Search

In the present study, LiFePO4/CNF self-standing cathodes for LIBs are synthesized by electrospinning. A lower active material amount (12.3 and 34.5 wt%) is used, compared to the conventional tape-casted cathodes (70–85 wt%). The characterization techniques (XRPD, SEM, TEM, EDS, Raman spectroscopy, and thermogravimetry) confirm that the olivine-type structure of LiFePO4 is maintained in the binder-free electrodes, and the active material is homogeneously dispersed into and within the carbon nanofibers. The electrochemical investigation demonstrates that higher Li+ diffusion coefficients (1.36 × 10−11 cm2/s) and improved reversibility are reached for free-standing electrodes, compared to the LiFePO4 tape-casted cathode (80 wt% of active material) appositely prepared for comparison. The 34.5 wt% LiFePO4 self-standing cathode displays a lower capacity fading, good reversibility and stability, enhanced capacity values at C-rates higher than 5C, and a good lifespan when cycled 1000 cycles at 1C and further cycled up to 20C, compared to the tape-casted counterpart. Notably, the improved electrochemical performances are obtained by only the 34.5 wt% of active material. The results evidence the relevant role of the CNF matrix suitable to host LiFePO4, to promote electrolyte permeation and contact with the active material, and to increase the electronic conductivity. [ABSTRACT FROM AUTHOR]

Self-standing Na3MnTi(PO4)3/carbon nanofiber (CNF) electrodes are successfully synthesized by electrospinning. A pre-synthesized Na3MnTi(PO4)3 is dispersed in a polymeric solution, and the electrospun product is heat-treated at 750 °C in nitrogen flow to obtain active material/CNF electrodes. The active material loading is 10 wt%. SEM, TEM, and EDS analyses demonstrate that the Na3MnTi(PO4)3 particles are homogeneously spread into and within CNFs. The loaded Na3MnTi(PO4)3 displays the NASICON structure; compared to the pre-synthesized material, the higher sintering temperature (750 °C) used to obtain conductive CNFs leads to cell shrinkage along the a axis. The electrochemical performances are appealing compared to a tape-casted electrode appositely prepared. The self-standing electrode displays an initial discharge capacity of 124.38 mAh/g at 0.05C, completely recovered after cycling at an increasing C-rate and a coulombic efficiency ≥98%. The capacity value at 20C is 77.60 mAh/g, and the self-standing electrode exhibits good cycling performance and a capacity retention of 59.6% after 1000 cycles at 1C. Specific capacities of 33.6, 22.6, and 17.3 mAh/g are obtained by further cycling at 5C, 10C, and 20C, and the initial capacity is completely recovered after 1350 cycles. The promising capacity values and cycling performance are due to the easy electrolyte diffusion and contact with the active material, offered by the porous nature of non-woven nanofibers. [ABSTRACT FROM AUTHOR]

The NASICON-structured Na3MnZr(PO4)3 compound is a promising high-voltage cathode material for sodium-ion batteries (SIBs). In this study, an easy and scalable electrospinning approach was used to synthesize self-standing cathodes based on Na3MnZr(PO4)3 loaded into carbon nanofibers (CNFs). Different strategies were applied to load the active material. All the employed characterization techniques (X-ray powder diffraction (XRPD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS), thermal gravimetric analysis (TGA), and Raman spectroscopy) confirmed the successful loading. Compared to an appositely prepared tape-cast electrode, Na3MnZr(PO4)3/CNF self-standing cathodes demonstrated an enhanced specific capacity, especially at high C-rates, thanks to the porous conducive carbon nanofiber matrix. Among the strategies applied to load Na3MnZr(PO4)3 into the CNFs, the electrospinning (vertical setting) of the polymeric solution containing pre-synthesized Na3MnZr(PO4)3 powders resulted effective in obtaining the quantitative loading of the active material and a homogeneous distribution through the sheet thickness. Notably, Na3MnZr(PO4)3 aggregates connected to the CNFs, covered their surface, and were also embedded, as demonstrated by TEM and EDS. Compared to the self-standing cathodes prepared with the horizontal setting or dip–drop coating methods, the vertical binder-free electrode exhibited the highest capacity values of 78.2, 55.7, 38.8, 22.2, 16.2, 12.8, 10.3, 9.0, and 8.5 mAh/g at C-rates of 0.05C, 0.1C, 0.2C, 0.5C, 1C, 2C, 5C, 10C, and 20C, respectively, with complete capacity retention at the end of the measurements. It also exhibited a good cycling life, compared to its tape-cast counterpart: it displayed higher capacity retention at 0.2C and 1C, and, after cycling 1000 cycles at 1C, it could be further cycled at 5C, 10C, and 20C. [ABSTRACT FROM AUTHOR]

