these effects increased with increasing temperature of the thermal treatment process. In most cases, no significant differences were observed between the changes in properties of the sapwood and the heartwood. [ABSTRACT FROM AUTHOR]

This study aimed to determine glucose and xylose content by acid hydrolysis of wood samples, both unmodified and thermally modified (modification time was 2, 6, 10 hours), using high performance liquid chromatography. Optimization of the hydrolysis process on the native ash wood samples showed that 3 h was the best time in the hydrolysis process. After that time, 58.8% of glucose and 20.8% of xylose were obtained. In turn, chromatographic analysis showed incomplete hydrolysis of ash wood samples, which were modified in a nitrogen atmosphere, especially at shorter times (2 and 6 h) of modification. With longer modification times (10 h), the hydrolysis of ash wood samples was completed. The above mentioned problem was caused mainly by the increase of cellulose crystallinity degree. The decrease of this parameter was observed only after 10 h of thermal modification, which would facilitate the process of acidic hydrolysis. Additionally, it was observed that the thermal modification of ash wood at 190 °C in a nitrogen atmosphere for 10 h caused a drastic decrease in the xylose content (from 20.8% to 8.0%) and only a slight decrease in the glucose content (from 58.8% to 54.9%). [ABSTRACT FROM AUTHOR]

Black poplar (Populus nigra L.) was thermally modified in nitrogen atmosphere. The effects of the modification process on poplar wood were evaluated for temperatures: 160 °C, 190 °C, and 220 °C applied for 2 h; and 160 °C and 190 °C for 6 h. The percentual impact of temperature and time of modification on the properties of modified wood was analysed. The study permitted the identification correlations between the chemical composition and selected physical properties of thermally modified poplar wood. The dimensional stability of poplar wood was improved after thermal modification in nitrogen. The higher the temperature of modification, the lower the equilibrium moisture content (EMC) of black poplar. At the temperature of 220 °C, EMC was two times lower than the EMC of non-modified black poplar. It is also possible to reduce the dimensional changes of wood two-fold (at the modification temperature of 220 °C), both in radial and tangential directions, independently of the acclimatization conditions (from 34% to 98% relative humidity, RH). Similar correlations have been found for wood that has been soaked in water. Higher modification temperatures and longer processing times contributed to a lower swelling anisotropy (SA). [ABSTRACT FROM AUTHOR]