Highlights This study is an attempt to develop high‐quality hybrid composites via functionalization (for homogeneous distribution) of the graphene nanoplatelets (FGNP) and then doping to carbon fiber reinforced especial aviation epoxy matrix (Araldite LY5052) via vacuum bagging molding (VBM). The utilized materials were characterized by UV–Vis spectroscopy, tensile, impact, hardness tests, and fracture mode analysis using a scanning electron microscope (SEM). The results revealed a 92% (502.5 MPa) and 85% (490 MPa) improvement in tensile strength values by doping the 1 and 1.5 wt% FGNPs, respectively. There was an improvement in impact strength with the addition of FGNP; a 28% (3.23 J/mm2) increase was achieved in the nanocomposite with 1 wt% FGNP added, and there was a decrease again in the nanocomposite with 1.5 wt% FGNP added. However, it was still 12% (2.83 J/mm2) better than the neat composite. In addition, the results of examining the fractured surface structures of the impact and tensile test specimens were compatible with these results. It reveals a significant separation of fiber‐matrix bonds with 1.5 wt% FGNP contribution. While tensile and impact strengths peak at 1 wt% FGNP value and decrease afterward, hardness values increase in parallel with the increase in FGNPs. Composites were developed by functionalized graphene nanoplatelets (FGNP). The fiber‐matrix interface was strengthened with FGNP interphase. A 92% tensile strength increase was achieved with 1 wt% FGNP additives. 28% in impact strength and 55% in hardness increase by 1 wt% FGNP. The morphology confirmed that the FGNP interphase filled the interface. [ABSTRACT FROM AUTHOR]

This work is an attempt to evaluate the effect of multi-wall carbon nanotube (MWCNT) reinforcement on the properties of non-crimp fabric (NCF) carbon fiber-reinforced polymer hybrid composite (CFRP). MWCNT NCF-CFRP plates were produced by vacuum infusion. Epoxy-MWCNT mixtures were prepared by adding a surfactant, Triton-X 100, and ethanol and mixing ultrasonically. The plates were subjected to thermal and electrical conductivity, DSC and FT-IR characterizations, and tensile testing. SEM image analyses evaluated tensile fracture surfaces. Results showed that 0.5 wt% MWCNT-reinforced nanocomposite samples exhibited better tensile properties than pure NCF-CFRP composites and other nanocomposite samples. The 1.5% MWCNT reinforced sample was the best conductor at all temperatures. The temperature increases also increase the conductivity. However, the conductivity value of 0.5% MWCNT reinforced material increased significantly at low frequencies such as 100–10,000 Hz. The heat reaction of the 0.5 wt% MWCNT nanocomposite was also a bit higher than that of 1–1.5 % wt MWCNT nanocomposites, indicating a decrease in the cure. [ABSTRACT FROM AUTHOR]