The aim of this study was to report the clinical case of an 8-year-old male patient seen at the Pediatric Dentistry outpatient clinic at the Universidade Federal do Paraná, Brazil, diagnosed with molar-incisor hypomineralization (MIH) after presenting with pain in teeth 16, 36, and 46, which had extensive atypical cavities and opacities on the adjacent enamel. A diagnostic wax-up of affected teeth was performed for manufacture of silicone occlusal matrix. Encapsulated high-viscosity glass ionomer cement was handled and inserted into the occlusal matrix which was fitted onto the teeth by slight finger pressure. After setting time, excess of material was removed, and occlusion was checked. A flowable resin coating material was applied, and the restorations were finished. Six months later, the restorations performed for treatment of the severe MIH lesions proved to be efficient, lowering the sensitivity reported by the patient, reshaping the teeth, improving their function, and refining dental esthetics. RESUMO O objetivo deste estudo foi relatar um caso clínico de um paciente com diagnóstico de Hipomineralização de Molares e Incisivos (HMI). Paciente do sexo masculino, de 8 anos de idade, compareceu à clínica de Odontopediatria da Universidade Federal do Paraná com queixa de dor nos dentes 16, 36 e 46 - os quais apresentavam extensas cavitações atípicas com opacidades no esmalte adjacente. O enceramento diagnóstico dos dentes afetados foi realizado para a confecção das matrizes oclusais de silicone. Cimento ionômero de vidro de alta viscosidade encapsulado foi manipulado e inserido na matriz oclusal, a qual foi encaixada sobre os dentes, exercendo-se leve pressão digital. Após a presa do material os excessos foram removidos e a oclusão foi checada. Aplicou-se uma camada de resina fluída de cobertura e as restaurações foram finalizadas. Após seis meses, as restaurações realizadas para tratar as lesões severas de HMI mostraram-se eficazes, reduzindo a sensibilidade relatada pelo paciente, além de reestabelecerem a anatomia, função e estética dentária.

O cimento de ionômero de vidro (CIV) é amplamente utilizado por suas propriedades clínicas satisfatórias e o sucesso clínico é grandemente atribuído a sua capacidade de liberação de flúor. É classificado de acordo com a composição química em: cimentos convencionais, cimentos anidros, cimentos reforçados com partículas metálicas, cimentos modificados por monômeros resinosos ou cimentos de alta viscosidade; sendo este último, uma excelente escolha em restaurações pela técnica restauradora atraumática. Devido às suas boas propriedades, e, em especial, o seu potencial anticariogênico, bacteriostático e remineralizador, o CIV é o material restaurador de escolha para os dentes decíduos, pois além de diminuir/estacionar o avanço da cárie, promove a recuperação dos tecidos lesionados e diminui a chance de recidiva da cárie (cárie secundária). Na utilização desse composto, as particularidades dos CIV’s devem ser respeitadas afim de garantir um tratamento efetivo, tendo como base protocolos clínicos corretos e efetivos. O objetivo desse trabalho é revisar a literatura científica no que se refere ao ionômero de vidro, com a finalidade de adquirir conhecimento técnico e científico para conhecer suas propriedades e aplicações clínicas.

Objective: evaluate the effect of a surface coating agents on the sorption and glass ionomer cements solubility. Materials and Methods: Four materials were selected: Encapsulated resin-modified ionomer (Riva Light Cure); Powder/liquid Encapsulated resin-modified (Vitremer); Encapsulated conventional (Equia Forte) and powder/ liquid conventional (Fuji IX). Twenty samples of each were made, half with surface protection of Equia Forte Coat. The samples were kept in an oven for 5 days. These were then weighed at 24-hour intervals. The thickness and diameter were measured using a digital caliper to calculate their volume. New weightings were performed to obtain the intermediate mass. Then, the samples were kept at rest for 5 days and weighed again. Results: The sorption and solubility data obtained were subjected to analysis of variance (two-way ANOVA, material and surface coating agents) and Tukey test ( =0.05). For sorption, there was a significant difference only for the material factor (p Equia Forte > Riva Light Cure > Fuji IX. The Fuji IX ionomer showed the lowest sorption values, differing significantly from the othermaterials, regardless of the use of surface coating agents. There was no significant difference for the surface protection factor (p>0.05). For solubility there was no significant difference for the material factor, surface coating agents or material*surface coating agent interaction. Conclusion: The use of surface coating agents did not influence the sorption and solubility values of the evaluated ionomersand the conventional Fuji IX ionomer showed lower sorption rates. Objetivo: Avaliar o efeito de um protetor de superfície na sorção e solubilidade de cimentos de ionômero de vidro. Materiais e Métodos: Quatro materiais foram selecionados: ionômero modificado por resina encapsulado (Riva Light Cure);modificado por resina pó/líquido (Vitremer); convencional encapsulado (Equia Forte) e convencional pó/líquido (Fuji IX). Foram confeccionados 20 espécimes de cada, sendo metade com proteção superficial do Equia Forte Coat. As amostras foram mantidas em estufa a 37°C em repouso por 5 dias. Em seguida, esses foram pesados em intervalos de 24 horas. A espessura e o diâmetro foram medidos com um paquímetro digital para o cálculo do volume. Novas pesagens foramrealizadas para a obtenção da massa intermediária. Em seguida, as amostras foram mantidas em repouso por 5 dias a 37°C e realizada nova pesagem. Resultados: Os dados obtidos de sorção e solubilidade foram submetidos à análise de variância (ANOVA dois fatores, material e protetor de superfície) e teste Tukey( =0,05). Para sorção, houve diferença significativa apenas para o fator material (p Equia Forte > Riva Light Cure > Fuji IX. O ionômero Fuji IX apresentou os menores valores de sorção, diferindo significativamente dos demais materiais, independentemente do uso do protetor superficial. Não houve diferença significativa para o fator proteção de superfície (p>0,05). Para solubilidade não houve diferença significativa no fator material, protetor de superfície ou interação material*protetor. Conclusão: O uso do protetor superficial não influenciou nos valores de sorção e solubilidade dos ionômeros avaliados e o ionômeroconvencional Fuji IX apresentou menores taxas de sorção.

