Search

Poly(methyl methacrylate-glycidyl methacrylate) [Poly(MMA-GMA)] cryogels were synthesized using monomers of methylmethacrylic acid and epoxy group bearing GMA via radical cryopolymerization technique. Synthesized cryogels were used for the immobilization of amyloglucosidase to the cryogel surface using epoxy chemistry. Characterizations of the free and immobilized amyloglucosidase were carried out by comparing the optimum and kinetic parameters of enzymes. For this, pH and temperature profiles of free and immobilized preparation were studied and, it was found that, optimum pH of enzyme was not change upon immobilization (pH 5.0), while optimum temperature of the enzyme shifted 10 °C to warmer region after immobilization (optimum temperatures for free and immobilized enzyme were 55 and 65 °C, respectively). Kinetic parameters of free and immobilized enzyme were also investigated and Km values of free and immobilized amyloglucosidase were found to be 2.743 and 0.865 mg/mL, respectively. Vmax of immobilized amyloglucosidase was found to be (0.496 µmol/min) about four times less than that of free enzyme (2.020 µmol/min). Storage and operational stabilities of immobilized amyloglucosidase were also studied and it was showed that immobilized preparation had much more stability than free preparation. In the present work, amyloglucosidase immobilized poly(MMA-GMA) cryogels were used for continuous glucose syrup production from starch for the first time. Efficiency of immobilized enzyme was investigated and released amount of glucose was found to be 2.54 mg/mL at the end of the 5 min of hydrolysis. The results indicate that the epoxy functionalized cryogels offer a good alternative for amyloglucosidase immobilization applications with increased operational and thermal stability, and reusability. Also, these cryogels can be used for immobilization of other industrially valuable enzymes beyond amyloglucosidase.

Poly(2-hydroxyethyl methacrylate-co-glycidyl methacrylate) [poly(HEMA-GMA)] cryogel was synthesized by cryopolymerization technique at frozen temperature. Iminodiacetic acid (IDA) was then attached covalently to the cryogel as a chelating agent. Then, poly(HEMA-GMA)-IDA cryogel was chelated with Ni(II) ions and this novel metal affinity support was used for adsorption of urease from its aqueous solution. Urease adsorption experiments were carried out in a continuous system by using a peristaltic pump. Maximum urease adsorption onto poly(HEMA-GMA)-IDA-Ni(II) cryogel was found to be 11.30 mg/g cryogel at pH 5.0 acetate buffer and in 25 °C medium temperature. Urease adsorption capacity decreased with increasing ionic strength and increasing chromatographic flow rate. Adsorption kinetics of urease onto poly(HEMA-GMA)-IDA-Ni(II) cryogel was also investigated and it was found that Langmuir adsorption model is applicable for this adsorption study. This novel immobilized metal affinity chromatography support was used 10 times without any decrease at their adsorption capacity. It was also observed that urease enzyme was repeatedly adsorbed and desorbed without significant lost in enzymatic activity.

Supermacroporous poly(2-hydroxyethyl methacrylate) [poly(HEMA)] monolithic cryogel was prepared by radical cryocopolymerization of HEMA with N,N'-methylene bisacrylamide as crosslinker. Reactive Green 5 dye was immobilized to the cryogel with nucleophilic substitution reaction, and this dye attached cryogel column was used for affinity purification of papain from Carica papaya latex. Reactive Green 5-immobilized poly(HEMA) cryogel was characterized by swelling studies, Fourier transform infrared spectroscopy, scanning electron microscopy, and energy dispersive X-ray analysis. Maximum papain adsorption capacity was found to be 68.5 mg/g polymer while nonspecific papain adsorption onto plain cryogel was negligible (3.07 mg/g polymer). Papain from C. papaya was purified 42-fold in single step with dye attached cryogel, and purity of papain was shown by silver-stained sodium dodecyl sulfate-polyacrylamide gel electrophoresis.

In this presented work, poly(HEMA-GMA) cryogel was synthesized and used for the immobilization of alcohol dehydrogenase. For this, synthesized cryogels were functionalized with iminodiacetic acid and chelated with Zn(2+). This metal-chelated cryogels were used for the alcohol dehydrogenase immobilization and their kinetic parameters were compared with free enzyme. Optimum pH was found to be 7.0 for both immobilized and free enzyme preparations, while temperature optima for free and immobilized alcohol dehydrogenase was 25 °C. Kinetic constants such as K(m), V(max), and k(cat) for free and immobilized form of alcohol dehydrogenase were also investigated. k(cat) value of free enzyme was found to be 3743.9 min(-1), while k(cat) for immobilized enzyme was 3165.7 min(-1). Thermal stability of the free and immobilized alcohol dehydrogenase was studied and stability of the immobilized enzyme was found to be higher than free form. Also, operational stability and reusability profile of the immobilized alcohol dehydrogenase were investigated. Finally, storage stability of the free and immobilized alcohol dehydrogenase was studied, and at the end of the 60 days storage, it was demonstrated that, immobilized alcohol dehydrogenase was exhibited high stability than that of free enzyme.

