Search

Purpose: To evaluate the peri-implant parameters of immediately placed and loaded mandibular overdentures over a 5-year follow-up period. Materials and Methods: All subjects who had been advised and planned for two-implant mandibular overdenture treatment were included in this study. The peri-implant parameters –including plaque index (PI), bleeding index (BI) and peri-implant pocket depth (PIPD) as well as marginal bone loss (MBL) – were assessed. In addition, prosthodontic parameters including abutment-, implant- and denture-related complications were assessed. Patients were evaluated at follow-up visits, scheduled at 1, 12, 24, 36, 48, and 60 months. The data distribution was analysed with the Shapiro-Wilk test. Data within follow-up categories were compared using ANOVA and the Tukey-Kramer test. A p-value < 0.05 was considered statistically significant. Results: Among the 32 participants, 19 were males and 13 were females, with a mean age of 60.5 ± 7.33. The mean plaque index (PI), bleeding index (BI) and peri-implant pocket depth (PIPD) varied over time. However, no statistically significant difference was observed in the plaque index, bleeding index and peri-implant pocket depth over time (p > 0.05). The mean value at baseline was found to be -0.9 ± 0.3. The values increased over time, with the highest value observed at 60 months 2.6 ± 0.7, which was statistically significant (p < 0.001). Conclusion: Immediately placed and loaded mandibular implant overdentures using two un-splinted implants with locator attachments showed acceptable PI, BI and PIPD at the 5-year follow-up. Statistically significantly greater marginal bone loss was observed from baseline to follow-up, but it was within acceptable limits. A moderate number of restorative and abutment complications were observed during the follow-up of IODs. [ABSTRACT FROM AUTHOR]

The current study aimed to compare the mechanical properties of CAD/CAM fabricated hybrid ceramic restorative materials. The current study assessed the mechanical properties of additively and subtractively manufactured CAD/CAM fabricated hybrid ceramic by conducting flexure strength test, compressive strength test, and Vickers hardness test. Flexural samples were subjected to a three-point bending test using a universal testing machine until the samples showed fracture. Moreover, samples for the compressive strength test were subjected to compression tests using a universal testing machine until samples were fractured. Samples for the Vickers hardness was tested using the Vickers hardness testing machine to determine the sample's hardness values. There were significant differences (p = 0.0001) were observed among the additive and subtractive groups in terms of flexure strength and compressive strength test. Regarding the Vickers hardness test, significant differences (p = 0.0001) were observed between the polished and unpolished groups in additive manufacturing. However, no significant (p = 0.681) differences were observed in the subtractive manufacturing technique. The subtractive group achieved ISO specifications in terms of flexural strength and was superior to additive groups in hardness while exhibiting lower performance in compressive strength. Moreover, printing orientation had a significant influence on the performance of additive groups. Flexural strength and hardness were improved when the printing orientation was in alignment with the direction of load (90°) while compressive strength was improved when the printing orientation was perpendicular to the direction of load (0°). [ABSTRACT FROM AUTHOR]