Título Libro: Processing and Manufacturing of Advanced Materials, The major challenge in a heat-resistant steel is to generate thermally stable microstructures that allow increasing the operating temperature, which will improve the thermal efficiency of the power plant without diminishing strength or time to rupture. The strengthening mechanism in tempered martensitic 9Cr steels comes mainly from the combination of solid solution effect and of precipitation hardening by fine MX carbo-nitrides, which enhance the sub-boundary hardening. This work is focused on the effect of ausforming processing on MX nanoprecipitation, on both their distribution and number density, during the subsequent tempering heat treatment. The creep strength at 700 oC was evaluated by small punch creep tests. The creep results after ausforming were compared to those obtained after conventional heat treatment concluding, in general, that ausforming boosts the creep strength of the steel at 700 oC. Therefore, conventional ausforming thermomechanical treatment is a promising processing route to raise the operating temperature of 9Cr heat-resistant steels., Authors acknowledge financial support to Spanish Ministerio de Economia y Competitividad (MAT2016-80875-C3-1-R) and Comunidad de Madrid (DIMMAT-CM_S2013/MIT-2775). This work is carried out under the auspices of the Joint Programme on Nuclear Materials of the European Energy Research Alliance Pilot Project CREMAR. J. Vivas acknowledges financial support in the form of a FPI Grant BES-2014-069863.

There is a worldwide need to develop materials for advanced power plants with steam temperatures of 700°C and above which have the capacity to achieve high efficiency and low CO2 emissions. This request involves the development of new grades of 9-12Cr heat-resistant steels, with a nanostructured martensite, mainly focusing on the long-term creep rupture strength of base metal and welded joints, creep-fatigue properties, and microstructure evolution during exposure at such elevated temperatures. The main shortcomings of actual 9-12Cr high-chromium steels are that the creep resistance is not enough to fulfill the engineering requirements at temperatures higher than 600°C and the material undergoes a cyclic softening. Creep strength at high temperature could be improved by a microstructural optimization through nano-precipitation, guided by computational thermodynamics, and thermomechanical control process optimization., We acknowledge support for the publication fee by the CSIC Open Access Publication Support Initiative through its Unit of Information Resources for Research (URICI).