The article presents the impact of drying process and selected parameters on the color changes on the surface of pine wood (Pinus sylvestris L.). Three predetermined process conditions (modes), mild, normal, and intensive, were investigated. The experiments were conducted using a semi-industrial scale dryer designed at the Gdańsk University of Technology with a loading capacity of 0.55 m3. The drying process was applied to pine wood grown in the northern part of Pomeranian region in Poland. The specimens were selected taking into consideration the radial angle of the growth rings. During each drying mode, 25 pieces of wood with dimensions (thickness, width, length) of 0.03 m, 0.2 m, and 1.5 m, respectively, were dried. The total color change (E) after drying process and color saturation (h*) before and after drying processes of the wood surface was determined using the normalized CIELAB methods. The obtained results indicated that the color change of the pine wood surface increased simultaneously with the intensification of the drying process. However, the normalized wood quality after drying under intensive drying process conditions remained within the standard limits. The application of intensive drying process conditions remarkably changes the surface color of the obtained material, while remarkably reducing the drying process duration. [ABSTRACT FROM AUTHOR]

This study examined the changes in the properties of beech wood (Fagus sylvatica L.) after intense drying. Beech wood with false red heartwood was selected as the test specimen. The test samples had dimensions of 50 mm thickness, 180 mm width, and 350 mm length. The specimens were divided into two groups, false red heartwood and sapwood. These specimens were selected with different angles of the growth rings (radial and tangential). The results showed that samples with red heartwood, in comparison to samples with sapwood content, had a remarkable effect in covering. Observation of specimens with false red heartwood and sapwood before and after drying process revealed significant differences in color changes and measured values during the covering-slicing test, but not between samples with different growth ring angles. [ABSTRACT FROM AUTHOR]

The influence of the impregnation process of pine wood (Pinus sylvestris L.) samples on the electrical resistance changes and the moisture-content measurement accuracy is presented in this paper. In this study, the resistances of impregnated and nonimpregnated green pine timber harvested from northern Poland were compared. An impregnation method based on a vacuum-pressure chamber was used. Copper salts were applied as the impregnated solutions. The obtained results of the electrical resistance comparison showed a dependence of wood resistance on the moisture content. Higher conductivity occurred in impregnated wood samples filled with copper salt compared with wood samples without impregnation. Noticeable differences in the electrical resistance values were observed when the wood moisture content was significantly above the Fibre Saturation Point (FSP). [ABSTRACT FROM AUTHOR]