Purpose: To determine the effect of glass ionomer sealants in preventing occlusal caries on erupting primary molars. Materials and Methods: A longitudinal clinical trial with children 1-3 years old was held in the city of São Luiz do Paraitinga - SP, participants of the "First Smile Project". The experimental design was a split-mouth for 62 healthy primary molars (1º and 2º molars), 31 on control group (C) and 31 on sealant group (S). Supervised toothbrushing was oriented with dentifrice "Oral-B Pro Saúde” (above 1000 ppm Fluoride), prophylaxis and diagnosis by ICDAS. Teeth on (S) group were sealed with glass ionomer. Revaluations for both groups were held after 3, 6, 12 and 18 months (T1, T2, T3 and T4) respectively by ICDAS and ICDAS CARS. The Chi-square test and Cox Regression analysis was used. Results: The results for progression or not of carious lesions (%), respectively, were Group C - T1, 46.8% and 53.2%; T2, 47.2% and 52.8%; T3, 48.5% and 51.5%; T4, 47.8% and 52.2%. Group S - T1, 66.7% and 33.3%; T2, 56.2% and 43.8%; T3, 52.6% and 47.4%; T4, 52.9% and 47.1%. Conclusion: There was no difference between groups on follow-up periods and there was no difference between variables to children and the teeth (p = 0.5), suggesting that the ionomer sealing presented the same preventive effect of the control group. Objetivo: Verificar el efecto de los selladores ionoméricos en la prevención de caries oclusal en molares temporales en erupción. Materiales y métodos: Se realizó un estudio clínico longitudinal con niños de 1 a 3 años, en la ciudad de São Luiz do Paraitinga - SP, participantes del “Projeto Primeiro Sorriso”. El diseño experimental fue de boca dividida para 62 molares temporales sanos (1er y 2do molar), 31 en el grupo control (C) y 31 en el grupo sellador (S). Para ambos grupos se orientó el cepillado supervisado con dentífrico fluorado Oral-B Pro Saúde (1100 ppm de fluoruro), la profilaxis y el diagnóstico a través de ICDAS. Los dientes del grupo S se sellaron con cemento de ionómero de vidrio. Se realizaron reevaluaciones para los dos grupos después de 3, 6, 12 y 18 meses (T1, T2, T3 y T4) respectivamente, utilizando ICDAS e ICDAS CARS. Se realizó la prueba de chi-cuadrado y regresión de Cox con fragilidad compartida. Resultados: Los resultados para la progresión o no de la lesión de caries (%), respectivamente, fueron: Grupo C - T1, 46,8% y 53,2%; T2, 47,2% y 52,8%; T3, 48,5% y 51,5%; T4, 47,8% y 52,2%. Grupo S - T1, 66,7% y 33,3%; T2, 56,2% y 43,8%; T3, 52,6% y 47,4%; T4, 52,9% y 47,1%. Conclusión: No hubo diferencia entre los grupos en los tiempos de seguimiento y las variables relacionadas con los niños y los dientes, lo que sugiere que el sellado ionomérico tuvo el mismo efecto preventivo que el grupo control. Objetivo: Verificar o efeito de selantes ionoméricos na prevenção da cárie oclusal em molares decíduos em irrupção. Materiais e métodos: Foi realizado um estudo clínico longitudinal com crianças de 1 a 3 anos, na cidade de São Luiz do Paraitinga – SP, participantes do “Projeto Primeiro Sorriso”. O delineamento experimental foi de boca dividida para 62 molares decíduos hígidos (1º e 2º molares), 31 no grupo controle (C) e 31 no grupo selante (S). Para ambos os grupos foi orientada escovação supervisionada com dentifrício fluoretado Oral-B Pro Saúde (1100 ppm Flúor), profilaxia e diagnóstico por meio do ICDAS. Os dentes do grupo S foram selados com cimento de ionômero de vidro. As reavaliações para os dois grupos foram feitas após 3, 6, 12 e 18 meses (T1, T2, T3 e T4) respectivamente, por meio de ICDAS e ICDAS CARS. Realizou-se o teste qui-quadrado e regressão de Cox com fragilidade compartilhada. Resultados: Os resultados para progressão ou não de lesão cárie (%), respectivamente, foram: Grupo C - T1, 46,8% e 53,2%; T2, 47,2% e 52,8%; T3, 48,5% e 51,5%; T4, 47,8% e 52,2%. Grupo S - T1, 66,7% e 33,3%; T2, 56,2% e 43,8%; T3, 52,6% e 47,4%; T4, 52,9% e 47,1%. Conclusão: Não houve diferença entre grupos nos tempos de acompanhamento e as variáveis relacionadas às crianças e aos dentes, sugerindo que o selamento ionomérico apresentou o mesmo efeito preventivo que o grupo controle.

Introduction Some experimental models have been used to evaluate the use of biomaterials in bone regeneration. Among them are the critical size defects (CSD) created in rat calvaria. An experimental model has been described in the literature, in which “L” markings are performed on the margins of the bone defects in order to assist in the precise identification of these defects during laboratory processing and analysis of the results. In the proposed model, the “L” markings are filled with amalgam. Objective The purpose of the present study was to evaluate the amalgam replacement of an experimental bony defect model in rat calvaria by heated or unheated glass ionomer. Material and method 24 rats were used. A 5 mm CSD was created at each animal calvaria. Two “L” shaped markings were made 2 mm from the margins of the bone defect, filled with amalgam (Group AM), heated glass ionomer cement (Group GIh) or not (Group GI). The animals were euthanized 15 days postoperatively. The areas of the surgical defect and the L-shaped marking were histomorphometrically analyzed and the data were analyzed statistically (p

Objective: To assess the superficial microhardness of enamel-restorations margins of glass ionomer cement reinforced with silver (RS), modified with resin (RI) and composite resin (CO) after cariogenic biofilm. Materials and Methods: Thirty bovine enamel blocks with standard cavities were divided into three groupsaccording to the materials used: RI (Riva Light Cure™, SDI), RS (Riva Silver™, SDI) and CO (Filtek™ Z350 XT, 3M). Half of each enamel block surface was covered by acid resistant varnish. After that, the blocks were exposed to Streptococcus mutans biofilm. The varnish was removed from the blocks and superficial microhardness (MDS) was measured (Knoop, 50 g, 15 s), with five indentations, 100 ?m from each other in three different directions. The data were analyzed by the Shapiro Wilk, Kruskal Wallis and Mann Whitney tests (p

