Search

Background: Current treatments for congenital heart defects often require surgery and implantation of a synthetic patch or baffle that becomes a fibrous scar and leads to a high number of reoperations. Previous studies in rats have shown that a prevascularized scaffold can integrate into the heart and result in regions of vascularized and muscularized tissue. However, increasing the thickness of this scaffold for use in human hearts requires a method to populate the thick scaffold and mature it under physiologic flow and electrical conditions. Experiment: We developed a bioreactor system that can perfuse up to six 7 mm porous scaffolds with tunable gravity-mediated flow and chronic electrical stimulation. Three polymers, which have been reported to be biocompatible, were evaluated for effects on the viability of induced pluripotent stem cell-derived cardiomyocytes (iPSC-CM). Bioreactor flow and electrical stimulation functions were tested, and the bioreactor was operated for up to 7 days to ensure reliability and lack of leaks in a 37°C, humidified incubator. Height and flow relationships were measured for perfusion through an electrospun polycaprolactone and gelatin scaffold, previously reported by our laboratory. Culture with cells was evaluated by plating human umbilical vein endothelial cells and human dermal fibroblasts on top of the scaffolds in both static and flow conditions for 2, 5, and 7 days. As a proof-of concept, scaffolds were cryosectioned and cell infiltration was quantified using immunofluorescence staining. Results: Neither MED610 (Stratasys), Vero (Stratasys), nor FORMLAB materials affected the viability of iPSC-CM, and MED610 was chosen for manufacture due to familiarity of 3D printing from this material. The generation of electrical field stimulation from 0 to 5 V and physiological ranges of pump capacities were verified. The relationship between height and flow was calculated for scaffolds with and without cells. Finally, we demonstrated evaluation of cell depth and structure in scaffolds cultured for 2, 5, and 7 days. Conclusion: The gravity-mediated flow bioreactor system we developed can be used as a platform for 3D cell culture particularly designed for perfusing vascularized tissue constructs with electrical stimulation for cardiac maturation.

Congenital heart defects (CHDs) are the leading cause of death in live-born infants. Currently, patches used in the repair of CHDs are exclusively inert and non-degradable, which increases the risk of arrhythmia, follow-up surgeries, and sudden cardiac death. In this preliminary study, we sought to fabricate biodegradable scaffolds that can support cardiac regeneration in the repair of CHDs. We electrospun biodegradable scaffolds using various blends of polyurethane (PU) and polycaprolactone (PCL) with and without sacrificial poly(ethylene oxide) (PEO) particles and assessed the mechanical properties, cell infiltration levels, and inflammatory response in vitro (surface cell seeding) and in vivo (subcutaneous mouse implant). We hypothesized that a blend of the two polymers would preserve the low stiffness of PU as well as the high cell infiltration observed in PCL scaffolds. The inclusion of PU in the blends, even as low as 10%, decreased cell infiltration both in vitro and in vivo. The inclusion of sacrificial PEO increased pore sizes, reduced Young's moduli, and reduced the inflammatory response in all scaffold types. Collectively, we have concluded that a PCL patch electrospun with sacrificial PEO particles is the most promising scaffold for further assessment as in our heart defect model., (© 2021 Wiley Periodicals LLC.)

A novel cardiac scaffold comprised of decellularized porcine heart matrix was investigated for use as a biodegradable patch with a potential for surgical reconstruction of the right ventricular outflow tract. Powdered heart matrix solution was blended with chitosan and lyophilized to form three-dimensional scaffolds. For this investigation, we examined the influence of different blending ratios of heart matrix to chitosan on porosity and mechanical properties, then gene expression and electrophysiological function of invading neonatal rat ventricular myocytes (NRVM) compared to type-A gelatin/chitosan composite scaffolds. Heart matrix/chitosan-blended hydrogels (1.6 mg/mL heart matrix) had similar porosity (109±34 μm), and elastic modulus (13.2±4.0 kPa) as previously published gelatin/chitosan scaffolds. Heart matrix/chitosan hydrogels maintained>80% viability and had higher NRVM retention (∼1000 cells/mm(2)) than gelatin/chitosan scaffolds. There was a significant increase in α-myosin heavy chain and connexin-43 expression in NRVM cultured on heart matrix/chitosan scaffolds after 14 days compared with gelatin/chitosan scaffolds. Further, heart matrix/chitosan scaffolds had significantly higher conduction velocity (12.6±4.9 cm/s) and contractile stress (0.79±0.13 mN/mm(2)) than gelatin/chitosan scaffolds. In summary, NRVM cultured on heart matrix scaffold showed improvements in contractile and electrophysiological function.

A three-dimensional scaffold composed of self-assembled polycaprolactone (PCL) sandwiched in a gelatin-chitosan hydrogel was developed for use as a biodegradable patch with a potential for surgical reconstruction of congenital heart defects. The PCL core provides surgical handling, suturability and high initial tensile strength, while the gelatin-chitosan scaffold allows for cell attachment, with pore size and mechanical properties conducive to cardiomyocyte migration and function. The ultimate tensile stress of the PCL core, made from blends of 10, 46 and 80kDa (Mn) PCL, was controllable in the range of 2-4MPa, with lower average molecular weight PCL blends correlating with lower tensile stress. Blends with lower molecular weight PCL also had faster degradation (controllable from 0% to 7% weight loss in saline over 30 days) and larger pores. PCL scaffolds supporting a gelatin-chitosan emulsion gel showed no significant alteration in tensile stress, strain or tensile modulus. However, the compressive modulus of the composite tissue was similar to that of native tissue (∼15kPa for 50% gelatin and 50% chitosan). Electron microscopy revealed that the gelatin-chitosan gel had a three-dimensional porous structure, with a mean pore diameter of ∼80μm, showed migration of neonatal rat ventricular myocytes (NRVM), maintained NRVM viability for over 7 days, and resulted in spontaneously beating scaffolds. This multi-layered scaffold has sufficient tensile strength and surgical handling for use as a cardiac patch, while allowing migration or pre-loading of cardiac cells in a biomimetic environment to allow for eventual degradation of the patch and incorporation into native tissue., (Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

This article reviews current applications and novel candidate biomaterials for use as tissue-engineered scaffolds in pediatric cardiac tissue engineering. This overview of different types of biomaterials includes naturally derived and synthetic polymers and their biological, physical, and biomechanical properties for the use as a patch or baffle for surgical reconstruction of congenital heart defects. Applications and characteristics of composite biomaterials are highlighted with their respective feasibilities in use as cardiac scaffolds. Currently, a wide range of biomaterials has been introduced for cardiovascular reconstruction for complex congenital cardiac defects. However, there are still many remaining challenges for engineered tissue implantations.