As hydrogen is touted as a key player in the decarbonization of modern society, it is critical to enable quantitative H analysis at high spatial resolution, if possible at the atomic scale. Indeed, H has a known deleterious impact on the mechanical properties (strength, ductility, toughness) of most materials that can hinder their use as part of the infrastructure of a hydrogen-based economy. Enabling H mapping, including local hydrogen concentration analyses at specific microstructural features, is essential for understanding the multiple ways that H affect the properties of materials, including for instance embrittlement mechanisms and their synergies, but also spatial mapping and quantification of hydrogen isotopes is essential to accurately predict tritium inventory of future fusion power plants, ensuring their safe and efficient operation for example. Atom probe tomography (APT) has the intrinsic capabilities for detecting hydrogen (H), and deuterium (D), and in principle the capacity for performing quantitative mapping of H within a material's microstructure. Yet the accuracy and precision of H analysis by APT remain affected by the influence of residual hydrogen from the ultra-high vacuum chamber that can obscure the signal of H from within the material, along with a complex field evaporation behavior. The present article reports the essence of discussions at a focused workshop held at the Max-Planck Institute for Sustainable Materials in April 2024. The workshop was organized to pave the way to establishing best practices in reporting APT data for the analysis of H. We first summarize the key aspects of the intricacies of H analysis by APT and propose a path for better reporting of the relevant data to support interpretation of APT-based H analysis in materials.

The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is available to drive plate growth. In Ti-6246, the plate growth velocity was found to be around 0.32 um min-1 at 850 oC, which was in good agreement with the model prediction of 0.36 um min-1 . The solute field around the growing plates, and the plate thickness, was found to be quite variable, due to the intergrowth of plates and soft impingement. This solute field was found to extend to up to 30 nm, and the interface concentration in the beta was found to be around 6.4 at.% Mo. It was found that increasing O content will have minimal effect on the plate lengths expected during continuous cooling; in contrast, Mo approximately doubles the plate lengths obtained for every 2 wt.% Mo reduction. Alloys using V as the beta stabiliser instead of Mo are expected to have much faster plate growth kinetics at nominally equivalent V contents. These findings will provide a useful tool for the integrated design of alloys and process routes to achieve tailored microstructures., Comment: Revised version resubmitted to journal