Devido à necessidade de encontrar-se um ionômero de vidro suficientemente radiopaco, para facilitar um futuro diagnóstico radiográfìco, este trabalho propõe-se a testar nove marcas comerciais de ionômeros (Chelon Fill, Chelon Silver, Fuji II LC, Variglass Azul, Variglass DY Vidrion P, Vitrebond, Vitremer Cimentação e Vitremer Restauração) para identificar qual apresenta maior radiopacidade. Para isso foram confeccionados corpos de prova, um de cada ionômero de vidro, e restaurados nove dentes pré-molares, nas regiões apical e oclusal e então radiografados. As radiografias dos corpos de prova foram submetidas a uma avaliação densitométrica e as dos dentes foram avaliadas por dez observadores. De acordo com as duas avaliações (densitométrica e visual) o Chelon Silver é o ionômero mais radiopaco, seguido do Variglass DY. O menos radiopaco é o Chelon Filll., The purpose study was to test nine commercial brands of glass ionomer (Chelor Fill, Chelon Silver, Fuji II LC, Variglass Azul Variglass DY, Vitrebond, Vitremer Cimentaçãc e Vitremer Restauração) in order to identify one that is most radiopaque. This informatior would help in a future radiographic diagnosis o: analysis. In carrying out this experiment, nine glas ionomer samples were made from the nine brands mentioned above, and the oclusal anc apical regions of nine premolars teeth wert restored. Later, the samples as well as the restoœc premolars wcre submited to radiographi¿ exposure. The subjects went through densitometric evaluation, and the premola5 were visually evaluated by ten observers. In both densitometric and visua. evaluation, the results showed Chelon Silver as the most radiopaque of the glass ionome: followcd by Variglass DY. The least radiopaqut was Chelon Fili.

Submitted by Diego Felipe Mardegan Gonçalves (mardegan.goncalves@unesp.br) on 2021-10-06T02:06:40Z No. of bitstreams: 1 Dissertação DFMG.pdf: 1300220 bytes, checksum: 8612b116b31a67db76e5f22872dac3a2 (MD5) Approved for entry into archive by Claudio Hideo Matsumoto null (claudio@foa.unesp.br) on 2021-10-06T13:14:20Z (GMT) No. of bitstreams: 1 gonçalves_dfm_me_araca_int.pdf: 1300220 bytes, checksum: 8612b116b31a67db76e5f22872dac3a2 (MD5) Made available in DSpace on 2021-10-06T13:14:21Z (GMT). No. of bitstreams: 1 gonçalves_dfm_me_araca_int.pdf: 1300220 bytes, checksum: 8612b116b31a67db76e5f22872dac3a2 (MD5) Previous issue date: 2021-07-08 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) O objetivo do presente estudo foi avaliar a influência de diferentes dentifrícios na dureza de superfície, em secção transversal e perfil de desgaste do esmalte, assim como na resistência de união de cimentos de ionômero de vidro de alta viscosidade (CIV-AV) à dentina, após indução de cárie artificial, ciclagem de pH e escovação. Foram utilizados 80 dentes bovinos, divididos em blocos de esmalte e dentina. Os espécimes de esmalte foram polidos e selecionados de acordo com a microdureza. Em seguida, metade de cada bloco de esmalte foi protegida com verniz ácido resistente. Os espécimes de dentina foram incluídos em resina acrílica e planificados. O protocolo de cárie artificial foi feito através de ciclos de desmineralização em esmalte (n=20) e pela imersão da dentina (n=40) em solução desmineralizadora. Vinte amostras de dentina não foram submetidas à cárie, sendo o grupo controle. Todas as amostras foram submetidas à ciclagem de pH e escovação durante 7 dias de acordo com cada dentifrício: Colgate Total 12 1450 ppm F (CT) e Clinpro 5000 ppm F + TCP (CL). Em seguida, os blocos de esmalte foram submetidos às análises de dureza de superfície, em secção transversal e perfilometria. Microscopia eletrônica de varredura foi realizada em três blocos representativos de cada grupo. Os espécimes de dentina foram subdivididos de acordo com material restaurador: CIV-AV Ketac Molar (KM) e cimento ionomérico híbrido Equia Forte (EF). Em seguida, as amostras foram armazenadas sob umidade relativa durante 24 horas e preparados para o teste de microcisalhamento. Os dados obtidos foram submetidos ao teste de normalidade, análise de variância (ANOVA) 1 critério para avaliar a recuperação mineral e perfil de desgaste, ANOVA 2 critérios com medidas repetidas para avaliar a dureza de superfície e em secção transversal, ANOVA 3 critérios para avaliar o microcisalhamento e pós teste de Tukey para comparações múltiplas, com significância de 5%. Observou-se recuperação parcial da dureza de superfície, independente do dentifrício. Os dados da dureza em secção transversal evidenciaram que CL obteve valores inferiores a CT até 90 micrômetros (m) no lado teste. O dentifrício CT apresentou maior desgaste quando comparado à CL. Em dentina, ao comparar os dentifrícios dentro de cada CIV, CT apresentou maior resistência adesiva para ambos os materiais. A comparação entre CIVs dentro do mesmo dentifrício evidenciou resistência adesiva superior para KM quando comparado à EF na dentina tratada com CL. Conclui-se que o dentifrício com maior concentração de flúor promoveu menor dureza em secção transversal no esmalte e o dentifrício convencional resultou em maior desgaste superficial. Na superfície dentinária, o dentifrício com maior concentração de flúor diminuiu a resistência adesiva de cimentos de ionômero de vidro. The aim of the present study was to evaluate the influence of different dentifrices on surface hardness and cross-sectional hardness, wear profile on enamel, as well as on the bond strength of high viscosity glass ionomer cements (HV-GIC) to dentin, after to produce artificial caries, pH cycling and brushing. Eighty bovine teeth were used, divided into enamel and dentin blocks. The enamel specimens were polished and selected according to microhardness. Then, half of each enamel block was covered with resistant acid varnish. Dentin specimens were embedded in acrylic resin and flattened. The artificial caries protocol was carried out through enamel demineralization cycles (n= 20), and the dentin (n= 40) was immersed in demineralizing solution. Twenty dentin specimens were not subjected to artificial caries, being the control group. All blocks were subjected to pH cycling and brushing for 7 days according to each dentifrice: Colgate Total 12 1450 ppm F (CT) and Clinpro 5000 ppm F + TCP (CL). Then, the protected enamel surfaces were exposed for the analysis of surface hardness, cross sectional hardness and profilometry. Scanning electron microscopy was performed in three representative blocks of each group. The dentin specimens were subdivided according to restorative material: HV-GIC Ketac Molar (KM), and hybrid GIC Equia Forte (EF). Then, the specimens were stored under relative humidity for 24 hours and prepared for the micro-shear test. The data were submitted to normality test, one-way analysis of variance (ANOVA) to assess mineral recovery and wear, two-way repeated measures ANOVA to assess surface and cross-sectional hardness, and three-way ANOVA to analyze the bond strength. Tukey post-test was used for multiple comparisons, with a significance level of 5%. It was observed a partial recovery of superficial microhardness, regardless of the dentifrice. Cross sectional hardness data showed that CL obtained values below CT up to 90 micrometers (m) on the test side. CT dentifrice presented greater wear when compared to CL. In dentin, when the dentifrices were compared within each GIC, CT showed greater adhesive resistance for both materials. A comparison between GICs within the same dentifrice showed superior adhesive resistance for KM when compared to EF in dentin treated with CL. It was concluded that the dentifrice with the highest fluoride concentration promoted less cross-sectional hardness in the enamel and the conventional dentifrice resulted in greater surface wear. On the dentin, the dentifrice with the highest fluoride concentration decreased the adhesive strength of glass ionomer cements. CAPES: 001 FAPESP: 19/13326-8

