Small-bandwidth n-type PbTe-MnTe alloys effectively modify the valley shape, while it also inevitably aggravates the deterioration of carrier mobility as nonpolar phonons dominate the scattering. It is found that a trace amount of Cu doping can alleviate the compromises among thermoelectric parameters, thereby significantly optimizing the electrical-transport performance near room temperature of n-type PbTe-MnTe alloys. The single-Kane model reveals that the physical origin of performance improvement lies in the carrier mobility enhancement and self-optimization of carrier concentration. The Debye-Callaway model further quantifies the contribution of copper defect scattering to the lattice thermal conductivity. Notably, the high thermoelectric quality factor obtained in this work rationalizes their superior properties and reveals immense potential for achieving higher zT. Herein, an extremely high zT of ∼0.52 at room temperature and a maximum zTmax of ∼1.2 at 823 K are achieved in 0.3% Cu-intercalated n-type PbTe-MnTe. The mechanism in balancing compromise elaborated in principle contributes to an improvement of thermoelectric properties of the n-type PbTe alloys in a broad temperature range.

The fact that the thermoelectric performance is far inferior to that of p-type PbTe has inspired many strategies to develop n-type PbTe thermoelectrics. Alloying PbS in n-type PbTe effectively changes the shape of a valley to trigger a heavier conduction band for improving the Seebeck coefficient, while the resulting small orbital overlap inevitably leads to phase separation hindering electron transport. The effect of vacancies on the solubility of sulfur in n-type PbTe is ambiguous; especially, the heterostructure due to phase separation in high-content PbS-alloyed PbTe also requires sufficient modification to optimize the electroacoustic transport. This motivates the current work on the introduction of vacancies by charge-balancing doping via Sb2Te3 and discovers striking new insight that the introduced vacancies can induce a new heterostructure of Pb2Sb2S5 and suppress the aggregation of Sb and PbS in high-solubility n-type PbTe–PbS. The modification of the band structure and optimization of the electron transport give rise to a prominent enhancement in electronic performance. Furthermore, the Debye–Callaway model validates the dramatic contribution of vacancy aggregation and heterostructures to lattice thermal conductivity. As a result, the synergistic modulation of electroacoustic characteristics achieves a significant improvement in both the maximum zT and the near-room-temperature zT. Understanding such unique findings is critical for applicability to other thermoelectric materials.