The evaluation of the performance of polyesters under in vitro physiologic conditions is essential to design scaffolds with an adequate lifespan for a given application. In this line, the degradation-durability patterns of poly(lactide-co-glycolide) (PLGA), polydioxanone (PDO), polycaprolactone (PCL) and polyhydroxybutyrate (PHB) scaffolds were monitored and compared giving, as a result, a basis for the specific design of scaffolds from short-term to long-term applications. For this purpose, they were immersed in ultra-pure water and phosphate buffer solution (PBS) at 37 °C. The scaffolds for short-time applications were PLGA and PDO, in which the molar mass diminished down to 20% in a 20–30 days lifespan. While PDO developed crystallinity that prevented the geometry of the fibres, those of PLGA coalesced and collapsed. The scaffolds for long-term applications were PCL and PHB, in which the molar mass followed a progressive decrease, reaching values of 10% for PCL and almost 50% for PHB after 650 days of immersion. This resistant pattern was mainly ascribed to the stability of the crystalline domains of the fibres, in which the diameters remained almost unaffected. From the perspective of an adequate balance between the durability and degradation, this study may serve technologists as a reference point to design polyester-based scaffolds for biomedical applications, Peer Reviewed, Postprint (published version)

Monitoring and understanding the in vitro behaviour of polyester based scaffolds both comprising the study of the hydrolytic degradation and the cell seeding viability is essential to ensure the desired functionality, according to a given biomedical purpose. As a model case to compare the performance of techniques to monitor the in vitro behaviour, poly(lactide-co-glycolide) (PLGA) scaffolds were chosen. The in vitro hydrolytic degradation of PLGA scaffolds was carried out in water and phosphate buffered saline (PBS). The evolution of the mass loss, the molar mass, the thermal properties and the surface morphology were monitored. The hydrolytic degradation media was correspondingly evaluated by means of the study of the pH, the amount of acid released and the conductivity. In addition, the in vitro biocompatibility regarding the cell culture viability was studied under physiological conditions. The cellular adhesion, cellular ability to proliferate on the scaffold, the scaffold inflammatory profile and the effect of the scaffold degradation compounds on the cells were assessed. A comparative analysis of the exploited techniques in terms of promptness of identification, depth of knowledge, simplicity of obtaining results and cost of the technique was implemented. The results showed that, depending on the balance between the interest in ascertaining the trigger of degradation or deep into the knowledge of the causes and effects of cell culture viability, an appropriate plan of analysis of the validation of polyester-based scaffolds could be designed., Peer Reviewed, Postprint (author's final draft)