Objective: This study aimed to evaluate surface dye penetration of two conventional glass ionomer cements (GIC), one of them a high viscous ionomer. Methods: 20 standard disk samples measuring 2 mm thick and 4 mm in diameter were made for each conventional GIC. The high viscous ionomer was used as the control (Group 1). Samples were embedded in wax and submitted to pH cycling for 7 days simulating a high cariogenic challenge in a kiln (37ºC). All samples were brushed with an extra-soft bristles infant toothbrush to mimic oral hygiene after exposure to a demineralizing solution for 6 hours. The samples were immersed in a 1% methylene blue solution for 2 hours at the end of cycling. The Mann-Whitney Rank Sum Test was used to analyze the difference between the two GIC. Results: All samples disclosed a superficial dye penetration of 0.6 to 1.5 mm depth. There was no statistical d ifference b etween t he G IC t ested ( p = 0.883). Conclusion: Both GIC tested in this study exhibited superficial dye penetration to depths of at least until their superficial third. Objetivo: Este estudo in vitro objetivou avaliar a infiltração superficial de dois cimentos de ionômero de vidro (CIV) convencionais, sendo um de alta viscosidade. Método: 20 amostras de discos padronizados de CIV, com 2 mm de espessura e 4 mm de diâmetro, foram feitos para cada grupo. O CIV de alta viscosidade foi utilizado como controle (Grupo 1). Esses corpos de prova foram embutidos em blocos de cera e submetidos à ciclagem de pH por 7 dias, a fim de simular um alto desafio cariogênico em estufa à 37º C. Todas as amostras foram escovadas com uma escova de dentes infantil de cerdas extra macias para reproduzir a higiene bucal após a exposição por 6 horas a solução desmineralizante. Ao final do processo de ciclagem de pH os corpos de prova foram submersos em azul de metileno à 1% por 2 horas. O teste estatístico Mann-Whitney foi usado para avaliar a diferença entre os dois CIV. Resultados: Todas as amostras tiveram mais de 0,5 mm de infiltração superficial. Não ocorreu diferença estatística significante entre os CIV testados (p = 0,883). Conclusão: Ambos CIV testados no presente estudo apresentaram infiltração superficial de corante na profundidade de até pelo menos um terço a partir da sua superfície.

Orientador: Regina Maria Puppin-Rontani Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba Resumo: A interação direta entre restauração e biofilme dentário está presente constantemente na cavidade bucal e suas conseqüências relacionam-se tanto com as características físicas e químicas do material quanto com a virulência da bactéria aderida. O objetivo deste estudo foi avaliar diferentes cimentos ionoméricos restauradores submetidos, in vitro, à biodegradação por biofilme de Streptococcus mutans e à abrasão por escovação. Cada material selecionado (Ketac N100, Vitremer, Ketac Molar Easymix e Fuji IX) foi utilizado na forma recém-manipulada ou na forma de discos, confeccionados sob condições assépticas. Enquanto o material pré-presa foi inserido em poços para o teste de difusão em ágar e análise dos halos de inibição de crescimento do S. mutans UA159 (n=8), os discos foram distribuídos em diferentes testes: a) teste de aderência desta cepa em 2 horas aos materiais, com a contagem das unidades formadoras de colônias (n=10); b) testes relacionados ao acúmulo bacteriano por sete dias (n=10) - peso úmido do biofilme, pH do meio de cultura a cada 48 horas (renovação do meio) e flúor liberado neste mesmo meio. Após os sete dias de biodegradação, os discos foram lavados e avaliados quanto à rugosidade e micro-morfologia de superfície. Como grupo controle, dez discos foram mantidos em umidade relativa pelo mesmo período para avaliação da superfície. A abrasão por escovação (degradação mecânica) foi realizada em seguida, e os espécimes foram reavaliados. Os dados obtidos nos testes de difusão, aderência e peso úmido do biofilme foram avaliados estatisticamente pelos testes de Kruskal-Wallis e Mann-Whitney, enquanto os dados de pH, flúor e rugosidade foram avaliados por ANOVA e Tukey (?=5%). Não houve diferença estatisticamente significante entre os materiais quanto à aderência inicial (p=0,6272) e peso final do biofilme (p=0,9612). Entretanto, Vitremer apresentou os maiores halos de inibição, valores de pH nas primeiras 48 horas superiores ao Ketac N100 e Fuji IX, e liberação de flúor superior ao Ketac N100 e Ketac Molar Easymix durante todo o período experimental. Ketac N100 apresentou maior halo de inibição que os materiais convencionais e menor liberação de flúor, com uma diminuição nos valores ao longo do tempo de aproximadamente doze vezes. Quanto à rugosidade, houve interação entre os três fatores: material, meio de armazenamento (umidade x biofilme) e abrasão (antes x depois). Vitremer foi o único material que não apresentou diferença entre os grupos de armazenamento, com similares valores de rugosidade, enquanto os outros materiais apresentaram maiores valores após a biodegradação. Quando a degradação foi cumulativa (biomecânica), Ketac N100 obteve os menores valores de rugosidade. Microscopicamente foi observado um aspecto corroído na matriz biodegradada e a exposição das partículas na superfície dos materiais após os seguidos desafios. Portanto, a incorporação da nanotecnologia ao nano-ionômero auxiliou na obtenção de resistência à degradação biomecânica superior aos outros materiais estudados. Entretanto, suas propriedades químicas anti-cariogênicas foram negativamente influenciadas e consideradas inferiores ao Vitremer Abstract: The direct interaction between restoration and dental biofilm frequently occurs in the oral cavity. Its consequences are related to physico-chemical characteristics of the restorative material and to virulence of the bacteria adhered. The aim of this study was to evaluate different restorative glass ionomer cements subjected to biodegradation by Streptococcus mutans biofilm and to brushing abrasion in vitro. Each material studied (Ketac N100, Vitremer, Ketac Molar Easymix e Fuji IX) was tested as recently handled mix or as set discs, prepared under aseptic conditions. At that condition, the material was inserted into wells for agar diffusion test and analysis of growth inhibition zones of S. mutans UA159 (n=8), while the discs were distributed in different tests: a) two-hours adherence test of this strain on those ionomeric materials, by counting the colony-forming units (n = 10); b) tests related to bacterial accumulation for seven days (n = 10) - biofilm wet weight, pH of growth medium every 48 hours (medium renewal) and fluoride released in that same medium. After seven days of biodegradation, the discs were washed and evaluated about surface roughness (Ra) and micromorphology. As control group, ten discs were kept in relative humidity for the same period. Then, toothbrush abrasion test (mechanical degradation) was performed, and specimens were reevaluated. Data from inhibition zones, S. mutans adherence and wet weight of biofilm were submitted to Kruskal-Wallis and Mann-Whitney tests. ANOVA and Tukey tests were applied to fluoride-released, pH and roughness data. The level of significance was set at 5%. There was no statistically significant difference among the materials regarding the initial adherence (p = 0.6272) and final biofilm weight (p = 0.9612). Vitremer showed the largest inhibitory zones, higher pH values than Ketac N100 and Fuji IX at the first exchange medium (48h), and higher fluoride release than Ketac N100 e Ketac Molar Easymix throughout the experimental period. Ketac N100 showed greater inhibitory zone than conventional ionomers and the lowest fluoride release, with a fall in values over time about twelve times. Concerning surface roughness, there was significant interaction among factors: material, storage (humidity/biofilm) and abrasion (before/after). Vitremer showed similar Ra values between storage groups, while other materials presented higher Ra values after biodegradation test. Concerning cumulative biomechanical challenge, Ketac N100 presented the lowest Ra values. The corroded aspect after biodegradation and the exposition of fillers after mechanical degradation were visualized at micrographs. Therefore, the nanotechnology incorporation in the nano-ionomer promoted better resistance to biomechanical degradation than other materials studied. However, its anticariogenic chemical properties were negatively influenced and considered inferior to Vitremer Doutorado Materiais Dentários Doutor em Materiais Dentários

