Search

The aim of the study was to determine the influence of PLGA bioresorbable polymer coating on corrosion resistance of metal biomaterial. Polymer coating deposited by immersion method was applied. Corrosion resistance of metal biomaterials (stainless steel, Ti6Al4V, Ti6Al7Nb) coated with PLGA polymer, after 90 days exposure to Ringer's solution was tested. The amount of metal ions released to the solution was also investigated (inductively coupled plasma-atomic emission spectrometry (ICP-AES) method). The surface of the samples was observed using atomic force microscopy (AFM) and scanning electron microscopy (SEM). Degradation of PLGA was monitored with the use of the 1H NMR spectroscopy and GPC (Gel Permeation Chromatography). The studies were carried out for non-sterilized (NS) and sterilized (S) samples. Application of the polymer coating causes a reduction of release of metal ions to the solution. Depending on metal substrate different course of destruction of polymer layer was observed. After 90 days of incubation in Ringer's solution polymer layer was highly degraded, however, the composition of copolymer (ratio of the comonomeric units in the chain) remained unchanged during the whole process, which suggests even degradation. The polymer layer reduced degradation kinetics of the metal substrate. Moreover, degradation process did not change surface morphology of metal substrate and did not disturb its integrity. The results obtained indicate that the applied polymer layer improves corrosion resistance of the alloys being investigated. Thus, the developed implants with bioresorbable coatings could be advantageous for medical applications.

Purpose: The paper presents the results of physicochemical and mechanical properties of the Ti-6Al-7Nb alloy with surface modified by formation of a diffusive nitrocarburized layer deposited in a low-temperature plasma process. The main aim of the study was to evaluate the influence of steam sterilization and exposure to Ringer's solution on the utility properties of the alloy., Methods: Based on the study of the microstructure, roughness, wettability, resistance to pitting corrosion, ion infiltration and mechanical properties, the usefulness of the proposed method of surface treatment for clinical application was proven., Results: Deposition of the nitrocarburized layer increased the surface roughness and surface hardness, but also reduced the contact angle, and corrosion resistance with respect to the polished surfaces. The nitrocarburized layer is a barrier against the infiltration of ions to the solution and sterilization and exposure to Ringer solution have greater effect on the physicochemical properties rather than on the mechanical ones., Conclusion: It was found that sterilization, and exposure to Ringer's solution greatly affect the change of physicochemical properties rather than mechanical properties for both nitrocarburized layers and the Ti-6Al-7Nb alloy of mechanically polished surface.

Purpose: The aim of the presented research was to find a combination of surface modification methods of implants made of the Ti-6Al-4V ELI alloy, that lead to formation of effective barrier for metallic ions that may infiltrate into solution., Methods: To this end, the following tests were carried out: roughness measurement, the voltamperometric tests (potentiodynamic and potentiostatic), and the ion infiltration test., Results: The electropolishing process resulted in the lowering of surface roughness in comparison with mechanical treatment of the surface layer. The anodization process and steam sterilization increased corrosion resistance regardless of the mechanical treatment or electropolishing. The crevice corrosion tests revealed that independent of the modification method applied, the Ti-6Al-4V ELI alloy has excellent crevice corrosion resistance. The smallest quantity of ions infiltrated to the solution was observed for surface modification consisting in the mechanical treatment and anodization with the potential of 97 V., Conclusions: Electric parameters deter- mined during studies were the basis for effectiveness estimation of particular surface treatment methods. The research has shown that the anodization process significantly influences the pitting corrosion resistance of the Ti-6Al-4V ELI alloy independent of the previous surface treatment methods (mechanical and electrochemical). The surface layer after such modification is a protective barrier for metallic ions infiltrated to solution and protects titanium alloy against corrosive environment influence.

Human papillomavirus (HPV) belongs to the diverse group of sexually transmitted viruses that manifest affinity to the squamous epithelia of the skin and mucous membranes. Over 100 types of HPV have been described and identified in human tissues, and it has been proved that persistent infection with high-risk types of the virus (types 16 and 18 in particular) could lead to cervical cancer. High-risk HPV types have been found in approximately 70% of all cases of cervical cancer worldwide. The aim of this study was to describe the role of HPV in the process of neoplastic transformation in epithelial cells and to emphasize the prophylactic significance of vaccinations against the virus.

The MCM (minichromosome maintenance protein) protein family was identified for the first time in budding yeast, Saccharomyces cerevisiae. The subgroup consists of MCM proteins 2-9, that possess the characteristic ATPase domain (MCM box). There are also MCM1 and MCM10, which are important in DNA replication, but they do not possess the specific MCM box. The main function of MCM proteins is cooperation with other factors in molecular mechanisms that form the replication fork and in regulation of DNA synthesis. MCM proteins form a ring-shaped complex, which is activated when other factors are bound. MCM 2-7 complex is one of the pre-replication factors. Association of MCM 2-7 complex is a crucial moment initiating the replication fork. MCM proteins play a role in maintaining genome integrity and prevent re-replication once per cell cycle. Proliferating cells have high levels of MCM, whereas they are not detected in quiescent, differentiated or senescent cells. They are also potential useful markers of cell proliferation. Recent studies suggested that MCMs are good markers of proliferation activity degree, because they are highly expressed in a variety of tumors. The aim of this work is to summarize current knowledge about the role of MCM proteins in DNA replication and potential diagnostic markers of proliferating cancer cells.