Search

Half masks (a.k.a. filtering facepieces, FFP) are personal protective equipment against dust in a work environment. Their filtration efficiency is legally regulated. Occupational safety and health services have not paid enough attention to speech disruption caused by FFPs, even though the latter could impair verbal communication and result in discomfort or increased risk of accidents. This study deals with the objective differences in speech suppression between masks of various construction belonging to the same filtration class, FFP2, and equipped with exhalation valves. We applied an objective method of white noise attenuation, suggested in our previous work. Its uniqueness lies in the fact that the acoustic apparati are applied in the whole procedure, and no human speakers/listeners participation is required. We compared seven types of masks: three moulded, one moulded with folded elements, two folded horizontally, and one vertically. We determined attenuation caused by the masks in 1/3 octave-wide bands with centre frequency from 100 Hz to 20 kHz. All the studied FFPs attenuated sound waves in a frequency range responsible for 80–90% of the perceived speech intelligibility. The attenuations of moulded masks were ca. 3 dB higher in 1–16 kHz bands than those of folded ones. The moulded mask with foldable parts for better fitting the face suppressed the high-pitch tones considerably more than the other masks. These observations were confirmed quantitatively by the cluster analysis based on the Euclidean distances between the acoustic spectra. [ABSTRACT FROM AUTHOR]

Various uses of ferrofluids for technical applications continuously raise the interest in improvement and optimization of preparation methods. This paper deals with preparation of finely granulated magnetite particles coated with oleic acid in hydrocarbon suspensions following either chemical co-precipitation from iron salt precursors or wet milling of micron size magnetite powder with the goal to compare the benefits and disadvantages of each method. Microstructural measurements showed that both methods gave similar magnetite particle size of 10-15 nm. Higher saturation magnetization was achieved for the wet-milled magnetite suspension compared to relatively rapid co-precipitation synthesis. Different efficacies of ferrophase incorporation into kerosene could be related to the different mechanisms of oleic acid bonding to nanoparticle surface. The comparative data show that wet milling represents a practicable alternative to the traditional co-precipitation since despite of longer processing time, chemicals impact on environment can be avoided as well as the remnant water in the final product.

By combining oppositely charged polydiallyldimethylammonium chloride (PDADMAC) and sodium polyacrylate (NaPA), interpolyelectrolyte complexes (IPECs) can be formed in aqueous solution. Such IPECs are studied for rather short NaPA and under variation of the Mw of PDADMAC. The focus is on elucidating the effect of having a hydrophobic modification of the NaPA, which is introduced by having 10 mol% of the monomeric units substituted by ones carrying a dodecyl alkyl chain. This modification renders the complexes more hydrophobic, which is seen in the fact that precipitation of the complexes occurs at a lower mixing ratio and the biphasic region is also wider. The structures of the soluble IPECs are studied by a combination of light and neutron scattering (SANS). It is observed that the complexes formed possess typical radii of gyration of ≈30–40 nm, which become somewhat smaller with increasing length of the PDADMAC chain. The SANS data can be described well with the Beaucage model for complexes, where locally small hydrophobic domains of cylindrical shape are formed, whose persistence length decreases with increasing content of NaPA in the complexes. In contrast no such structures are seen for NaPA without the hydrophobic modification. The cylindrical domains are then arranged within larger‐sized clusters of 30–40 nm, which become more compact with reduced length of the PDAMAC chains. The structure of the IPECs is largely determined by the presence of the hydrophobic modification of the NaPA and is further controlled by the length of the hydrophobic modification. Such IPECs of controlled structure, relatively small size, and containing hydrophobic domains are potentially interesting as delivery systems due to having domains of variable polarity. [ABSTRACT FROM AUTHOR]

Magnetic iron oxide-silica shell nanocomposites (IONP@SiO2) have been prepared in a two-step procedure. IONPs were obtained by coprecipitation of iron salts, and coated by silica in sol-gel method under sonication. Two IONP/silica ratios and two drying methods, heating in oven and supercritical CO2 drying, were used. The samples were analyzed using X-ray diffraction (XRD), infrared spectroscopy, magnetic measurements, small-angle neutron scattering (SANS), nitrogen sorption, and scanning electron microscopy (SEM) coupled with energy-dispersive X-ray analysis (EDX). The iron oxide silica nanocomposites obtained via supercritical drying exhibited higher values of the specific surface area and of saturation magnetization compared to the samples synthesized with the same iron oxide content but obtained after drying at 60 °C. Pd(II) adsorption experiments were performed on the materials prepared by supercritical drying. The maximum adsorption capacity 6.5 mg/g showed that the materials can be used as good and cheap adsorbent for palladium ions from aquatic environment. [ABSTRACT FROM AUTHOR]

The purpose of the study was to investigate the appearance of certain microstructures developing in the SiO2/PVA nanocomposite xerogels at different temperatures by small-angle neutron scattering (SANS). The samples were prepared by the alcoxide route of the sol-gel method. The SANS measurements were performed over a q (scattering vector) range from 0.05 to 3.7 nm-1, providing structural information at length scales (2π/q) between approximately 1 and 100 nm. The measured small-angle scattering intensities of silica and silica/PVA samples aged at 60°C and heat-treated at different temperatures, are presented in log-log plots. It is shown that both the molecular mass of organic and the temperature of thermal treatment have strong influence on transition tendency from mass fractal toward surface fractal structures.

An alkoxysilane derivative bearing a 10-vertex closo-decaborate nanocluster (B10H102–) was successfully synthesized and immobilized in a SiO2 aerogel matrix. closo-Decaborate-containing SiO2 aerogels showed high specific surface (∼750 m2/g), open porosity (∼95%), and extremely low apparent density (80 mg/cm3) as well as increased thermal stability of the closo-decaborate moiety. Despite the low boron content (∼1.2 mol % of boron nanoclusters comprising natural mixture of boron isotopes), the aerogel nanomaterial demonstrated excellent neutron capture properties exceeding lightweight polymer-based analogues. Cell viability assessment indicated the pronounced dose-dependent toxicity of the borylated aerogel with respect to malignant cells (U251 MG glioblastoma line) and low toxicity with respect to normal cells (dental pump stem cells). The combination of the properties of closo-decaborate-modified silica aerogels makes them good candidate material for shielding of patients and healthcare personnel during boron neutron capture therapy procedures. [ABSTRACT FROM AUTHOR]