The reactive hydride composite (RHC) LiBH4–MgH2 is regarded as one of the most promising materials for hydrogen storage. Its extensive application is so far limited by its poor dehydrogenation kinetics, due to the hampered nucleation and growth process of MgB2. Nevertheless, the poor kinetics can be improved by additives. This work studied the growth process of MgB2 with varying contents of 3TiCl3·AlCl3 as an additive, and combined kinetic measurements, X-ray diffraction (XRD), and advanced transmission electron microscopy (TEM) to develop a structural understanding. It was found that the formation of MgB2 preferentially occurs on TiB2 nanoparticles. The major reason for this is that the elastic strain energy density can be reduced to ~4.7 × 107 J/m3 by creating an interface between MgB2 and TiB2, as opposed to ~2.9 × 108 J/m3 at the original interface between MgB2 and Mg. The kinetics of the MgB2 growth was modeled by the Johnson–Mehl–Avrami–Kolmogorov (JMAK) equation, describing the kinetics better than other kinetic models. It is suggested that the MgB2 growth rate-controlling step is changed from interface- to diffusion-controlled when the nucleation center changes from Mg to TiB2. This transition is also reflected in the change of the MgB2 morphology from bar- to platelet-like. Based on our observations, we suggest that an additive content between 2.5 and 5 mol% 3TiCl3·AlCl3 results in the best enhancement of the dehydrogenation kinetics. [ABSTRACT FROM AUTHOR]

The hampered kinetics of reactive hydride composites (RHCs) in hydrogen storage and release, which limits their use for extensive applications in hydrogen storage S1and energy conversion, can be improved using additives. However, the mechanism of the kinetic restriction and the additive effect on promoting the kinetics have remained unclear. These uncertainties are addressed by utilizing versatile transmission electron microscopy (TEM) on the LiBH4-MgH2 composite under the influence of the 3TiCl3·AlCl3 additives. The formation of the MgB2 phase, as the rate-limiting step, is emphatically studied. According to the observations, the heterogeneous nucleation of MgB2 relies on different nucleation centers (Mg or TiB2 and AlB2). The varied nucleation and growth of MgB2 are related to the in-plane strain energy density at the interface, resulting from the atomic misfit between MgB2 and its nucleation centers. This leads to distinct MgB2 morphologies (bars and platelets) and different performances in the dehydrogenation kinetics of LiBH4-MgH2. It was found that the formation of numerous MgB2 platelets is regarded as the origin of the kinetic improvement. Therefore, to promote dehydrogenation kinetics in comparable RHC systems for hydrogen storage, it is suggested to select additives delivering a small atomic misfit. [ABSTRACT FROM AUTHOR]