Introduction: The sandwich technique is a procedure that combines the glass ionomer cement (GIC) with the composite resin (CR) in order to obtain the best physical-mechanical and aesthetic properties of each one. Objective: perform a literary review on the use of this method in direct restorations and analyze how the interaction between the two materials occurs. Methods: A search of the literature published between 2010 and 2021 was carried out in the databases PubMed/ Medline, SciELO, Lilacs and Google Scholar, using pre-selected descriptors. 40 studies were included that met the inclusion and exclusion criteria. Results: The association of GIC with CR brings to the direct restoration the benefits of pulp protection, anti-cariogenic effect, less polymerization contraction, greater retention and better aesthetic properties. This method can be classified as open, closed, mediate and immediate, these variations will depend, respectively, on the indication and the form of preparation of the procedure. Conclusion: When carrying out the acid conditioning of the surface of the conventional GIC, it is necessary to be cautious, since the differences in the setting reactions of this material and the CR can interfere with the final properties of the restoration. However, resin-modified glass ionomer cement does not require this procedure. Although some scholars do not suggest this type of pre-treatment, due to the possibility of promoting cracks and decreasing its strength, research claims that the mixed technique can be performed effectively when using both conventional and self-etching adhesive systems, as no were observed significant differences bond strength when comparing them. Introducción: La técnica sandwich es un procedimiento que combina el cemento de ionómero de vidrio (CIV) con la resina compuesta (RC) con el fin de obtener las mejores propiedades físico-mecánicas y estéticas de cada uno. Objetivo: realizar una revisión literaria sobre el uso de este método en restauraciones directas y analizar cómo se produce la interacción entre los dos materiales. Metodología: Se realizó una búsqueda de la literatura publicada entre 2010 y 2021 en las bases de datos PubMed / Medline, SciELO, Lilacs y Google Scholar, utilizando descriptores preseleccionados. Se incluyeron 40 estudios que cumplieron con los criterios de inclusión y exclusión. Resultados: la asociación de CIV con RC aporta a la restauración directa los beneficios de protección pulpar, efecto anticariógeno, menor contracción de polimerización, mayor retención y mejores propiedades estéticas. Este método se puede clasificar en abierto, cerrado, mediato e inmediato, estas variaciones dependerán, respectivamente, de la indicación y la forma de preparación del procedimiento. Conclusión: a la hora de realizar el acondicionamiento ácido de la superficie de la CIV convencional, es necesario tener precaución, ya que las diferencias en las reacciones de fraguado de este material y la CR pueden interferir con las propiedades finales de la restauración. Sin embargo, el cemento de ionómero de vidrio modificado con resina no requiere este procedimiento. Aunque algunos estudiosos no sugieren este tipo de pretratamiento, debido a la posibilidad de promover grietas y disminuir su resistencia, la investigación afirma que la técnica mixta se puede realizar de manera efectiva cuando se utilizan sistemas tanto convencionales como autograbantes, ya que no se encontraron diferencias significativas fuerza de unión observada al compararlos. Introdução: A técnica sanduíche é um procedimento que combina o cimento de ionômero de vidro (CIV) com a resina composta (RC) com a finalidade de obter as melhores propriedades físico-mecânicas e estéticas de cada um. Objetivo: realizar uma revisão literária sobre a utilização desse método nas restaurações diretas e analisar como ocorre a interação entre os dois materiais. Metodologia: Foi realizada uma busca da literatura publicada entre 2010 a 2021 nas bases de dados PubMed/Medline, SciELO, Lilacs e Google Acadêmico, através da utilização de descritores pré-selecionados. Foram incluídos 40 estudos que respeitaram os critérios de inclusão e exclusão. Resultados: a associação do CIV a RC traz à restauração direta os benefícios de proteção pulpar, efeito anticariogênico, menor contração de polimerização, maior retenção e melhores propriedades estéticas. Esse método pode ser classificado em aberto, fechado, mediato e imediato, essas variações vão depender, respectivamente, da indicação e da forma de confecção do procedimento. Conclusão: ao realizar o condicionamento ácido da superfície do CIV convencional é preciso ser cauteloso, pois as diferenças nas reações de presa desse material e da RC pode interferir nas propriedades finais da restauração. Já o cimento de ionômero de vidro modificado por resina dispensa esse procedimento. Apesar de alguns estudiosos não sugerirem esse tipo de pré-tratamento, pela possibilidade de promover rachaduras e diminuição da sua força, pesquisas afirmam que a técnica mista pode ser realizada com eficácia ao utilizar tanto sistemas adesivos convencionais como autocondicionantes, pois não foram observadas diferenças significativas na resistência de união ao compará-los.

