Search

A unique 1D nanostructure of Pt@CeO2-BDC was prepared from Pt@CeBDC MOF. The Pt@CeO2-BDC was rich in oxygen vacancies (i.e., XPS O-beta/(O-alpha + O-beta) = 39.4%), and on the catalyst, the 2 nm Pt clusters were uniformly deposited on the 1D mesoporous polycrystalline CeO2. Toluene oxidation was conducted in a spectroscopic operando Raman-online FTIR reactor to elucidate the reaction mechanism and establish the structure-activity relationship. The reaction proceeds as follows: (I) adsorption of toluene as benzoate intermediates on Pt@CeO2-BDC at low temperature by reaction with surface peroxide species; (II) reaction activation and ring-opening involving lattice oxygen with a concomitant change in defect densities indicative of surface rearrangement; (III) complete oxidation to CO2 and H2O by lattice oxygen and reoxidation of the reduced ceria with consumption of adsorbed oxygen species. The Pt clusters, which mainly exist as Pt2+ with minor amounts of Pt-0 and Pt4+ on the surface, facilitated the adsorption and reaction activation. The Pt-CeO2 interface generates reduced ceria sites forming nearby adsorbed peroxide at low temperature that oxidize toluene into benzoate species by a Langmuir-Hinshelwood mechanism. As the reaction temperature increases, the role of lattice oxygen becomes important, producing CO2 and H2O mainly by the Mars-van Krevelen mechanism.

A unique 1D nanostructure of Pt@CeO2-BDC was prepared from Pt@CeBDC MOF. The Pt@CeO2-BDC was rich in oxygen vacancies (i.e., XPS O-beta/(O-alpha + O-beta) = 39.4%), and on the catalyst, the 2 nm Pt clusters were uniformly deposited on the 1D mesoporous polycrystalline CeO2. Toluene oxidation was conducted in a spectroscopic operando Raman-online FTIR reactor to elucidate the reaction mechanism and establish the structure-activity relationship. The reaction proceeds as follows: (I) adsorption of toluene as benzoate intermediates on Pt@CeO2-BDC at low temperature by reaction with surface peroxide species; (II) reaction activation and ring-opening involving lattice oxygen with a concomitant change in defect densities indicative of surface rearrangement; (III) complete oxidation to CO2 and H2O by lattice oxygen and reoxidation of the reduced ceria with consumption of adsorbed oxygen species. The Pt clusters, which mainly exist as Pt2+ with minor amounts of Pt-0 and Pt4+ on the surface, facilitated the adsorption and reaction activation. The Pt-CeO2 interface generates reduced ceria sites forming nearby adsorbed peroxide at low temperature that oxidize toluene into benzoate species by a Langmuir-Hinshelwood mechanism. As the reaction temperature increases, the role of lattice oxygen becomes important, producing CO2 and H2O mainly by the Mars-van Krevelen mechanism.

A catalytic material which includes a metal oxide catalyst anchored to a nano-sized metal oxide crystal as support and functions well at low temperatures. The catalytic material may optionally include another metal oxide as a promoter deposited on the surface of the support to modify the properties of the metal oxide catalyst and/or the properties of the support. The catalyst may be vanadium oxide, tungsten oxide, manganese oxide, chromium oxide or molybdenum oxide; the support may be TiO2 , SiO2 , Al2O3 , ZrO2 , or WO3 ; and the promoter may be vanadium oxide, tungsten oxide, manganese oxide, chromium oxide or molybdenum oxide. The present invention also provides a method of producing the catalytic materials, which is useful in removing ammonia and other nitrogen containing contaminants.