Search

To endow an implant surface with enhanced properties to ensure an appropriate seal with the host tissue for inflammation/infection resistance, next-generation bone implant collagen–polyphenol nanolayers were built on conventional titanium surfaces through a multilayer approach. X-ray Photoelectron Spectroscopy (XPS) analysis was performed to investigate the chemical arrangement of molecules within the surface layer and to provide an estimate of their thickness. A short-term (2 and 4 weeks) in vivo test of bone implants in a healthy rabbit model was performed to check possible side effects of the soft surface layer on early phases of osteointegration, leading to secondary stability. Results show the building up of the different nanolayers on top of titanium, resulting in a final composite collagen–polyphenol surface and a layer thickness of about 10 nm. In vivo tests performed on machined and state-of-the-art microrough titanium implants do not show significant differences between coated and uncoated samples, as the surface microroughness remains the main driver of bone-to-implant contact. These results confirm that the surface nanolayer does not interfere with the onset and progression of implant osteointegration and prompt the green light for specific investigations of the potential merits of this bioactive coating as an enhancer of the device/tissue seal. [ABSTRACT FROM AUTHOR]

An injectable delivery platform for promoting delayed bone healing has been developed by combining a thermosensitive polyurethane-based hydrogel with strontium-substituted mesoporous bioactive glasses (MBG_Sr) for the long-term and localized co-delivery of pro-osteogenic Sr2+ ions and an osteogenesis-enhancing molecule, N-Acetylcysteine (NAC). The incorporation of MBG_Sr microparticles, with a final concentration of 20 mg/mL, did not alter the overall properties of the thermosensitive hydrogel, in terms of sol-to-gel transition at a physiological-like temperature, gelation time, injectability and stability in aqueous environment at 37 °C. In particular, the hydrogel formulations (15% w/v polymer concentration) showed fast gelation in physiological conditions (1 mL underwent complete sol-to-gel transition within 3–5 min at 37 °C) and injectability in a wide range of temperatures (5–37 °C) through different needles (inner diameter in the range 0.4–1.6 mm). In addition, the MBG_Sr embedded into the hydrogel retained their full biocompatibility, and the released concentration of Sr2+ ions were effective in promoting the overexpression of pro-osteogenic genes from SAOS2 osteoblast-like cells. Finally, when incorporated into the hydrogel, the MBG_Sr loaded with NAC maintained their release properties, showing a sustained ion/drug co-delivery along 7 days, at variance with the MBG particles as such, showing a strong burst release in the first hours of soaking. [ABSTRACT FROM AUTHOR]

This case report provided a unique opportunity to investigate the extent of microbiota infiltration on the oxidized implant surface that has been compromised by peri-implantitis. Scanning electron microscopic analysis confirmed the etiologic role of the bacteria on the loss of supporting structure and the difficulty in complete removal of bacterial infiltration on the implant surface. This case report emphasizes the need to perform definitive surface decontamination on failing dental implants prior to a regeneration procedure. [ABSTRACT FROM AUTHOR]

Purpose: This study was conducted to analyze how a cleaning treatment using plasma of argon would affect fibroblast growth on titanium disks at different time points to determine whether this treatment could enhance soft tissue healing around titanium dental implant abutments. Materials and Methods: Sixty sterile disks made of machined grade 5 titanium were divided into two groups; 30 disks were left untreated (control) and 30 were cleaned using plasma of argon (test). To simulate clinical conditions during soft tissue healing around titanium abutments, both groups were immersed in a culture of murine fibroblasts (L929) for 2, 8, or 48 hours. After preparation, they were stained using 4',6-diamidino-2-phenylindole dihydrochloride (DAPI) to label the cellular nuclei and fluorescent phalloidin to label the cellular bodies. The nuclei were counted, and cellular bodies were analyzed with fluorescent microscopy and imaging analysis software. Analysis was performed at the three different time points. Results: Fibroblast adhesion for the test group was statistically significantly greater versus the control group at 2 and 8 hours but not at 48 hours. At 2 and 8 hours, the cellular bodies in the test group appeared flatter and more spread out, revealing more advanced cellular adhesion, compared to the cells observed in the control group. At 48 hours, the test and control specimens were nearly indistinguishable. Conclusion: The removal of organic and inorganic contaminants from the surfaces of titanium disks using plasma of argon accelerated fibroblast adhesion in the early stages of colonization (2 to 8 hours). This effect disappeared after 48 hours as a result of saturation. Clinically, abutment cleaning using plasma of argon might positively affect soft tissue healing in early stages. [ABSTRACT FROM AUTHOR]

