Search

The results of simulation experiments on different materials are analyzed. Using irradiation with charged particle beams one can reproduce and examine practically all the known radiation effects and investigate physical nature of these effects in more details under well-controlled conditions. Characteristics of some radiation sources used for studies of radiation effects and radiation resistance and experimental procedures are presented. The accelerator systems, high-tech instrumentations and methodologies for the analysis of experimental data provide a comprehensive tool for determination of mechanisms of radiation damage and selection of materials with high radiation resistance. Проанализированы результаты имитационных экспериментов на различных материалах. Используя облучение пучками заряженных частиц, можно воспроизвести и исследовать практически все известные радиационные эффекты, а также изучить физическую природу этих эффектов более детально в хорошо контролируемых условиях. Представлены характеристики некоторых источников облучения, используемых для исследования радиационных эффектов, радиационной стойкости, и экспериментальные процедуры. Ускорительные системы, высокотехнологичные измерительные приборы и методики для анализа экспериментальных данных являются всеобъемлющим инструментом для определения механизмов повреждения и отбора материалов с высокой радиационной стойкостью. Проаналізовано результати імітаційних експериментів на різних матеріалах. Використовуючи опромінення пучками заряджених часток, можна відтворити та дослідити практично всі відомі радіаційні ефекти, а також вивчити фізичну природу цих ефектів більш детально в добре контрольованих умовах. Представленo характеристики деяких джерел опромінення, що використовуються для дослідження радіаційних ефектів, радіаційної стійкості, та експериментальні процедури. Прискорювальні системи, високотехнологічні вимірювальні прилади та методики для аналізу експериментальних даних є всеосяжним інструментом для визначення механізмів пошкодження та відбору матеріалів з високою радіаційною стійкістю.

Using mechanical alloying, experimental samples of austenitic stainless steel 08Cr18Ni10Ti dispersion hardening nano systems Y₂O₃-ZrO₂ different composition. The microstructure of samples at various stages of preparation, depending on the composition of an oxide of the alloying conditions and thermal-mechanical processing. Defined structural parameters tape sample (particle size, density and size distribution of the precipitates, etc.). The mechanical properties of tapes at room temperature and at 700 ºC and it is shown that the characteristics ODS steel is significantly higher compared with a conventional steel, obtained according to the same modes. This difference is particularly significant in the test conditions at 700 ºC, where the yield strength of ODS steel is 2.3 times higher than for initial steel 08Cr18Ni10Ti. ODS steel ductility is somewhat lower than the initial one, but its value remains at a level sufficient for the technological and operational goals. С использованием механического легирования получены экспериментальные образцы аустенитной нержавеющей стали 08Х18Н10Т, дисперсно-упрочненной нанооксидами системы Y₂O₃-ZrO₂ различного состава. Изучена микроструктура образцов на разных стадиях получения в зависимости от состава легирующего оксида и условий механико-термической обработки, определены их структурные параметры (размер зерен, плотность и распределение выделений по размерам и др.). Измерены механические свойства лент и показано, что характеристики ДУО стали существенно выше по сравнению с обычной сталью, полученной по тем же режимам. Особенно существенное различие в условиях испытаний при 700 ºС, где увеличение условного предела текучести составляет 2,3 раза. Пластичность ДУО стали несколько ниже, чем у исходной, однако ее величина остается на уровне, достаточном для технологических и эксплуатационных целей. З використанням механічного легування отримані експериментальні зразки аустенітної нержавіючої сталі 08Х18Н10Т, дисперсно-зміцненої нанооксидами системи Y₂O₃-ZrO₂ різного складу. Вивчено мікроструктуру зразків на різних стадіях отримання залежно від складу легуючого оксиду та умов механіко-термічної обробки. Визначено структурні параметри стрічкових зразків (розмір зерен, щільність і розподіл виділень за розмірами та ін.). Виміряно механічні властивості стрічок при кімнатній температурі і при 700 ºС і показано, що характеристики ДЗО сталі істотно вищі в порівнянні із звичайною сталлю, отриманою за тими ж режимами. Особливо істотне це розходження в умовах випробувань при 700 ºС, де зростання умовної межі текучості становить близько 2,3 рази. Пластичність ДЗО сталі трохи нижча, ніж у вихідної, однак її величина залишається на рівні, достатньому для технологічних та експлуатаційних цілей.