Search

Sodalite, a candidate ceramic for the immobilisation of pyroprocessing nuclear waste, showed no observable lattice dilatation in grazing incidence X-ray diffraction when irradiated with up to 1017 5 MeV He ions/cm². However micro-Raman scattering showed considerable spectral broadening characteristic of radiation damage near the end of the ~22 μm He range. Partial amorphism plus nepheline formation was observed in grazing incidence X-ray diffraction when sodalite was irradiated by 1016 12 MeV Au ions/cm². Nepheline appeared less susceptible to 12 MeV Au ion damage than sodalite, with ~25% less amorphous fraction at 1016 ions/cm². [ABSTRACT FROM AUTHOR]

Cerium titanate CeTi2O6 was prepared by a new soft chemistry route in aqueous solution. A suite of characterization techniques, including X-ray diffraction, thermal analysis, vibrational spectroscopy, and scanning and transmission electron spectroscopy, were employed to S investigate the brannerite structure formation and its bulk properties. The J synthesized powder formed the brannerite crystal structure upon calcination at temperatures as low as 800°C. Samples sintered at 1350 °C possess a high level of crystallinity. X-ray absorption near-edge structure results indicate the presence of six-coordinated Ce4+ in the brannerite samples. [ABSTRACT FROM AUTHOR]

Highlights: [•] The incorporation of neptunium (Np) and plutonium (Pu) in thorutite (ThTi2O6) has been studied. [•] The effect of Np/Pu doping on the unit cell parameter changes has been discussed from the structure point of view. [•] The effect of Y as charge compensator to encourage the formation of higher valences of Np and Pu has been explored. [•] The resulting Np/Pu doped thorutite samples have been characterised by using XRD, SEM and DRS. [ABSTRACT FROM AUTHOR]

Abstract: A series of uranium-containing gadolinium zirconate samples have been fabricated at 1450°C in oxidizing, inert and reducing atmospheres. X-ray diffraction, Raman spectroscopy and transmission electron microscopy have been utilized to confirm adoption of pyrochlore or defect fluorite structures. X-ray diffraction allowed determination of the bulk averaged structure while Raman spectroscopy and transmission electron microscopy were used to determine ordering at the microdomain scale. Diffuse reflectance, X-ray absorption near edge structure and X-ray photoelectron spectroscopies indicated a predominantly U6+ oxidation state for all the air-sintered samples, even when Ca2+ or A-site vacancies were incorporated to charge balance for U4+, a mixed U5+/U6+ oxidation state was found for samples sintered in argon, while a mixed U4+/U5+ oxidation state occurred for sintering under N2–3.5%H2. This demonstrates a degree of uranium oxidation state control through sintering conditions, and the potential of using gadolinium zirconates as host materials for uranium in nuclear waste applications. [Copyright &y& Elsevier]

The title compound is synthesized in aqueous medium from a mixture of titanium(IV) bis(ammonium lactato)dihydroxide and Ce(NO3)3 (sintering between 800 and 1400 °C). [ABSTRACT FROM AUTHOR]

MgO-Nd 2 Zr 2 O 7 composites with ratios of 50–70 vol% MgO were produced via a one-pot combustion synthesis. A suite of characterization techniques, including X-ray diffraction, scanning and transmission electron microscopy were employed to investigate the structural properties while dilatometry, simultaneous thermal analysis and laser flash analysis were used to characterize the thermal properties of the composites. Dense pellets were produced after sintering at 1400 °C with grain sizes between 200 and 500 nm for both phases. The thermal properties of the composites are similar to those produced using standard methods. The composite with 70 vol% MgO was found to have the highest thermal conductivity below 1000 °C, while above this temperature the thermal conductivity was found to be similar and independent of MgO content. This novel synthesis route produces materials which show significant improvements in homogeneity with smaller particle sizes when compared to current standard synthesis techniques without significantly reducing thermal conductivity. [ABSTRACT FROM AUTHOR]

Abstract: The structure of one of the oxides proposed to be present in the grey phase of irradiated mixed oxide fuel, the double perovskite Ba2SrUO6 has been investigated from room temperature to 1300K using synchrotron X-ray powder diffraction methods. The divalent strontium and hexavalent uranium are found to be fully ordered in the double-perovskite arrangement of alternating octahedra sharing corner oxygen atoms. At room temperature Ba2SrUO6 adopts a monoclinic structure in space group P21/n. Heating to above 900K induces a first order transition to a rhombohedral structure, and further heating to above 1200K results in a continuous transition to a cubic structure. The sequence of structures is associated with the progressive loss of cooperative tilting of the corner sharing SrO6 and UO6 octahedra. [Copyright &y& Elsevier]