Search

The article discusses a method for producing silver nanoparticles (NPs) in aqueous solutions by reducing sodium borohydride in the presence of polyvinyl alcohol; selected optimal conditions for the synthesis. The resulting silver NPs have a spherical shape, with a diameter of from 30 to 130 nm. NPs are stable, do not precipitate and do not change color for 3–4weeks. Electron microscopic images confirm the formation of a thin polymer film on the surface of cellulose fiber and show a change in the morphological surface of the treated samples compared to untreated ones. The energy dispersive microanalysis data showed that the raw cotton fabric contains C – 57.02%, O – 42.98%. After processing, nanoscale particles of silver are encapsulated on the surface of the fabric – 0.18–0.28%, which are distributed rather unevenly. Modification of cellulosic textile materials of silver NPs imparts a stable antimicrobial effect , as well as improves their physico-mechanical and hygienic properties. The air permeability indicators for cotton original fabric 180 dm3/m2×sec., For the treated composition based on polyvinyl alcohol, NaBH4, and silver nitrate – 175 dm3/m2×sec. The breaking load of the fabric is: for the initial – 311 N, for treated – within 320–360 N. The indicators of air permeability and strength characteristics of cotton fabric treated with the proposed composition comply with the regulatory requirements for this group of fabrics., В статье рассматривается метод получения наночастиц (НЧ) серебра в водных растворах путем восстановления боргидридом натрия в присутствии поливинилового спирта;подобраны оптимальные условия синтеза. Образующиеся НЧ серебра имеют сферическую форму, диаметром от 30 до 130 нм. НЧ стабильны, не осаждаются и не меняют окраску в течение 3–4 недель. Электронно-микроскопические снимки подтверждают образование тонкой полимерной пленки на поверхности целлюлозного волокна и показывают изменение морфологической поверхности обработанных образцов по сравнению с необработанными. Данные энергодисперсионного микроанализа показали, что необработанная хлопковая ткань содержит C – 57.02%, O – 42.98%. После обработки на поверхности ткани инкапсулируются наноразмерные частицы серебра – 0.18–0.28%, которые распределены достаточно неравномерно. Модификация целлюлозных текстильных материалов НЧ серебра придает устойчивый антимикробный эффект, а также улучшает их физико-механические и гигиенические свойства. Показатели воздухопроницаемости для хлопчатобумажной исходной ткани – 180 дм3/м2×сек., для обработанной составом на основе поливинилового спирта, NaBH4, и нитрата серебра – 175 дм3/м2×сек. Разрывная нагрузка ткани составляет: для исходной – 311 Н, для аппретированной – в пределах 320–360 Н. Показатели воздухопроницаемости и прочностные характеристики хлопчатобумажной ткани, обработанной предлагаемой композицией, соответствуют нормативным требованиям для данной группы тканей.

The paper presents data on the development of cellulosic textile materials with increased antimicrobial properties using copper nanoparticles. Synthesis of copper nanoparticles was carried out by simple chemical reduction of an aqueous solution of copper using ascorbic acid as a reducing agent. The influence of the concentration of copper, a reducing agent, and a stabilizer on the synthesis of copper nanoparticles was studied.A composition based on polyvinyl alcohol and copper nanoparticles was developed to impart enhanced antimicrobial properties to cellulosic textile materials. The results of the studies showed that a significant growth of bacteria was observed in the control sample (untreated fabric), the amount of mesophilic aerobic and facultative anaerobic microorganisms (Staphylococcus aureus) decreased with increasing concentrations of copper nanoparticles, antibacterial properties increased. Modified by the proposed method cellulosic textile materials showed high resistance to the action of microorganisms and can be used for the production of sanitary and hygienic textile products., В статье представлены данные по разработке целлюлозных текстильных материалов с повышенными антимикробными свойствами с применением наночастиц меди. Синтез наночастиц меди осуществляли простым химическим восстановлением водного раствора сульфата меди с использованием в качестве восстановителя аскорбиновой кислоты. Исследовано влияние концентрации сульфата меди, восстановителя, стабилизатора на синтез наночастиц меди.Впервые разработана композиция на основе поливинилового спирта и наночастиц меди для придания повышенных антимикробных свойств целлюлозным текстильным материалам. Результаты исследований показали, что в контрольном образце (необработанная ткань) наблюдался значительный рост бактерий, в образцах, содержащих наночастицы меди, количество мезофильных аэробных и факультативно-анаэробных микроорганизмов (Staphylococcus aureus) снижается, с возрастанием концентрации наночастиц меди антибактериальные свойства возрастают. Модифицированные предлагаемым способом целлюлозные текстильные материалы показали высокую устойчивость к действию микроорганизмов и могут быть использованы для изготовления текстильных изделий санитарно-гигиенического назначения.