A series of Dy2Co17−xGax polycrystalline samples with x from 0 to 7 were prepared by arc melting. X-ray powder diffraction analysis indicated that these compounds have the hexagonal Th2Ni17 structure for x≤3 and the rhombohedral Th2Zn17 structure for 3.5≤x≤7. The lattice parameters a and c increase linearly with the gallium content until x=5.3. With further increasing the gallium content x up to 7, the lattice parameter c slightly decreases, whereas the lattice parameter a increases more quickly than that for 0≤x≤5.3. The unit-cell volume shows an approximately linear increase of 6.1 Å3/Ga for 0≤x≤3.0 and 10.1 Å3/Ga for 3.5≤x≤7.0, respectively. Rietveld refinement of the Dy2Co11.7Ga5.3 compound reveals that the Ga atoms occupy all the 6c, 9d, 18f, and 18h sites and preferentially occupy the 6c site. The Curie temperature and the saturation magnetization of the rhombohedral Dy2Co17−xGax compounds decrease almost linearly with increasing Ga content.

Diaspore (α-AlOOH) was heated at various temperatures from 300 to 1 000 °C for 2 h. The alteration of diaspore by thermal treatment was investigated by differential thermal analysis, thermogravimetric analysis and X-ray diffraction. The mechanism of thermal decomposition of diaspore was discussed according to the Coats-Redfern equation. It is found that after thermal treatment at 500 °C, diaspore is transformed entirely to corundum (α-Al2O3). Combined with the mass loss ratio obtained from the thermogravimetric analysis data, the activation energies for the thermal treatment of diaspore are calculated as Ea=10.4 kJ/mol below 400 °C and Eb=47.5 kJ/mol above 400 °C, respectively, which is directly related to the structural alteration of diaspore during the thermal treatment. The results indicate that the thermal decomposition of diaspore is conducted primarily by means of an interfacial reaction.