Objectives: Development of a new generation of stable β alloy, free of aluminum or vanadium and with better biological and mechanical compatibility and evaluate the surface properties of Ti-6Al-4V and Ti-35Nb-7Zr-5Ta after anodization in hydrofluoric acid, followed by deposition of different electrolyte concentrations of magnesium particles by micro arc-oxidation treatment., Methods: Disks were anodized in hydrofluoric acid. After this first anodization, the specimens received the deposition of magnesium using different concentration (8.5% and 12.5%) and times (30s and 60s). The surface morphology was assessed using scanning electron microscopy, and the chemical composition was assessed using energy dispersive x ray spectroscopy. The surface free energy was measured from the contact angle, and the mean roughness was measured using a digital profilometer., Results: Anodization in hydrofluoric acid provided the formation of nanotubes in both alloys, and the best concentration of magnesium considered was 8.5%, as it was the condition where the magnesium was incorporated without covering the morphology of the nanotubes. X-ray dispersive energy spectroscopy showed magnesium incorporation in all conditions. The average roughness was increased in the Ti-35Nb-7Zr-5Ta alloy., Conclusions: It was concluded that anodizing could be used to deposit magnesium on the surfaces of Ti-6Al-4V and Ti-35Nb-7Zr-5Ta nanotubes, with better results obtained in samples with magnesium concentration in 8.5% and the process favored the roughness in the Ti-35Nb-7Zr-5Ta group., (© 2020 The Author(s).)

Statement of Problem: The changes that occur after brushing yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) are unknown. These changes may favor the retention of microorganisms and chemisorption of water, impairing its longevity., Objective: The purpose of this in vitro study was to evaluate the effects of a whitening dentifrice on Y-TZP surfaces after simulating 10 years of brushing., Material and Methods: Seventy-two bar-shaped specimens (20×4×1.2 mm) were divided into 4 groups: storage in distilled water (SW, control), brushing with distilled water (BW), brushing with dentifrice (BD), and brushing with whitening dentifrice (BWD). Brushing was conducted using a linear brushing machine (878400 cycles, 0.98 N, soft toothbrush). The mean roughness (Ra) was analyzed with a profilometer and the superficial topography with scanning electron microscopy (SEM) at baseline and after treatment. Crystalline phases were characterized using x-ray diffraction. Baseline and posttreatment Ra were analyzed using the 1-way ANOVA and Tukey HSD multiple comparison test; the paired t test was used for intragroup comparison (all α=.05)., Results: The Ra (μm) means (before/after treatment) were SW 0.28/0.28; BW 0.32/0.31; BD 0.28/0.36; BWD 0.30/0.20. No statistically significant difference was found for Ra at baseline (P=.108) than for posttreatment results (P<.001); the BD group had higher Ra values when compared with baseline (P=.019); the BWD group had the lowest values (P<.001). The BD surfaces showed pronounced scratches and detachment of the surface, while BWD showed smoother surfaces; similar crystallographic results among groups were observed., Conclusions: Brushing Y-TZP with conventional dentifrice increased roughness, while brushing with whitening dentifrice reduced roughness. Neither dentifrice changed the crystallographic phases after brushing., (Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.)

Statement of Problem: The mechanical properties of new titanium alloys with an elastic modulus closest to cortical bone have been studied. However, potentially damaging conditions experienced in the oral cavity, such as fluoride ions, can initiate a localized or crevice process of corrosive degradation in the alloy surfaces., Purpose: The purpose of this in vitro study was to evaluate the effects of long-term immersion in artificial saliva or in fluoride solution on mean roughness (Ra), Vickers hardness, and topography of the new titanium alloy Ti-35Nb-7Zr-5Ta (TNZT) compared with those of cp Ti and Ti-6Al-4V (TAV)., Material and Methods: Disks (N=210) were divided into cp Ti, TAV, and TNZT and subdivided according to the following treatments: no immersion (N(-), control), immersion in artificial saliva (S), and immersion in fluoride (F) during periods equivalent to 5, 10, 15, and 20 years. The Ra and Vickers hardness were measured with a profilometer and a hardness tester. The topography was analyzed by scanning electronic microscopy. Data were compared using the Kruskal-Wallis and Dunn tests (α=.05)., Results: Values of Ra and hardness were significantly different among the metals (Ra: TAV

