Search

The aim of this study was to determine the changes occurring in the wood cellulose of the fast-growing poplar (Populus deltoides × maximowiczii) under the influence of steam explosion (SE) pretreatment. Cellulose from native wood and after pretreatment at 160 and 205 °C was isolated. Cellulose polymerization degree by size exclusion chromatography (SEC) and cellulose crystallinity index by Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR) were determined. The profiles of sugars in the native wood and in the solid fraction after pretreatment (using the acid hydrolysis method) were also determined. In addition, the profile of monosaccharides in the liquid fraction obtained after steam explosion and in the liquid fraction after acid hydrolysis of the oligosaccharides were investigated using high-performance liquid chromatography (HPLC). This allowed to determine the change in the yield of hexoses and pentoses in the studied material. The behavior of cellulose in wood subjected to steam explosion at 160 and 205 °C and isolated by the Kürschner–Hoffer method was studied by determining the absorption bands of FTIR-ATR spectra. The lateral order index (LOI) of cellulose was calculated from the ratio of the intensity of the corresponding absorption bands A1422/A896 cm−1. Total crystallinity index (TCI) of cellulose was calculated from the ratio of the intensity of absorption bands A1372/A2900 cm−1. TCI of Kürschner-Hoffer cellulose isolated from wood subjected to steam explosion at 160 and 205 °C decreased by 5.6 and 5.0%, respectively, with regard to the applied temperature. LOI increased in cellulose isolated from wood subjected to steam explosion at 160 °C (by 0.7%) and at 205 °C (by 19.2%) in relation to the index of cellulose isolated from native wood. Kürschner–Hoffer cellulose isolated from wood subjected to steam explosion at 160 and 205 °C exhibited, respectively, a reduced degree of polymerization of about 11% and about 8%. Polydispersity index in Kürschner–Hoffer cellulose was 1% lower after both pretreatments than native sample. [ABSTRACT FROM AUTHOR]

The wood of five European species: black poplar (Populus nigra L.), European beech (Fagus sylvatica L.), European ash (Fraxinus excelsior L.), European oak (Quercus robur L.), and Scots pine (Pinus sylvestris L.) was subjected to thermal modification in nitrogen atmosphere at 190 °C during 6 h. Native and modified wood was varnished and oiled in industrial conditions. Thermally modified (TM) wood was characterized by a greater absorption of varnish and oil when applying the first layer to the surface, which finally resulted in higher application values compared to native wood. In particular, after varnishing, there was a significant increase in gloss and radical change of colour. Regardless of the wood species, finishing process (varnishing, oiling), the ΔE values were close to or higher than 6, which proves high colour changes. Modified poplar, ash, and oak after varnishing had a different colour (ΔE higher than 12). The surface colour changes as a result of UV photoaging was individual, depending on the wood species and the method of finishing. In the case of the thickness of varnish coatings, the wood structure was important, i.e., on ring-porous hardwood and softwood they were thicker. In the case of wood species with a lower density, i.e., black poplar and pine, the thermal modification in nitrogen atmosphere process did not reduce the resistance of the varnish coat, and in the case of species with a higher density (oak, ash, beech) it decreased by one level. Thermal modification reduced the Brinell hardness of wood with wide rays (oak and beech) by 11%. The applied process of surface finishing by double varnishing or oiling did not significantly change the hardness of tested wood. [ABSTRACT FROM AUTHOR]

The main objective of this research was to investigate tropical wood sorptive properties. For selected tropical wood species (courbaril, ipe, light red meranti, merbau, tatajuba, and teak), the equilibrium moisture content was determined at 20 °C and 9, 30, 55, 70, and 97% relative humidity. The experimentally determined values were analysed using the Hailwood-Horrobin sorption model to compute the fibre saturation point and mono- and multi-layer sorption. There were significant differences in the sorption behaviour of different wood species. Generally, the fibre saturation point of tropical wood species is lower than in wood species from moderate climate zones. The lowest values of fibre saturation point were found for ipe (18.7%), courbaril (20.4%), and tatajuba (20.5%). Furthermore, chloroform-ethanol extractives content was correlated with multilayer sorption and the fibre saturation point, such that a higher content of chloroform-ethanol extractives was associated with a lower equilibrium moisture content. Therefore, chemisorption was not influenced by chloroform-ethanol extractives. Ethanol extracts showed an influence on monomolecular-bound water. [ABSTRACT FROM AUTHOR]

Black poplar (Populus nigra L.) was thermally modified in nitrogen atmosphere. The effects of the modification process on poplar wood were evaluated for temperatures: 160 °C, 190 °C, and 220 °C applied for 2 h; and 160 °C and 190 °C for 6 h. The percentual impact of temperature and time of modification on the properties of modified wood was analysed. The study permitted the identification correlations between the chemical composition and selected physical properties of thermally modified poplar wood. The dimensional stability of poplar wood was improved after thermal modification in nitrogen. The higher the temperature of modification, the lower the equilibrium moisture content (EMC) of black poplar. At the temperature of 220 °C, EMC was two times lower than the EMC of non-modified black poplar. It is also possible to reduce the dimensional changes of wood two-fold (at the modification temperature of 220 °C), both in radial and tangential directions, independently of the acclimatization conditions (from 34% to 98% relative humidity, RH). Similar correlations have been found for wood that has been soaked in water. Higher modification temperatures and longer processing times contributed to a lower swelling anisotropy (SA). [ABSTRACT FROM AUTHOR]