Search

In the iron and steel industry, improving the usage amount of New Zealand sea sand ore as a raw material for ironmaking can reduce the production costs of iron and steel enterprises to a certain extent. In this paper, the New Zealand sea sand ore without any grinding pretreatment was used as raw material, oxidized pellets were prepared by using a disc pelletizer, and the experimental conditions for preparing oxidized pellets were investigated and optimized. The effects of binder dosages, roasting temperature and roasting time on the properties of pellets were mainly investigated, and the effects of roasting temperature and roasting time on the microstructure of oxidized pellets was discussed by researching XRD patterns and SEM-EDS. With the increase of binder dosages, the drop strength of green pellets and the compressive strength of oxidized pellets were gradually increased. With the increase of roasting temperature and roasting time, the compressive strength of oxidized pellets increased gradually. When the amount of New Zealand sea sand ore was increased to 40–50%, the optimal process conditions for the preparation of oxidized pellets were as follows: the dosage of binder was 1.5%, the roasting temperature was 1200 °C, and the roasting time was 20 min. [ABSTRACT FROM AUTHOR]

In the iron and steel industry, improving the usage amount of New Zealand sea sand ore as a raw material for ironmaking can reduce the production costs of iron and steel enterprises to a certain extent. In this paper, New Zealand sea sand ore without any grinding pretreatment was used as a raw material, oxidized pellets were prepared by using a disc pelletizer, and the effect of sea sand ore on the performance of green pellets and the metallurgical properties of oxidized pellets was investigated. The effects of sea sand ore on the compressive strength, falling strength, compressive strength of oxidized pellets, and reduction performance were mainly investigated. X-Ray Diffraction (XRD) patterns and Scanning Electron Microscope (SEM) analysis methods were used to discuss the influence of sea sand ore on the microstructure of the pellets' oxidation and reduction process. As the amount of sea sand ore used increased, the compressive strength of green pellets was gradually decreased, and the falling strength of green pellets and the compressive strength of oxidized pellets were gradually increased. When the amount of sea sand ore used was 40%, the reduction swelling index of pellets was 16.31%. The increase of sea sand ore used made the reduction of pellets suppressed and the reduction rate decreased. When the amount of sea sand ore used increased to 40%, the reduction degree of sea sand ore pellets was only 60.06%. The experimental results in this paper provide specific experimental data for the large-scale application of New Zealand sea sand ore in the blast furnace ironmaking process. [ABSTRACT FROM AUTHOR]

The New Zealand sea sand ore is a kind of vanadia–titania magnetite formed by erosion in the coastal zone. Because of its coarse particle size, smooth spherical particles, complex chemical composition, it has been added to sinter as an auxiliary material. Based on the principle of optimizing ore blending to strengthen advantages and weaken disadvantages, this paper used New Zealand sea sand raw ore that has not undergone any pretreatment as the main material and prepared it into oxidized pellets using a disc pelletizer and explored the influence of high-proportion unground sea sand ore on the preparation process and reduction performance of oxidized pellets. The influence of unground sea sand ore on the falling strength, compressive strength, reduction swelling index, and reduction degree of pellets was analyzed by the ICPAES, XRF, XRD, SEM-EDS, and other detection methods, and the change laws and influencing factors of oxidized pellets were analyzed. With the increase of the amount of unground sea sand ore used, the falling strength and compressive strength of the green pellets first decreased and then gradually increased, while the compressive strength of the oxidized pellets first increased and then decreased. At the same time, as the amount of sea sand ore used increased, the reduction process of pellets was restricted. The reduction swelling index and the reduction degree index generally show a downward trend. However, the compressive strength of the pellets gradually increased after reduction. Through the research on the pellet-forming performance and reduction properties of unground sea sand ore, it is shown that when the amount of unground sea sand ore used was 40%, it can still be used as raw material for blast furnace ironmaking. Thus, this research provided specific data support for iron and steel enterprises to improve the ratio of unground sea sand ore and reduce production cost. [ABSTRACT FROM AUTHOR]