Search

As dental 5 mol% yttria-stabilized (5Y-) zirconia demand high esthetics, it is necessary to clarify how the optical properties are affected by high-speed sintering, which is not yet fully understood. Our study aimed to investigate the effect of high-speed sintering on the translucency and opalescence parameters (TP and OP, respectively), as well as their related microstructure and phase distribution, using two types of multilayered 5Y-zirconia. Multilayered 5Y-zirconia (Cercon xt ML, Lava Esthetic) were cut layer-by-layer, followed by conventional and high-speed sintering. The TP and OP values were subsequently obtained using a spectrophotometer, and field emission scanning electron microscopy images were used to analyze the average grain size. The phase fractions were analyzed using X-ray diffraction. Regardless of the zirconia type, the TP was slightly lowered by high-speed sintering in all the layers except the dentin layer (DL) for Lava Esthetic (p < 0.05). The OP decreased by high-speed sintering in the DL for Cercon xt ML and in all the layers for Lava Esthetic (p < 0.05). The decrease in translucency after high-speed sintering was attributed to a decrease in the yttria-rich t'-phase with low tetragonality, along with an increase in the yttria-lean t-phase with high tetragonality. [ABSTRACT FROM AUTHOR]

The differences in the optical properties of multi-layered zirconia with and without yttria-gradient are not fully understood. This study aimed to evaluate and compare the optical properties, related microstructures, and phase fractions of multi-layered zirconia with and without yttria-gradient. For this, multi-layered zirconia of 5 mol% yttria (5Y) stabilized (Katana STML) and 4Y/5Y stabilized (e.max MT Multi) were cut layerwise, sintered, and analyzed using the opalescence parameter (OP), average transmittance (AT%), translucency parameter (TP), and contrast ratio (CR). The average grain size and phase fractions were obtained from field-emission scanning electron micrographs and X-ray diffraction patterns, respectively. Although the TP values of Katana STML and e.max MT Multi did not show a significant difference (except for transition layer 1), the results of AT and CR showed that the translucency of e.max MT Multi was slightly higher than that of Katana STML (p < 0.05). The opalescence gradient was higher in Katana STML than in the e.max MT Multi. In both zirconia types, translucency increased from the dentin to enamel layer based on the AT, TP, and CR results, while OP decreased (p < 0.05). The higher translucency from the dentin to enamel layer in Katana STML was caused by the pigmentation gradient, while in e.max MT Multi, it was caused by the difference in phase fraction and the pigmentation gradient. [ABSTRACT FROM AUTHOR]

Glazing is the final heat treatment process in the manufacturing of a monolithic zirconia prosthesis. Herein, the effect of cooling rate during zirconia glazing was investigated. A 3 mol% yttria-stabilized tetragonal zirconia polycrystal was glazed at the general cooling rate suggested by the manufacturer, as well as at higher and lower cooling rates, and the differences in flexural strength, hardness, optical properties, and crystal structure were evaluated. A higher cooling rate did not affect the flexural strength, hardness, grain size, optical properties, or crystal structure; however, the Weibull modulus decreased by 1.3. A lower cooling rate did not affect the flexural strength, optical properties, or crystal structure; however, the Weibull characteristic strength increased by 26.7 MPa and the Weibull modulus increased by 0.9. The decrease in hardness and the increase in grain size were statistically significant; however, the numerical differences were negligible. This study revealed that a lower cooling rate provides more reliable flexural strength. Therefore, glazing can proceed at a general cooling rate, which takes 3–4 min; however, glazing at a lower cooling rate will provide a more consistent flexural strength if desired, despite being time-consuming. [ABSTRACT FROM AUTHOR]