Search

Improving current injection into r- and m-planes of nanowires (NWs) is essential to realizing efficient GaInN/GaN multiple quantum shell (MQS) NW-based light-emitting diodes (LEDs). Here, we present the effects of different p-GaN shell growth conditions on the emission characteristics of MQS NW-LEDs. Firstly, a comparison between cathodoluminescence (CL) and electroluminescence (EL) spectra indicates that the emission in NW-LEDs originates from the top region of the NWs. By growing thick p-GaN shells, the variable emission peak at around 600 nm and degradation of the light output of the NW-LEDs are elaborated, which is attributable to the localization of current in the c-plane region with various In-rich clusters and deep-level defects. Utilizing a high growth rate of p-GaN shell, an increased r-plane and a reduced c-plane region promote the deposition of indium tin oxide layer over the entire NW. Therefore, the current is effectively injected into both the r- and m-planes of the NW structures. Consequently, the light output and EL peak intensity of the NW-LEDs are enhanced by factors of 4.3 and 13.8, respectively, under an injection current of 100 mA. Furthermore, scanning transmission electron microscope images demonstrate the suppression of dislocations, triangular defects, and stacking faults at the apex of the p-GaN shell with a high growth rate. Therefore, localization of current injection in nonradiative recombination centers near the c-plane was also inhibited. Our results emphasize the possibility of realizing high efficacy in NW-LEDs via optimal p-GaN shell growth conditions, which is quite promising for application in the long-wavelength region.

The superior crystalline quality of coaxial GaInN/GaN multiple-quantum shell (MQS) nanowires (NWs) was demonstrated by employing an AlGaN undershell during metal-organic chemical vapor deposition. Scanning transmission electron microscopy (STEM) results reveal that the NW structure consists of distinct GaInN/GaN regions on different positions of the NWs and the cores were dislocation-free. High-resolution atomic contrast STEM images verified the importance of AlGaN undershells in trapping the point defects diffused from n-core to MQSs (m-planes), as well as the improvement of the grown crystal quality on the apex region (c-planes). Time-integrated and time-resolved photoluminescence (PL) measurements were performed to clarify the mechanism of the emission within the coaxial GaInN/GaN MQS NWs. The improved internal quantum efficiency in the NW sample was attributed to the unique AlGaN undershell, which was able to suppress the point defects diffusion and reduce the dislocation densities on c-planes. Carrier lifetimes of 2.19 ns and 8.44 ns were derived from time-resolved PL decay curves for NW samples without and with the AlGaN undershell, respectively. Hence, the use of an AlGaN undershell exhibits promising improvement of optical properties for NW-based white and micro light-emitting diodes.

Ga-rich zones created along macrosteps in n-AlGaN plausibly function as electron pathways of AlGaN-based deep-ultraviolet (DUV) LEDs fabricated on AlN templates using 1.0°-miscut c(0001) sapphire substrates toward the m[1-100] axis. This work was performed to clarify AlN mole fractions (xAl) of Ga-rich zones. xAl ≃ (7/12, 6/12, and 5/12) was observed in Ga-rich zones in AlαGa1−αN (α ≃ 0.63, 0.55, and 0.43, respectively) by the method proposed in our previous article in which we showed that Ga-rich zones of Al8/12Ga4/12N were created in Al0.7Ga0.3N. xAl in the Ga-rich zones obtained from an energy-dispersive x-ray signal by scanning transmission electron microscopy calibrated by Rutherford backscattering well agreed with xAl obtained by cross-sectional cathodoluminescence (CL) spectroscopy using scanning electron microscopy. A weak CL shoulder peak corresponding to Al4/12Ga8/12N was also observed for Al0.43Ga0.57N. In addition, xAl ≃ n/12 (n = 6–9) in Al-rich zones appeared in the rest of the Ga-rich zones. Furthermore, nanobeam electron diffraction patterns of the Ga-rich zones indicated a high possibility of a regular configuration of Ga and Al atoms on the c(0001) plane in our samples. Consequently, xAl values in nonflat AlGaN layers with macrosteps were often determined to be near n/12 (n: integer). Thus, Ga-rich zones (xAl = n/12: n = 4–8) formed in our nonflat AlGaN layers, which originated from the macrosteps along [11–20] edgelines normal to the m[1–100] axis, are suggested to be metastable. The creation of discrete xAl in Ga-rich zones should contribute to the stable production of DUV-LEDs using high-miscut sapphire substrates. [ABSTRACT FROM AUTHOR]