The aim of this study was to evaluate the impact of different restorative techniques to treat deep caries lesions of primary molars on children’s self-reported discomfort. A randomized clinical trial with two parallel arms (1:1) was conducted in São Paulo, Brazil. 4-8 years-old children with at least one occlusal or occlusoproximal deep caries lesion in primary molars were selected. Molars were randomly allocated into two groups: (1) restoration performed with calcium hydroxide cement followed by high-viscosity Glass Ionomer Cement (CHC+HVGIC), and (2) HVGIC restoration. Immediately after the intervention, children reported the experienced discomfort during restoration to an external examiner using a Wong-Baker face-scale. Children’s self-reported discomfort was analyzed using Poisson regression comparing both groups and assessing other variables’ influence (α=5%). One hundred and eight children fulfilled the eligibility criteria and were randomized in the two groups (n=54). Most of the children who received CHC+HVGIC restorations reported none or minimal discomfort (83.3%). Similar scores (92.6%) were reported for those treated with HVGIC (p=0.758). The mean reported discomfort in children with CHC+HVGIC restorations was 0.37(1.01), and 0.41(1.01) for those with HVGIC restorations. Children’s self-reported discomfort was associated with age, sex, children’s cooperation, and intervention duration. We can conclude that CHC+HVGIC or HVGIC restorations result in none or minimal discomfort in the management of deep caries lesions, being considered a reliable option. El objetivo de este estudio fue evaluar el impacto de diferentes técnicas restauradoras para el tratamiento de lesiones cariosas profundas en molares primarios sobre las molestias reportadas por los niños. Se realizó un ensayo clínico aleatorizado con dos brazos paralelos (1: 1) en São Paulo, Brasil. Se seleccionaron niños de 4 a 8 años con al menos una lesión de caries oclusal u oclusoproximal profunda en molares temporales. Los molares se asignaron al azar en dos grupos: (1) restauración realizada con cemento de hidróxido de calcio seguida de cemento de ionómero de vidrio de alta viscosidad (CHC + CIVAV), y (2) restauración CIVAV. Inmediatamente después de la intervención, los niños informaron su malestar durante la técnica de restauración a un examinador externo utilizando la escala facial de Wong-Baker. El malestar autoinformado de los niños se analizó mediante regresión de Poisson comparando ambos grupos y evaluando la influencia de otras variables (α = 5%). Ciento ocho niños cumplieron con los criterios de elegibilidad y fueron asignados al azar en dos grupos (n = 54). La mayoría de los niños que recibieron restauraciones de HCC + CIVAV informaron un malestar mínimo o nulo (83,3%). Los niños tratados con restauración CIVAV informaron puntuaciones similares (92,6%) (p = 0,758). El malestar medio de los niños por CHC + CIVAV fue de 0,37 (1,01) y 0,41 (1,01) para los del grupo de restauración de CIVAV. La incomodidad autoinformada de los niños se asoció con la edad, el género, la cooperación de los niños y el tiempo de intervención. Podemos concluir que la restauración de CHC + CIVAV o CIVAV resulta en una incomodidad mínima o nula para el manejo de las lesiones cariosas profundas y puede considerarse como una opción confiable. O objetivo deste estudo foi avaliar o impacto de diferentes técnicas restauradoras para tratar lesões de cárie profundas em molares decíduos no desconforto relatado pelas crianças. Um estudo clínico randomizado com dois braços paralelos (1:1) foi conduzido e, São Paulo, Brasil. Crianças de 4 a 8 anos com pelo menos uma lesão de cárie oclusal ou oclusoproximal profunda em molares decíduos foram selecionadas. Os molares foram alocados aleatoriamente em dois grupos: (1) restauração realizada com cimento de hidróxido de cálcio seguida de cimento de iônomero de vidro de alta viscosidade (CHC+CIVAV), e (2) restauração de CIVAV. Imediatamente após a intervenção, as crianças relataram seu desconforto durante a técnica restauradora a um examinador externo utilizando a escala de faces de Wong-Baker. O desconforto autorreferido pelas crianças foi analisado usando regressão de Poisson comparando ambos os grupos e avaliando a influência de outras variáveis (α=5%). Cento e oito crianças preencheram os critérios de elegibilidade e foram randomizados nos dois grupos (n=54). A maioria das crianças que receberam restaurações de CHC+CIVAV relatou mínimo ou nenhum desconforto (83,3%). Escores semelhantes (92,6%) foram reportados pelas crianças tratadas com restauração de CIVAV (p=0,758). A média de desconforto das crianças para CHC+CIVAV foi de 0,37(1,01), e 0,41(1,01) para aquelas do grupo de restauração de CIVAV. O desconforto autorreferido pelas crianças foi associado com a idade, sexo, cooperação das crianças e tempo de intervenção. Nós podemos concluir que CHC+CIVAV ou restauração de CIVAV resultam em mínimo ou nenhum desconforto para o manejo das lesões de cárie profunda, podendo ser considerado como uma opção confiável.