Favorable results in the use of castor oil polyurethane (COP) as pulp capping, membrane material, sealer, mouthwash and in bone repair, associated with the fact that Ricinus communis is not derived from petroleum and it is abundant in Brazil, encourage researches in the development of luting agents. Objectives This study compared the flexural strength (FS) of a castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate (COP10) with RelyX ARC (RX) after mechanical cycling (MC) and distilled water storage. Material and Methods Sixty-four specimens (25x2x2 mm) were fabricated and divided into two groups, COP10 and RX (control). Each group was divided into 4 subgroups (n=8) according to the storage time, 24 hours (24 h) or 60 days (60 d), and the performance (MC+FS) or not (only FS) of the mechanical cycling test. The FS (10 kN; 0.5 mm/min) and MC tests (10,000 cycles, 5 Hz, 0.5 mm/min) were carried out using an MTS-810 machine. The data were analyzed using ANOVA (α=0.05). Results The obtained FS (MPa) values were: COP10 24h- 19.04±2.41; COP10 60d- 17.92±3.54; RX 24h- 75.19±3.43; RX 60d- 88.77±6.89. All the RX specimens submitted to MC fractured, while the values for COP10 after MC were as follows: COP10 24h- 17.90±1.87 and COP10 60d- 18.60±1.60. Conclusions A castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate is resistant to mechanical cycling without decreases in flexural strength. However, mean COP10 showed only about 25% of the RelyX ARC mean flexural strength.

Statement of Problem: Although cement-retained implant prostheses are widely used, the quantification of optimal retention remains controversial, and new dental luting agents should be evaluated., Purpose: The purpose of this study was to compare, in vitro, the casting retention on implant abutments after cementation with 3 commercially available luting agents and an experimental luting agent (castor oil polyurethane, COP) with variable weight percentages (wt%) of calcium carbonate (CaCO3)., Material and Methods: Seventy-two palladium-silver cast copings were fabricated and divided into 6 groups: Temp Bond interim cement (TB); zinc phosphate cement (ZP); Rely X ARC resin cement (RX); pure COP (COP); COP + 10% wt% CaCO3 filler (COP 10); and COP + 50% wt% CaCO3 filler (COP 50). After cementation, the specimens were stored in distilled water at 37°C for 24 hours and subjected to removal force tests in a universal testing machine (5 kN; 0.5 mm/min). Statistical analyses were performed with the Kruskal-Wallis and Student-Newman-Keuls tests (α=.05)., Results: The median values of casting retention (N) were as follows: TB=57.20 ±10.4; ZP=343.56 ±50.3; RX=40.07 ±9.7; COP=258.98 ±41.4; COP 10=466.57 ±79.3; and COP 50=209.63 ±31.4. The Kruskal-Wallis test showed significant differences among the groups (P<.01). TB and RX had the lowest mean retention values; COP, COP 10, and COP 50 were equal to ZP, and COP 10 had the highest retention., Conclusions: The casting retention on implant-abutments provided by COP was similar to that of copings cemented with zinc phosphate and may be influenced by the addition of calcium carbonate., (Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.)

This study compared the effectiveness of Ricinus communis (RC) with Nystatin (NYS) and Miconazole (MIC) in the treatment of institutionalised elderly with denture stomatitis (DS). They (n = 30) were randomly distributed into three groups: MIC, NYS or RC. Clinical and mycological evaluations were performed prior to the use of the antifungal (baseline) and repeated after 15 and 30 days of treatment. The sample was clinically examined for oral mucosal conditions. Standard photographs were taken of the palate, and the oral candidiasis was classified (Newton's criteria). Mycological investigation was performed by swabbing the palatal mucosa, and Candida spp. were quantified by counting the number of colony-forming units (cfu mL⁻¹). The clinical and mycological data were analysed, respectively by Wilcoxon and Student's t-test (α = 0.05). Significant improvement in the clinical appearance of DS in the MIC and RC groups was observed between the 1st and 3rd collections (MIC - P = 0.018; RC - P = 0.011) as well as between the 2nd and 3rd collections (MIC - P = 0.018; RC - P = 0.011). Neither groups showed a statistically significant reduction in cfu mL⁻¹ at any time. Although none of the treatments decreased the cfu mL⁻¹, it was concluded that Ricinus communis can improve the clinical condition of denture stomatitis in institutionalised elderly patients, showing similar results to Miconazole., (© 2013 Blackwell Publishing Ltd.)