Mesoporous bioactive glass nanoparticles (MBG) are multifunctional building blocks for tissue regeneration and nanomedicine applications. Incorporation of biologically active ions can endow MBG with additional functionalities toward promoted therapeutic effects. Here, boron is incorporated into MBG by using a sol–gel approach. The concentration of boron incorporated is controllable by tuning the amount of boron precursor. Two types of boron‐doped MBG, namely 10B‐ and 15B‐MBG (5.8 and 6.5 mol% of B2O3, respectively) are synthesized. Boron incorporation does not significantly influence the particle morphology. All synthesized particles exhibit a sphere‐like shape with a size ranging from 100 to 300 nm. 10B‐ and 15B‐MBG show large specific surface area (346 and 320 m² g−1, respectively) and pore volume. Both boron‐doped MBG exhibit remarkable in vitro bioactivity and noncytotoxicity. Boron incorporation is shown to reduce the inflammatory response linked to macrophages as indicated by downregulated expression of pro‐inflammatory genes. However, boron incorporation delays the osteogenic differentiation in osteoblasts as indicated by the downregulated expression of pro‐osteogenic genes. The results demonstrate the promising potential of using boron‐doped MBG to modulate inflammatory response for bone regeneration under inflammatory conditions, as shown in this study for the first time. [ABSTRACT FROM AUTHOR]

Purpose: The aim of this study was to evaluate the surface chemistry and the microhardness at the implant-bone interface using a recently developed collagen-coated titanium implant in a short-term rabbit model. Materials and Methods: Surface chemistry was evaluated by x-ray photoelectron spectroscopy (XPS), while in vivo studies involved 4-week implants mid-diaphysis in the lateral femurs of adult male rabbits. After conventional embedding and evaluation of histologic sections, the resinembedded blocks containing the implanted screws were used to measure bone hardness by means of an indentation test. Results: Decomposition of the C1s peak obtained by XPS analysis confirmed that surface-immobilized collagen retained all the molecular features of the control, nonimmobilized reference. As to microhardness measurement, newly formed bone at the collagen-coated-implant/bone interface was significantly harder than bone at the interface of the uncoated control implant and bone. Discussion: These results suggested that collagen coating significantly improves bone maturation and mineralization at the interface in comparison with uncoated commercially pure titanium. Surface modification of titanium implants by collagen coating has recently been discussed as a promising approach to the biochemical modification of implant surfaces. The present results support previous histologic findings and demonstrated that the biomolecular layer linked over the titanium implant can increase the bone healing rate, at least in this animal model. Conclusions: The present microhardness measurement at the bone-implant interface showed that collagen coating can significantly improve bone maturation and mineralization at the interface in comparison with uncoated commercially pure titanium, confirming and substantiating previous findings by histomorphometric measurements from the same model. [ABSTRACT FROM AUTHOR]

Purpose: To analyze the surface composition of 34 different commercially available titanium dental implants. Materials and Methods: Surface composition was evaluated by x-ray photoelectron spectroscopy (XPS). Samples were divided into 4 groups, depending on their surface topography (machined, sandblasted, acid etched, or plasma sprayed). Results: Statistical analysis of the data showed a clear relationship between surface composition and topography, which can be easily accounted for by the chemical effects of the surface treatment performed. On average, acid-etched and plasma-sprayed surfaces had higher titanium and lower carbon concentration than machined surfaces. Discussion and Conclusion: Current studies aimed at the evaluation of implants with different topography should not implicitly assume that topography is the only variable controlling the biologic response. Rather, when comparing different topographies, it should be taken into account that surface chemistry may be a variable as well. [ABSTRACT FROM AUTHOR]

Purpose: To determine, in vitro, cytotoxicity and cell adhesion on 3 different implant surfaces. Materials and Methods: All samples had machined surfaces, but they were subjected to different cleaning procedures, which produced 3 different surface chemistries. One of the samples was "as-produced" from the machining tools. The other samples were subjected to partial and total cleaning routines. Cytotoxicity was evaluated using mouse fibroblast cultures, and cell adhesion was evaluated with osteoblast-like SaOS-2 cells. Results: The "as-produced" sample showed a pronounced surface contamination by lubricating oils. For partially and totally cleaned samples, an increasing amount of titanium and a decreasing carbon/titanium ratio was observed as cleaning became more complete. Discussion: Differences in surface chemistry such as those normally found on titanium implant surfaces (see part 1 of this series) can lead to those same effects which, in in vitro experiments, are normally accounted for in terms of surface topography alone. Conclusion: Effects related to surface chemistry can operate over and above surface topography, making it impossible, without proper characterization, to make definite statements about the role of topography alone. [ABSTRACT FROM AUTHOR]

The goal of the present work was to investigate the relationship between in vivo healing and inflammatory response and in vitro cytokine expression by macrophages of a synthetic bone filler (25% hydroxylapatite-75% β-tricalcium phosphate) bearing a surface nanolayer of collagen. A clinically accepted, state-of-the-art xenograft material was used as a “negative control,” that is, as a material that provides the correct clinical response for the intended use. In vitro data show that both materials exert a very low stimulation of proinflammatory cytokines by macrophages, and this was confirmed by the very mild inflammatory response detected in in vivo tests of local response in a rabbit model. Also, in vitro findings suggest a different mechanism of healing for the test and the control material, with a higher regenerative activity for the synthetic, resorbable filler, as confirmed by in vivo observation and literature reports. Thus, the simple in vitro model adopted provides a reasonable forecast of in vivo results, suggesting that new product development can be guided by in vitro tuning of cell-materials interactions. [ABSTRACT FROM AUTHOR]