The present work aimed at decorating halloysite nanotubes (HNT) with magnetic Fe3O4 nanoparticles through different synthetic routes (co-precipitation, hydrothermal, and sol-gel) to test the efficiency of three magnetic composites (HNT/Fe3O4) to remove the antibiotic ofloxacin (OFL) from waters. The chemical–physical features of the obtained materials were characterized through the application of diverse techniques (XRPD, FT-IR spectroscopy, SEM, EDS, and TEM microscopy, thermogravimetric analysis, and magnetization measurements), while ecotoxicity was assessed through a standard test on the freshwater organism Daphnia magna. Independently of the synthesis procedure, the magnetic composites were successfully obtained. The Fe3O4 is nanometric (about 10 nm) and the weight percentage is sample-dependent. It decorates the HNT's surface and also forms aggregates linking the nanotubes in Fe3O4-rich samples. Thermodynamic and kinetic experiments showed different adsorption capacities of OFL, ranging from 23 to 45 mg g−1. The kinetic process occurred within a few minutes, independently of the composite. The capability of the three HNT/Fe3O4 in removing the OFL was confirmed under realistic conditions, when OFL was added to tap, river, and effluent waters at µg L−1 concentration. No acute toxicity of the composites was observed on freshwater organisms. Despite the good results obtained for all the composites, the sample by co-precipitation is the most performant as it: (i) is easily magnetically separated from the media after the use; (ii) does not undergo any degradation after three adsorption cycles; (iii) is synthetized through a low-cost procedure. These features make this material an excellent candidate for removal of OFL from water. [ABSTRACT FROM AUTHOR]

FeNb11O29 is an intriguing and promising material that has been emerging in the last few years. It is isostructural with Nb12O29, one of the rare compounds in which Nb displays a local magnetic moment and shows both antiferromagnetic ordering and metallic conductivity at low temperatures. Both the two polymorphic monoclinic and orthorhombic forms have a mono-dimensional magnetic arrangement, but the different disposition of the structural building blocks leads to a strong frustration phenomenon of the magnetic order in the high-temperature orthorhombic form. Whereas Nb12O29 has been widely studied, barely few magnetic data can be found on its analogous FeNb11O29, for which a role of the Fe3+ localized d electrons in affecting the original magnetic behaviour can be foreseen. In this paper, we report how we synthesized undoped and, for the first time, Mn- and V-doped FeNb11O29. Both the monoclinic and orthorhombic polymorphs, stable in different temperature ranges, were then thoroughly structurally characterized. With the help of micro-Raman spectroscopy, we investigated the differences introduced into the vibrational levels by doping, while EPR data allowed us to obtain information on the transition metal ions and to point out the related peculiar structural features. Static magnetization measurements evidenced the paramagnetic character of the compounds and the high-spin configuration of Fe3+ ions. [ABSTRACT FROM AUTHOR]

The experiments performed are presented where Ga-doped Li-Mn-spinels were investigated to verify the lattice capability to allocate the Ga(super 3+) ions on both tetrahedral and octahedral sites and to determine the lowest amount of dopant that prevents the occurrence of Jahn-Teller (J-T) transition. The results show that the electronic and magnetic features of the spinel framework are strongly dependent on substitution of the cationic sublattice.

Spinel ferrites are an amazing class of materials that can find application in different fields, from sensors and lithium-ion batteries to the intriguing biomedical field. For the use as anode in lithium-ion batteries, ZnFe2O4 is rather competitive due to low price, abundance, environmental benignity, working voltage of ~1.5 V, and, most importantly, a high theoretical specific capacity (~1072 mA h g−1). For its practical application, however, some issues must be overcome, in particular its fast capacity fading and poor rate capability resulting from an inherent low electronic conductivity. Possible strategies are represented by ferrite carbon coating/embedding, peculiar synthesis routes, and doping. In this frame, we synthesized Ca- and Al-doped ZnFe2O4 nanoparticles by using microwave-assisted combustion synthesis, followed by a classical carbon coating (determined as about 5 wt% by thermogravimetry). A good solubility of Ca and Al up to 25 atom% on both Zn and Fe sites was obtained. Cyclic voltammetries evidenced redox reactions involving Zn and Fe ions, but also the Al intervention could be supposed. Galvanostatic charge-discharge cycles proved that particularly Al ions were useful to improve the anode structural stability at high C rate (up to 3C), thanks to the stronger Al-O bonds with respect to Fe-O ones. A further improvement of capacities comes from the use of sodium alginate as binder to substitute polyvinylidene fluoride in the anode preparation. [ABSTRACT FROM AUTHOR]