Ceramic processing is one of the most efficient and environmentally friendly solutions to the enormous amounts of industrial mud produced in metal surface treatments. Moreover, ceramized products may represent an important secondary source to replace clay materials and cut down manufacturing costs. After characterization, in order to prepare specimens by uniaxial die pressing, mud was incorporated into a clay matrix at rates between 1 and 5 wt %. Compression strength, linear contraction, suction capacity and water absorption of the moulded materials were evaluated. Finally, metal leakage was characterized through chemical analysis of lixiviates. The results showed an improvement in mechanical properties following the incorporation of mud into the ceramic materials. The resulting materials meet health and safety regulations regarding dangerous waste recycling.La ceramización es una de las soluciones más eficientes y medioambientalmente más ecológicas para las enormes cantidades de lodos industriales que se producen en el tratamiento de superficies metálicas. Además estos lodos convenientemente ceramizados pueden representar una fuente de materia prima que sustituya en parte el consumo de arcilla, lo que se traduce en una disminución de los costes de fabricación. Tras caracterizarse, los lodos fueron incorporados en la matriz cerámica en proporciones desde el 1% hasta el 5%, fabricándose así piezas cerámicas por compresión uniaxial en seco. A las piezas conformadas se les midieron una serie de características tecnológicas tales como la resistencia a la compresión, la contracción lineal, capacidad de succión y la absorción de agua. Finalmente se realizaron análisis químicos de lixiviados para evaluar la liberación al medio de metales. Los resultados conseguidos muestran una mejora de las propiedades mecánicas tras la inclusión de los lodos en matrices cerámicas. Los materiales así fabricados satisfacen la normativa referente al reciclaje de residuos peligrosos.

A new aluminium polynuclear crystalline species, Al(13)(OH)(30)(H(2)O)(15)Cl(9) has been synthesized and characterized. It is a particular case of the Al(13)(OH)(30-y)(H(2)O)(18-x)Cl(9) x zH(2)O family. It has been obtained from aluminium waste cans treated with HCl solution in strong acid media, followed by an ageing period. The crystalline structure of the complex was determined by XRD spectroscopy. Twelve reflections were found and indexed with the DICVOL04 software. Morphologically, a flattened preferred orientation was observed by SEM and FESEM. The chemical structure was studied by several absorption spectroscopy techniques: FTIR, ATR-FTIR and Raman dispersion spectroscopy. The coordination of the aluminium nuclei was determined by Al-MAS-NMR. Only octahedral sites were observed. Thermal characterization of the compound was performed by evolved gas analysis (EGA) coupled to simultaneous TGA-DSC.