Orientador: Jaime Aparecido Cury Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba Resumo: Interferindo localmente com o processo físico-químico de desenvolvimento de lesões de cárie, fluoreto age eficazmente no controle da cárie dentária. Nesse sentido, por sua capacidade de liberar fluoreto constantemente no meio ambiente bucal, os cimentos de ionômero de vidro (CIV) disponibilizam fluoreto no lugar certo (fluido do biofilme), no momento certo (antes da ingestão de açúcar) e na concentração mínima necessária para interferir com o processo de cárie que ocorre ao redor das restaurações. Vários meios de imersão têm sido utilizados para estimar a liberação de fluoreto e o potencial anticárie de CIV e o mais adequado é o uso de soluções desmineralizante (Des-) e remineralizante (Re-) porque simulam a dinâmica do processo de cárie. Diferentes tipos de CIV estão disponíveis no mercado e o potencial deles liberarem fluoreto tem sido avaliado em água ou saliva, meios que não simulam o processo de cárie. O objetivo desse estudo foi avaliar a liberação de fluoreto de 15 CIV, simulando o desenvolvimento do processo de cárie. Seis corpos de prova cilíndricos (161,8 mm2) foram preparados de acordo com as recomendações dos fabricantes. Os corpos de prova foram polidos e submetidos diariamente à ciclagens por 6 e 18 h em volumes de 1 ml de soluções Des- (tampão acetato 50 mM, pH 5,0 contendo 1,12 mM de Ca e 0,73 mM de Pi) e Re- (tampão Tris 0,1 M, pH 7,0 contendo 1,5 mM de Ca, 0,9 mM de Pi e 150 mM de KCl), respectivamente. As soluções foram trocadas diariamente durante 12 dias, nas quais a concentração de fluoreto foi determinada com eletrodo específico pela técnica direta. Os resultados foram expressos em concentração de fluoreto diária liberada nas soluções Des- e Re- (µg F/ml), quantidade de fluoreto liberada diariamente em soluções Des+Re por área de corpo de prova (µg F/cm2/dia) e liberação acumulativa durante os 12 dias (?g F/cm2). A diferença de liberação diária nas soluções Des- e Re- para cada material foi avaliada descritivamente. A liberação diária nas soluções Des+Re e a acumulada foram analisadas por ANOVA, considerando respectivamente os fatores material e tempo ou só material. Para ambos os casos, as diferenças entre os CIV foram comparadas pelo teste de Tukey (p?0,05). Todos os CIV mostraram uma alta liberação inicial de fluoreto nos primeiros dias, seguido por um declínio gradual e posterior estabilização. Três padrões distintos de liberação foram observados nas soluções Des- e Re-: Maior liberação de fluoreto na solução Des- do que na Re- durante todo o período (A); Liberação inicial maior na solução Des- (B) e liberação similar em ambas das soluções durante todo o período (C). Os CIV diferiram estatisticamente na liberação diária e cumulativa de flúor (p

Submitted by arlindo kohlrausch (ajfk@uepg.br) on 2022-04-04T23:21:47Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Angela de Lima da Ros Gonçalves.pdf: 923691 bytes, checksum: 20bd6d4cf5618775063179e327d20504 (MD5) Made available in DSpace on 2022-04-04T23:21:47Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Angela de Lima da Ros Gonçalves.pdf: 923691 bytes, checksum: 20bd6d4cf5618775063179e327d20504 (MD5) Previous issue date: 2020-02-20 A presente revisão sistemática da literatura avaliou a conformidade de ensaios clínicos randomizados sobre longevidade de restaurações atraumáticas (ART) com as recomendações CONSORT e o risco de viés desses estudos. Após desenvolvimento de uma estratégia específica, uma ampla busca na literatura foi realizada em diferentes bases de dados para encontrar triagens clínicas randomizadas que avaliassem a longevidade de restaurações atraumáticas comparadas com outros procedimentos restauradores. Uma ferramenta específica para avaliação dos itens pertencentes às recomendações CONSORT foi aplicada, com pontuação variando entre 0 (sem descrição do ítem), 1 (descrição pobre/inadequada) e 2 (descrição adequada/completa), num total de 32 pontos. A análise do risco de viés foi realizada por meio da ferramenta Cochrane para avaliação do risco, classificando cada domínio em baixo risco, risco indefinido ou alto risco. Os resultados foram apresentados sob a forma de estatística descritiva, com o número de estudos publicados classificados segundo periódico, período de acompanhamento e país do autor principal, com as respectivas médias de adesão às recomendações CONSORT obtidas. A comparação destas médias frente a cada uma destas classificações foi realizada com ANOVA por postos (α=0.05); as correlações entre o fator de impacto dos periódicos e a média CONSORT e o fator de impacto e o risco de viés foram analisadas por meio da correlação de Pearson (α=0.05). Após a busca na literatura, foram identificados 2167 estudos. Destes, 33 ensaios clínicos randomizados preencheram os critérios e foram incluídos na revisão sistemática. A média geral de adesão ao CONSORT destes estudos foi de 21,3 ± 6,1 pontos, o que representa 66% da pontuação máxima possível. Os itens considerados mais críticos e com o maior número de falta ou falhas na descrição foram protocolo, fluxograma e sigilo de alocação, pois aproximadamente 70% dos estudos obtiveram escore 0. A correta descrição do cálculo amostral também esteve faltante em mais de 50% dos artigos. Diferenças nas médias da adesão ao CONSORT foi observada na análise segundo periódico, país do autor principal e período de acompanhamento (p

