Search

Abstract: A range of SiO x -like coatings was deposited on glass slides from a hexamethylsiloxane precursor by plasma-assisted CVD. The effect of varying deposition parameters, specifically ion cleaning time and HMDSO/O2 ratios, on the coating properties and antifouling performance was investigated. At low HMDSO/O2 ratios, the resulting coatings were close to SiO2. Carbon content in the bulk of the coatings increased with increasing HMDSO/O2 ratio. Coatings deposited at high HMDSO/O2 ratios and with the longest cleaning time (30min), elevated the relative carbon content to 25 atomic %. Surface energies (22–43mJ/m) were correlated with the degree of surface oxidation and hydrocarbon content. With the exception of the most polar coatings the apolar component of the surface energy (γ LW) was the dominant component. In the most hydrophilic coatings, the Lewis base component of the surface energy (γ −) was dominant. Significantly improved antifouling performance was detected with the most reduced coatings deposited using the extended ion cleaning times. For both, the removal of sporelings of the marine green alga, Ulva linza and the initial adhesion of the freshwater bacterium, Pseudomonas fluorescens, there was a strong, positive correlation between strength of attachment and ion cleaning time. Increased ion cleaning time will elevate the deposition temperature, increasing decomposition rates and thus the crosslinking of the polymer. Increased cross-linking may render these coatings less permeable to penetration and mechanical interlocking by the adhesive polymers used by these organisms, thus reducing their adhesion. Films with improved biological performance have potential for use as coatings in the control of biofouling in applications such as heat exchangers, where thin films are important for effective thermal transfer, or optical windows where transparency is important. [Copyright &y& Elsevier]

Printed electronics are considered for wireless electronic tags and sensors within the future Internet-of-things (loT) concept. As a consequence of the low charge carrier mobility of present printable organic and inorganic semiconductors, the operational frequency of printed rectifiers is not high enough to enable direct communication and powering between mobile phones and printed e-tags. Here, we report an all-printed diode operating up to 1.6 GHz. The device, based on two stacked layers of Si and NbSi2 particles, is manufactured on a flexible substrate at low temperature and in ambient atmosphere. The high charge carrier mobility of the Si microparticles allows device operation to occur in the charge injection-limited regime. The asymmetry of the oxide layers in the resulting device stack leads to rectification of tunneling current. Printed diodes were combined with antennas and electrochromic displays to form an all-printed e-tag. The harvested signal from a Global System for Mobile Communications mobile phone was used to update the display. Our findings demonstrate a new communication pathway for printed electronics within loT applications. [ABSTRACT FROM AUTHOR]

Abstract: A range of hybrid, SiOCH films were deposited on silicon substrates within a radio frequency plasma reactor using hexamethyldisiloxane (HMDSO) as a precursor. The plasma polymerized films were deposited at various HMDSO/argon/oxygen ratios. The composition and structure, at microscopic and nanoscopic levels, of the deposited films were determined by external reflection and transmission Fourier Transform Infrared (FTIR) spectroscopy as well as by X-Ray Photoelectron Spectroscopy (XPS). The content of carbon and oxygen in films were found to be inversely proportional to each other. XPS results showed that the outermost surface of the deposited films are nanoporous and coexist with microporosity which was revealed by electron microscopy. The structure of deposited coatings is anisotropic as was documented by polarized external reflection FTIR spectroscopy. Several correlations between the film chemical composition, surface structure, and macroscopic properties of the films such as: hydrophobicity and hydrophilicity were established. [Copyright &y& Elsevier]