In this study, poly (methyl methacrylate-glycidyl methacrylate) [poly(MMA-GMA)] cryogels were prepared by radical cryocopolymerization of MMA with GMA as a functional comonomer. Reactive Green 19 dye was then attached to the cryogel by nucleophilic substitution reaction, and this dye-attached cryogel column was used for lysozyme adsorption. Characterization of the cryogel was performed by Fourier transform infrared spectroscopy, environmental scanning electron microscopy, Brunauer-Emmett-Teller, and energy dispersive X-ray analysis. Pore size of the cryogels was 15-30 μm and pores were interconnected structure. Attached amount of Reactive Green 19 to cryogel support was calculated as 106.25 μmol/g cryogel. Lysozyme adsorption studies were carried out by using a continuous system. It was found that the maximum amount of lysozyme adsorption (32 mg/g cryogel) obtained from experimental results was found to be approximately same with the calculated Langmuir adsorption capacity (33 mg/g cryogel). Desorption of adsorbed lysozyme was carried out by using 1.5 M NaCl in pH 4.5 acetate buffer, and desorption yield was found to be 97.4%. Cryogels were very stable, and it was found that there was no remarkable reduction in the adsorption capacity at the end of ten adsorption-desorption cycles. As a result, Reactive Green 19-attached cryogels have great advantages such as easy preparation, rapid adsorption, and desorption, being economic and allowing the direct separation of proteins.

In this work, bacterial cellulose nanofibers were produced by using the Gluconacetobacter hansenii HE1 strain. These nanofibers were derivatized with dye affinity ligand Reactive Green 5, and these newly synthesized dye-attached nanofibers were used for affinity adsorption of urease. Reactive Green 5-attached nanofibers were characterized by Fourier transform infrared spectroscopy, SEM, and energy-dispersive x-ray spectroscopy analysis. Some adsorption conditions which significantly affect the adsorption efficiency were investigated. The maximum urease adsorption capacity was found to be 240 mg/g nanofiber in pH 6.0 and at room temperature. Dye-free plain nanofibers also used for studying nonspecific urease adsorption onto plain nanofibers and nonspecific adsorption were found to be negligible (3.5 mg/g nanofiber). Prepared dye-attached nanofibers can be used in five successive adsorption/desorption steps without any decrease in their urease adsorption capacity. The desorption rate of the adsorbed urease was found to be 98.9 %. The activity of the urease was also investigated, and it was found that free and desorbed urease from the dye-attached nanofibers showed similar specific activity.

In this study, poly(2-hydroxyethyl methacrylate-glycidylmethacrylate) [poly(HEMA-GMA)] cryogels were prepared by radical cryocopolymerization of HEMA with GMA as a functional comonomer and N,N'-methylene-bisacrylamide (MBAAm) as a crosslinker. Iminodiacetic acid (IDA) functional groups were attached via ring opening of the epoxy group on the poly(HEMA-GMA) cryogels and then Zn(II) ions were chelated with these structures. Characterization of cryogels was performed by FTIR, SEM, EDX and swelling studies. These cryogels have interconnected pores of 30-50 μm size. The equilibrium swelling degree of Zn(II) chelated poly(HEMA-GMA)-IDA cryogels was approximately 600%. Zn(II) chelated poly(HEMA-GMA)-IDA cryogels were used in the adsorption of alcohol dehydrogenase from aqueous solutions and adsorption was performed in continuous system. The effects of pH, alcohol dehydrogenase concentration, temperature, and flow rate on adsorption were investigated. The maximum amount of alcohol dehydrogenase adsorption was determined to be 9.94 mg/g cryogel at 1.0mg/mL alcohol dehydrogenase concentration and in acetate buffer at pH5.0 with a flow rate of 0.5 mL/min. Desorption of adsorbed alcohol dehydrogenase was carried out by using 1.0M NaCI at pH8.0 phosphate buffer and desorption yield was found to be 93.5%. Additionally, these cryogels were used for purification of alcohol dehydrogenase from yeast with a single-step. The purity of desorbed alcohol dehydrogenase was shown by silver-stained SDS-PAGE. This purification process can successfully be used for the purification of alcohol dehydrogenase from unclarified yeast homogenates and this work is the first report about the usage of the cryogels for purification of alcohol dehydrogenase.

A novel metal-chelate affinity matrix utilizing N-acetyl cysteine as a metal chelating agent was synthesized. For this, magnetic Fe3O4 core was coated with silver by chemical reduction. Then, these magnetic silver nanoparticles were covered with N-acetyl cysteine, and Fe3+ was chelated to this modified magnetic silver nanoparticle. These magnetic nanoparticles were characterized by SEM, AFM, EDX, and ESR analysis. Synthesized nanoparticles were spherical and average size is found to be 69 nm. Fe3+ chelated magnetic silver nanoparticles were used for the adsorption of ferritin from its aqueous solution. Optimum conditions for the ferritin adsorption experiments were performed at pH 6.0 phosphate buffer and 25 °C of medium temperature and the maximum ferritin adsorption capacity is found to be 89.57 mg/g nanoparticle. Ferritin adsorption onto magnetic silver nanoparticles was increased with increasing ferritin concentration while adsorption capacity was decreased with increasing ionic strength. Affinity of the magnetic silver nanoparticles to the ferritin molecule was shown with SPR analysis. It was also observed that the adsorption capacity of the magnetic silver nanoparticles was not significantly changed after the five adsorption/desorption cycles.