In this study, we aim to understand the thermodynamics inside the junctions of GaInN-based LEDs through optical operation of the device (the wavelength of the pumping laser is 405 nm for quasi-resonant optical excitation). First, to achieve this goal, the short-circuit current vs the open-circuit voltage curve and photoluminescence spectrum are carefully analyzed and compared with the current–voltage curve and electroluminescence spectrum. By this comparative study, we experimentally demonstrate the electrical–optical energy conversion efficiency (ECE) > 100% under optical excitation. Second, the intra-band phonon absorption and emission inside and/or outside the junction (PPeltier and PHC) are investigated through the power-loss analysis. In so doing, we ascertain that the carriers in the multiple quantum wells are energized by phonons, which introduces the ECE > 100%. Specifically, after the energization, the Boltzmann carrier distribution is no longer controlled by the ambient lattice temperature but by higher temperature, namely, that of the carriers themselves. Based on the analysis, we propose a thermally enhanced effective temperature for the Boltzmann distribution. Finally, we compare the junction efficiency by photoluminescence (PL), composed of the internal quantum efficiency by PL and the ECE by PL, of the sample at various temperatures to investigate the effect of PHC on the overall PL efficiency. [ABSTRACT FROM AUTHOR]

AlGaN-based deep-ultraviolet light-emitting diodes (LEDs) incorporating uneven multiple quantum wells (MQWs) with inclined and terrace zones, which were fabricated on an AlN template with dense macrosteps, have exhibited a high internal quantum efficiency (IQE). To investigate the microscopic structure of uneven MQWs, cathodoluminescence (CL) mapping characterization was carried out, and the maps of the CL intensity at 300 K relative to that at 38 K were obtained for uneven MQWs that targeted 265 and 285 nm LEDs. At an electron beam current of less than 1.0 nA, the signals from inclined and terrace zones of the uneven MQWs were confirmed to satisfy the nonsaturated excitation condition at 300 K. Nonradiative recombination (NR) was insufficiently frozen even at 38 K, specifically on the terraces in the 265 nm MQW, suggesting high concentrations of NR centers due to point defects (PDs). In contrast, NR in the 285 nm MQW at 38 K was closer to freeze-out. The concentration of PDs in the 285 nm MQW was likely to be lower than that in the 265 nm MQW. Finally, the ratios of the CL intensity at 300 K to those at 38 K were mapped, demonstrating an approach to creating an approximate map of IQE. The values in the CL intensity ratio maps are discussed by considering the analytical error factors. The results support the model of localized current injection through Ga-rich stripe zones in the n-AlGaN cladding layer. [ABSTRACT FROM AUTHOR]

Herein, the growth mechanism and defect structure of GaN‐based nanowire multiple‐quantum‐shells (NW‐MQSs) with cap layers combining tunnel junctions and n‐GaN are investigated in detail. In the NW‐MQS structure, defect structures are formed in three regions: (i) From the c‐plane active layer at the tip of NW because of the low crystal quality of the active layer. (ii) Basal‐plane stacking faults (BSFs) with partial dislocations (PDs) are generated from the m‐planes of the NW‐MQSs; these defects are triggered by the silicon nitride (SiNx) formed on the NW surface. While some defects terminate because of the half loop formed by the PDs along the lateral growth of cap layers, others terminate at the coalesced region of the cap layers grown from adjacent MQSs. (iii) Line defects due to low‐angle grain boundaries and planar defects due to the BSFs in region (ii) are formed in the region wherein cap layers coalesce. The defects reaching the surface of the cap layers predominantly depend on the number of defects generated from the c‐plane active layers in region (i). The growth mode and propagation mechanism of such defects are associated, and a method for realizing optical devices based on the high‐quality NW‐MQS structures is discussed. [ABSTRACT FROM AUTHOR]