Search

Purpose: The surface characteristics of thermally and chemically modified wood, such as surface roughness, surface free energy (SFE) and wettability, are important properties that influence further manufacturing processes such as gluing and coating. The aim of this paper was to determine the influence of the surface roughness of thermally and chemically modified teak wood on their SFE, wettability and bonding quality for water-based acrylic and solvent-based alkyd varnishes. In addition, durability against subterranean termites in the field of these modified teak woods was also investigated to give a valuable information for their further application. Design/methodology/approach: The woods tested in this study were fast-growing teak woods that were prepared in untreated and treated with furfuryl alcohol (FA), glycerol maleic anhydride (GMA) and thermal. SFE values were calculated using the Rabel method. The wettability values were measured based on the contact angle between varnish liquids and wood surfaces using the sessile drop method, and the Shi and Gardner model model was used to evaluate the wettability of the varnishes on the wood surface. The bonding quality of the varnishes was measured using a cross-cut test based on ASTM 3359-17 standard. In addition, durability against subterranean termites in the field of these modified teak woods was also investigated according to ASTM D 1758-06. Findings: The results showed that furfurylated and GMA-thermal 220°C improved the durability of teak wood against termites. The furfurylated teak wood had the roughest surface with an arithmetic average roughness (Ra) value of 15.65 µm before aging and 27.11 µm after aging. The GMA-thermal 220°C treated teak wood was the smoothest surface with Ra value of 6.44 µm before aging and 13.75 µm after aging. Untreated teak wood had the highest SFE value of 46.90 and 57.37 mJ/m2 before and after aging, respectively. The K values of untreated and treated teak wood increased owing to the aging treatment. The K values for the water-based acrylic varnish were lower than that of the solvent-based alkyd varnish. The untreated teak wood with the highest SFE produced the highest bonding quality (grades 4–5) for both acrylic and alkyd varnishes. The solvent-based alkyd varnish was more wettable and generated better bonding quality than the water-based acrylic varnish. Originality/value: The originality of this research work is that it provides evaluation values of the durability and SFE. The SFE value can be used to quantitatively determine the wettability of paint liquids on the surface of wood and its varnish bonding quality. [ABSTRACT FROM AUTHOR]

Wood surface roughness, surface free energy (SFE), wettability, and bonding quality for water-based acrylic coatings were investigated. The samples tested in this study included Pinus radiata, Pinus sylvestris, Larch, Hemp oak, Catalpa tree, and Camphor. Sandpaper with grits of 180, 240, 320, 400, and 500 was utilized to sand wood surfaces. The van OSS-Chaudhury-Good equation (vOCG) was used to calculate the SFE values. The modified model (M-D) was used to calculate the wettability based on the contact angle change rate (K value). The higher the K value, the faster the contact angle approaches equilibrium. A cross-cut test was used to evaluate the coating's bonding quality. The anatomical structure of wood has an impact on the roughness of hardwood. The equilibrium contact angle is influenced by the wood species and sandpaper grit size. Sanding can make the surface of wood more wettable. Radiata pine that had been sanded to 180 grit had the highest SFE value. After finishing with waterborne acrylic, hardwood had a slightly better coating adhesion than softwood. Hemp oak wood had the lowest coating adhesion (0.6) and the highest K value (0.82). The best bonding quality (0.4) was supplied by the camphor wood with the lowest K value (0.13). Wettability in terms of K values was a good indication of determining the bonding quality of the water-based acrylic coatings. [ABSTRACT FROM AUTHOR]

Wettability and bonding quality of exterior coatings on fast-growing wood surfaces were studied. Samples of air-dried flat-grained (tangential surface) and edge-grained (radial surface) pattern of jabon ( Anthocephalus cadamba) and sengon ( Paraserianthes falcataria) woods were used. Before application of exterior coatings, the surfaces of the lumber samples were sanded. To provide wood surfaces with various degrees of roughness, abrasive papers of 120, 240, and 360 grits were used for the surface preparation. The wettability of two exterior coatings (water-based acrylic and oil-based alkyd varnishes) on the sanded wood surfaces was measured using a sessile drop contact angle method. The Shi and Gardner (S/G) model was used to evaluate and compare the wettability of the surface coatings on the wood. The sanded wood samples were coated with the two coatings (two layers each). Bonding quality of the coating layers was measured using a crosscut tape test method. Experimental results show that constant contact angle change rate ( K value) of the S/G model decreased as the grit number of abrasive paper increased. This indicates that the wettability decreased as the roughness of the surface decreased (surface becomes smoother). There was no evidence of differences in wettability between tangential and radial wood surfaces. The oil-based alkyd coating generated better wettability compared to the water-based acrylic. The crosscut tests showed that the bonding quality of the coating films on both jabon and sengon wood decreased as the surface became smoother. The sengon wood compared to jabon wood provided better coating wettability and bonding quality. Wettability in terms of the K values was a good indication for determining the bonding quality of the two varnish layers. [ABSTRACT FROM AUTHOR]