Purpose: To assess the influence of fluoride on the adhesion of Streptococcus mutans to titanium using an experimental paradigm simulating 10 years of brushing., Materials and Methods: Commercially pure titanium (cpTi) and titanium alloy (Ti-6Al-4V) disks (6 mm in diameter and 4 mm thick) were mirror-polished and randomly assigned to one of the following six groups (n = 6): immersion (I) or brushing (B) in deionized water (groups IW [control] and BW), fluoride-free toothpaste (groups IT and BT), or fluoridated toothpaste (groups IFT and BFT). Specimens subjected to immersion were statically submerged into the solutions without brushing. For the brushed specimens, a linear brushing machine with a soft-bristled toothbrush was used. The experiments lasted a total of 244 hours. Before and after treatment, the specimens were analyzed under an atomic force microscope to determine the mean roughness (Ra) and the mean of the maximum peak-to-valley heights of the profile (Rtm). The disks were contaminated with standard strains of S mutans in well plates with brain-heart infusion broth. Adhesion was analyzed based on the numbers of colony-forming units (CFU/mL) of adhered viable cells using scanning electronic microscopy. Differences in CFU/mL between the groups were analyzed by one-way analysis of variance., Results: Immersion did not affect either surface. As suggested by Ra and Rtm, BW, BT, and BFT induced changes on the surface of cpTi, whereas only BT and BTF induced changes on the surface of Ti-6Al-4V. No significant differences were observed regarding CFU/mL among the cpTi or Ti-6Al-4V groups. S mutans adhesion was similar for all surfaces., Conclusions: The changes in titanium induced by 10 years of simulated brushing with fluoride toothpaste did not increase the adhesion of S mutans.

Objectives: To conduct a controlled study contrasting titanium surface topography after procedures that simulated 10 years of brushing using toothpastes with or without fluoride., Methods: Commercially pure titanium (cp Ti) and Ti-6Al-4V disks (6 mm Ø×4 mm) were mirror-polished and treated according to 6 groups (n=6) as a function of immersion (I) or brushing (B) using deionised water (W), fluoride-free toothpaste (T) and fluoride toothpaste (FT). Surface topography was evaluated at baseline (pretreatment) and post-treatment, using atomic force microscope in order to obtain three-dimensional images and mean roughness. Specimens submitted to immersion were submerged in the vehicles without brushing. For brushed specimens, procedures were conducted using a linear brushing machine with a soft-bristled toothbrush. Immersion and brushing were performed for 244 h. IFT and BFT samples were analysed under scanning electron microscope with Energy-Dispersive X-ray Spectroscopy (EDS). Pre and post-treatment values were compared using the paired Student T-test (α=.05). Intergroup comparisons were conducted using one-way ANOVA with Tukey post-test (α=.05)., Results: cp Ti mean roughness (in nanometers) comparing pre and post-treatment were: IW, 2.29±0.55/2.33±0.17; IT, 2.24±0.46/2.02±0.38; IFT, 2.22±0.53/1.95±0.36; BW, 2.22±0.42/3.76±0.45; BT, 2.27±0.55/16.05±3.25; BFT, 2.27±0.51/22.39±5.07. Mean roughness (in nanometers) measured in Ti-6Al-4V disks (pre/post-treatment) were: IW, 1.79±0.25/2.01±0.25; IT, 1.61±0.13/1.74±0.19; IFT, 1.92±0.39/2.29±0.51; BW, 2.00±0.71/2.05±0.43; BT, 2.37±0.86/11.17±2.29; BFT, 1.83±0.50/15.73±1.78. No significant differences were seen after immersions (p>.05). Brushing increased the roughness of cp Ti and of Ti-6Al-4V (p<.01); cp Ti had topographic changes after BW, BT and BFT treatments whilst Ti-6Al-4V was significantly different only after BT and BTF. EDS has not detected fluoride or sodium ions on metal surfaces., Conclusions: Exposure to toothpastes (immersion) does not affect titanium per se; their use during brushing affects titanium topography and roughness. The associated effects of toothpaste abrasives and fluorides seem to increase roughness on titanium brushed surfaces., (Copyright © 2012 Elsevier Ltd. All rights reserved.)

