Search

Pure silicon oxide was produced in this study utilizing a sodium silicate solution made from Kankara clay as a precursor. The Kankara clay that was obtained from Nigeria was first beneficiated to produce pure dried powder clay. After that, the dried powdered clay was treated with heat activation and acid leaching, respectively. In a 500 mL Erlenmeyer flask, appropriate amounts of each clay (raw, thermally treated clay, and leached clay) were reacted with 3M NaOH solution. The flask was heated to 200°C and stirred continuously for 3 hours on a magnetic stirring hot plate connected to a reflux condenser. The solution was filtered to yield sodium silicate solution, which was then precipitated with 3M HCl while constantly stirring to produce a gelly-like white substance. The gel was aged for 18 hours, then washed with de-ionized water several times before being dried at 80°C for 12 hours to get pure white silica particles, which were subsequently described. The XRD analysis revealed that the silicon oxide synthesized is amorphous, but the microstructure evaluation revealed particles aggregation, which is usual in sol-gel synthesized powder. [ABSTRACT FROM AUTHOR]

The photovoltaic device's economic and environmental merits have made it the most suitable clean energy alternative to help developing countries achieve the SDG-7. However, the low efficiency of the device, which is undergoing massive study across the globe, there is another omnipresent factor, such as surface soiling that has a deleterious effect on a solar cell's performance, which is influenced by wind speed/direction, humidity and temperature. This study investigates the impact of dust on four PV types (Monocrystalline Silicon, Polycrystalline Silicon, Cadmium Telluride and amorphous Silicon) in a city with two large commissioned and one massive solar farm under construction considering wind, humidity, rain, temperature and dust particles under extreme conditions. Low iron glass coupons were also exposed in seasonal, monthly, and annual categories to determine optical losses, soiling rates, and deposition mass. Accumulated dust particles on the surface of the coupon were subjected to SEM/EDX imaging to identify the deposited minerals' morphology. The findings reveal a massive performance decline due to soiling on all exposed modules with a most significant I SC decrease recorded about 73% on a-Si and least about 65% of the Si modules in one year without cleaning and a total of seventeen months exposure. The outcome shows significant losses recorded, where a yield loss of 78.3% and efficiencies decline of 78% for amorphous Si, 77% and 77% for cadmium telluride, 70% and 71% for polycrystalline and 68.6% and 71% for the monocrystalline Si module. A wide variation of performance losses was recorded between months and seasons in 2021, and the dry season presented the most alarming rates. The optical loss results validated the above output performance losses with a similar trend. The particle characterisation reveals that mineral particles > PM 10 size with opaque and translucent morphology were the main constituent of dust formation on the examined coupons. It is recommended to study various mitigation techniques and use the correct one in an optimal cycle, which is cost-effective, which could restore and maintain the installation's optimal efficiency. • Yield losses of 78%, 77%, 70%, and 69% for modules in 12 months without cleaning. • Efficiency drop of 78% for a-Si, 77% for CdTe and 71% c-Si modules in 17 months. • Air quality data could be used to determine a region's dust property type. • The soiling losses rates of high solar potential regions are relatively unexplored. • Determining PV soiling rates and mitigation approach could enhance PV penetration. [ABSTRACT FROM AUTHOR]