Submitted by MARIANA DIAS MODA null (moda_mariana@hotmail.com) on 2020-01-15T14:45:24Z No. of bitstreams: 1 TESE Mariana Dias Moda.pdf: 3085065 bytes, checksum: a6fd93b0ac9282510839c9faafa5e777 (MD5) Approved for entry into archive by Claudio Hideo Matsumoto null (claudio@foa.unesp.br) on 2020-01-15T20:48:13Z (GMT) No. of bitstreams: 1 moda_md_dr_araca_int.pdf: 2937081 bytes, checksum: f6eb7c7cf74f29c7a0e9e2bb8b5a774e (MD5) Made available in DSpace on 2020-01-15T20:48:14Z (GMT). No. of bitstreams: 1 moda_md_dr_araca_int.pdf: 2937081 bytes, checksum: f6eb7c7cf74f29c7a0e9e2bb8b5a774e (MD5) Previous issue date: 2019-12-19 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) O objetivo desse estudo foi avaliar o desgaste, as propriedades mecânicas, topografia e composição química dos substratos dentários e materiais restauradores após ciclo erosivo/abrasivo, utilizando diferentes dentifrícios. Foram utilizados 244 blocos, sendo 122 de esmalte e 122 blocos de dentina, medindo 4 x 4 mm, obtidos a partir de incisivos bovinos que foram cortados e polidos. Cada amostra continha um bloco de esmalte e um de dentina, entre os blocos foram confeccionadas restaurações com cimento de ionômero de vidro modificado por resina (CIVMR) e resina composta (RC). Após as restaurações, a hemiface de cada amostra foi recoberta com verniz ácido-resistente, afim de produzir o lado controle. Esses dois grupos foram subdivididos em três grupos, de acordo com o dentifrício utilizado no processo de abrasão: SF - sem flúor (controle negativo), NaF - com fluoreto de sódio 1450 ppm de F (controle positivo) e SnF2 - com fluoreto de estanho 1100 ppm de F. O ácido cítrico a 0,05 M, pH= 3.2, foi utilizado nos ciclos de erosão, sendo realizados 4x/dia, 2 minutos cada, com intervalos de 1 hora entre cada ciclo. Os espécimes foram submetidos à abrasão (2x/dia, ao final do primeiro e último ciclo erosivo/dia), aplicando o slurry (1:3) sobre as amostras por 2 minutos, seguidos de 15 segundos de escovação por espécime (200 g por 15 s), ao longo de 5 dias. Na sequência, o verniz ácido resistente foi removido da hemiface de cada amostra e estas foram analisadas quanto ao desgaste das superfícies através de perfilometria (n=12), microdureza, apenas dos materiais restauradores (n =12), topografia por microscopia de força atômica (AFM) (n=2), nanodureza (H) e módulo de elasticidade (Er) (n=5), composição química através de energia dispersiva de raios-X (EDS) (n=3), microscopia Raman (n= 5). Os dados de perfilometria, microdureza dos materiais restauradores, (H / Er) e EDS e Raman foram submetidos a ANOVA dois fatores medidas repetidas e teste de Tukey (p< 0,05). Em relação às imagens de AFM foram analisadas apenas qualitativamente. O dentifrício NaF promoveu o maior desgaste nas superfícies dentinárias adjacentes ao CIVMR e RC. Apenas as interfaces adjacentes ao esmalte sofreram influência do dentifrício. Os mais baixos valores de microdureza foram observados para CIVMR quando se utilizou o dentifrício SnF2 (p < 0,05). Em relação aos valores de H e Er, pode-se notar que não houve diferenças entre os dentifrícios (p> 0,05), apenas entre as superfícies dentro de cada dentifrício (p< 0,05). Em relação às superfícies controle e erodida, apenas RC manteve seus valores constantes após erosão (p> 0,05). Em relação à composição química, os substratos dentários erodidos mostraram menores concentrações de cálcio e fosfato, enquanto para a superfície do material ionomérico houve uma diminuição de flúor e aumento de cálcio para as superfícies erodidas; as superfícies de resina composta mostraram-se inalteradas em sua composição química após os desafios erosivos (p > 0.05). Os dentifrícios não foram capazes de promover diferença nas propriedades mecânicas das superfícies após ciclo erosivo-abrasivo. Entretanto, promoveram diferenças quanto ao desgaste, composição química e topografia das superfícies, à exceção das superfícies de resina composta. The aim of this study was to evaluate the wear, mechanical properties, topography and chemical composition of dental substrates and restorative materials after erosive / abrasive cycle using different toothpastes. A total of 244 blocks were used: 122 enamel and 122 dentin blocks, measuring 4 x 4 mm, obtained from bovine incisors that were cut and polished.Each sample contained one enamel and one dentin block, between the blocks were made restorations with resin modified glass ionomer cement (RMGIC) and composite resin (CR). After restorations, the hemiface of each sample was coated with acid-resistant varnish to produce the control side. These two groups were subdivided into three groups according to the toothpaste used in the abrasion process: SF - no fluoride (negative control), NaF – sodium fluoride with 1450 ppm F (positive control) and SnF2 – stannous fluoride with 1100 ppm F. The 0.05 M citric acid, pH = 3.2, was used in the erosion cycles, being performed 4x / day, 2 minutes each, with 1 hour intervals between each cycle. The specimens were subjected to abrasion (2x / day at the end of the first and last erosive cycle / day), applying the slurry (1: 3) to the samples for 2 minutes, followed by 15 seconds of brushing per specimen (200 g per 15 s) over 5 days. Next, acid resistant varnish was removed from the hemiface of each sample and these were analyzed for surface wear by profilometry (n = 12), microhardness of restorative materials only (n = 12), atomic force microscopy (AFM) topography (n = 2), nanohardness (H) and modulus of elasticity (Er) (n = 5), chemical composition by X-ray dispersive energy (EDS) (n = 3), Raman microscopy (n = 5). The profilometry, microhardness of the restorative materials, (H / Er) and EDS and Raman data were submitted to two-way repeated measures ANOVA and Tukey test (p 0.05), only among the surfaces into each toothpaste (p< 0.05). In relation to control and eroded surfaces, only CR maintened constant values after erosive-abrasive cycles (p> 0.05). Regarding the chemical composition, the eroded dental substrates presented lower calcium and phosphate concentrations, while for the surface of the ionomeric material there was a decrease of fluoride and calcium increase for the eroded surfaces. Composite resin surfaces were unchanged in their chemical composition after erosion challenges (p> 0.05). The toothpastes were not able to promote difference in the mechanical properties of surfaces after erosive-abrasive cycle. However, promoted differences in surface wear, chemical composition and topography, except for composite resin surfaces. Código de Financiamento 001

Objetivo: este estudo avaliou in vitro o desempenho de restaurações mistas sob diferentes protocolos de união. Material e Métodos: 40 dentes bovinos, divididos aleatoriamente em: condicionamento ácido total (CAT), condicionamento ácido seletivo (CAS); resina composta convencional (RCC), resina composta bulk fill (RCBF), e um adesivo universal (n=10): G1 - CAT + RCC; G2 - CAS + RCC; G3 - CAT + RCBF e G4 - CAS + RCBF. Cavidades classe V (3 mm X 3 mm) foram preenchidas em 1/2 interna de dentina com CIV convencional e o restante da cavidade restaurado conforme distribuição dos grupos. As amostras foram armazenadas em água destilada, a 37ºC por 24h. Realizou-se termociclagem (1000 ciclos; 5-55ºC). Em seguida, as amostras foram impermeabilizadas, imersas em azul de metileno a 1%, por 24h, seccionadas no sentido VL, e avaliadas, pelos escores de infiltração: 0 - sem; 1 -esmalte; 2 - dentina; 3 - parede pulpar. Os dados obtidos foram submetidos ao teste Kruskal-Wallis e Mann-Whitney (p

Among the minimally invasive approaches available today, the atraumatic restorative treatment (ART) has demonstrated promising results both in the primary and permanent dentition. Objective To evaluate the survival of Class I ART restorations in preschoolers with two Brazilian brands of glass ionomer cements (GIC) in comparison with a reference GIC. Material and method The cavities of 49 preschool children (three to five years) with carious lesions in the posterior teeth (N=81) were filled by two experienced pediatric dentists according to the ART technique. The Brazilian GICs Maxxion-R (MR) and Vitro-Fil LC (VF), and the reference GIC Ketac-Molar (KM) were placed in a randomly pre-established sequence. Restorations were evaluated after 6 and 12 months by another investigator. Scores 0 and 1 were considered successful, while scores 3-9 were classified as failures. Kaplan-Meier survival analysis and the log-rank test were performed (p