Unlabelled: The need to develop new dental luting agents in order to improve the success of treatments has greatly motivated research., Objective: The aim of this study was to evaluate the diametral tensile strength (DTS) and film thickness (FT) of an experimental dental luting agent derived from castor oil (COP) with or without addition of different quantities of filler (calcium carbonate - CaCO3)., Material and Methods: Eighty specimens were manufactured (DTS N=40; FT N=40) and divided into 4 groups: Pure COP; COP 10%; COP 50% and zinc phosphate (control). The cements were mixed according to the manufacturers' recommendations and submitted to the tests. The DTS test was performed in the MTS 810 testing machine (10 KN, 0.5 mm/min). For FT test, the cements were sandwiched between two glass plates (2 cm²) and a load of 15 kg was applied vertically on the top of the specimen for 10 min. The data were analyzed by means of one-way ANOVA and Tukey's test (α=0.05)., Results: The values of DTS (MPa) were: Pure COP- 10.94 ± 1.30; COP 10%- 30.06 ± 0.64; COP 50%- 29.87 ± 0.27; zinc phosphate- 4.88 ± 0.96. The values of FT (µm) were: Pure COP- 31.09 ± 3.16; COP 10%- 17.05 ± 4.83; COP 50%- 13.03 ± 4.83; Zinc Phosphate- 20.00 ± 0.12. One-way ANOVA showed statistically significant differences among the groups (DTS - p=1.01E-40; FT - p=2.4E-10)., Conclusion: The experimental dental luting agent with 50% of filler showed the best diametral tensile strength and film thickness.

Statement of Problem: A new short-cycle, spinel-based investment was developed to minimize the long heating cycle generally required for conventional investments for titanium castings, but the quality of castings made using this material has yet to be evaluated., Purpose: The purpose of this study was to compare the Vickers hardness, castability, surface roughness, in vitro marginal misfit, and internal porosity of castings made using silica phosphate-based and spinel-based investments., Material and Methods: The specimens were commercially pure titanium cast using silica phosphate-based investment, Rematitan Plus (RP), and spinel-based investments, Rematitan Ultra (RU) or short-heat-cycle Trinell (TR). Disc-shaped patterns (6 × 3 mm) were cast, and Vickers hardness was measured at the surface, and 50, 100, 150, and 200 μm beneath the surface (n=10). Microstructure was analyzed by optical microscopy (×100). Mesh patterns (14 × 14 × 0.5 mm) were used for castability testing (n=10). Surface roughness (Ra) was measured on disc-shaped patterns (13 × 3 mm) with a profilometer (n=8). Wax copings were cast, screwed to implant abutments, and the marginal misfit was measured using image analysis software (n=10). Internal porosity of the copings was evaluated by density comparisons (n=10). Hardness data were analyzed by 2-way ANOVA and the Tukey HSD test. Castability, surface roughness, and marginal misfit were analyzed by 1-way ANOVA and the Tukey HSD test, and internal porosity by Kruskal-Wallis and Student-Newman-Keuls tests (α=.05)., Results: RP had the highest hardness values at the surface and 50 μm beneath, but the hardness values of TR, RU, and RP were statistically equivalent at 100, 150, and 200 μm. Significant differences were seen when comparing RU and TR with RP for castability (P<.001), surface roughness (P<.001), and marginal misfit (P<.001). No significant differences were seen for internal porosity., Conclusions: The quality of castings made from the new investment, TR, was similar to the quality of those made using the conventional spinel-based investment, RU, and superior to those made using RP., (Copyright © 2010 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.)

Objective: This study compared the cutting capacity of carbide burs sterilized with microwaves and traditional sterilization methods., Material and Methods: Sixty burs were divided into 5 groups according to the sterilization methods: dry heat (G1), autoclave (G2), microwave irradiation (G3), glutaraldehyde (G4) or control - no sterilization (G5). The burs were used to cut glass plates in a cutting machine set for twelve 2.5-min periods and, after each period, they were sterilized (except G5) following the protocol established for each group. The cutting capacity of the burs was determined by a weight-loss method. Data were analyzed statistically by Kruskal-Wallis and Dunn's test., Results: The means of the cutting amount performed by each group after the 12 periods were G1 = 0.2167 +/- 0.0627 g; G2 = 0.2077 +/- 0.0231 g; G3 = 0.1980 +/- 0.0326 g; G4 = 0.1203 +/- 0.0459 g; G5 = 0.2642 +/- 0.0359 g. There were statistically significant differences among the groups (p<0.05); only dry heat sterilization was similar to the control., Conclusion: Sterilization by dry heat was the method that least affected the cutting capacity of the carbide burs and microwave sterilization was not better than traditional sterilization methods.